Introduction

Interest in diamond nanocrystals stems from applications that range from materials to medical sciences1,2,3,4,5. These nanocrystals possess high hardness and wear resistance, are chemically inert and are promising for drug delivery. Wide band gap, optical transparency and unusually high thermal conductivity make them attractive materials for preparing semiconductors4 and electron-field emitters2. Fluorescent nanodiamonds have been used as non-toxic alternatives to semiconductor quantum dots for biomedical imaging5. Biocompatibility and resistivity enable use of nanodiamonds for coatings on medical implants6. The broad spectrum of possible functional chemical groups, biocompatibility, small sizes and homogeneous size distributions offer extensive possibilities for using them in nanofabrication, bioconjugation and drug delivery3,7.

Literature reports indicate that many diamond nanocrystals are structurally inhomogeneous, consisting of ordinary cubic (c-) diamond (space group: Fd-3m), plus several poorly characterized sp3-bonded forms, variously called polymorphs, allotropes, or polytypes8,9,10,11,12,13,14,15,16,17,18. For uniformity, we call these polymorphs. They are of interest to materials scientists because they are thought to possess exceptional physical properties. For example, h-diamond (aka lonsdaleite), whose existence as a distinct material was recently questioned19, has received attention because it is thought to possess superior compressive strength, hardness and rigidity, compared to c-diamond20,21. The i-diamond polymorph has been proposed to be a super-dense form, with a calculated density of 4.1 g/cm3, which is 15% greater than that of c-diamond22. m-diamond was attributed to a material that could possess extreme hardness23. Wen et al.24 suggested that, in distinction to c-diamond, n-diamond absorbs electromagnetic radiation and thus could eliminate electromagnetic interference caused by wireless communication tools.

Nanodiamonds of extraterrestrial origin are abundant in some meteorites25,26,27 and have been reported from impact-related horizons in sedimentary rocks such as the K/Pg boundary28. Meteoritic nanodiamonds also have the potential to provide insights into early Solar System formation conditions26. Of particular interest are reports of a world-wide nanodiamond-rich layer associated with the onset of the Younger Dryas (YD) cooling episode at ~12,800 before present29,30,31,32,33. These nanodiamonds are postulated to have formed from terrestrial carbon during an extraterrestrial impact, producing c-, h-, i- and n-diamonds33. According to this scenario, the catastrophic event had serious consequences on the climate and brought about the extinctions of most Pleistocene megafauna including Mammoths29,30,31,32,33. However, questions have been raised about the temporal association of nanodiamonds with the YD34,35, the occurrence of diamond polymorphs in these sediments34,36,37,38 and even evidence for impact signatures during the YD39. Although controversial, YD reports commonly use the presence of nanodiamond polymorphs as the impact signature.

The proposed polymorphs could be attractive for a range of applications and as proxies of major terrestrial impacts, but they have not been synthesized in pure form and have only been reported as mixtures of different carbonaceous phases such as graphite and amorphous carbon. As such, the structures and characteristics of the reported polymorphs are either controversial or not diagnostic (Table 1). In particular, the existence of h-diamond was recently questioned19 and several structural and chemical models were proposed for i-, m- and n-diamond, including substitution of carbon by hydrogen9,13,40 and incompletely described diamond forms41. Recently, Li et al.42 suggested a structure model for n-diamond consisting of layers of h-diamond and _C_3 isosceles triangle rings. In any case, there is no consensus on the structure or synthesis conditions of the polymorphs.

Table 1 Diamond and reported nanosized polymorphs.

Full size table

Transmission electron microscopy (TEM) is uniquely suited for the structural and chemical investigation of individual nanosized particles. Diamond polymorphs have been reported from high-resolution transmission electron microscope (HRTEM) images and selected-area electron diffraction patterns based on features absent from c-diamond. However, these features are not unique for the presumed polymorphs (Supplementary Note 1, Supplementary Figs 1-2). We show that natural and synthetic c-nanodiamonds commonly consist of sub-nanometer twin domains, which give rise to the characteristic features attributed to the proposed diamond polymorphs.

Results

Nano-sized twins in c-diamond

In order to investigate the diamond-polymorph issue, we selected several synthetic and natural samples for study. The synthetic samples were produced through chemical vapor deposition (CVD) and the natural ones were obtained from primitive (Murchison and Orgueil) and impact-shocked (Gujba) meteorites42. Samples of similar origins reportedly contain various diamond polymorphs9,10,11,12,13,16,25,27.

HRTEM images of these nanodiamonds reveal fringes with 0.206-, 0.126- and 0.108-nm spacings, corresponding to c-diamond {111}, {202} and {113} planes, respectively (Figs 1 and 2). All investigated grains show one or more of these sets of fringes and the C K-edge EELS spectral shapes from these crystals are consistent with c-diamond (Supplementary Fig. 2a). Twinning is characteristic of the nanocrystals (Figs 1, 2, 3, 4, 5), which commonly display both reflection and rotation twins. The most abundant types are the {111} reflection twins (Fig. 1a,b), also called ∑3 twins, which are consistent with previous studies25,44,45. These twins can give rise to the common <011> rotation twins25,45, in which the domains are rotated ∼71º with respect to each other around <011> (Fig. 1b). We report a new type of rotation twins (<11> twins) (Fig. 2), which divide the grains into sub-nanometer domains, similar to the <011> rotation twins. The symmetry of these domains matches that of c-diamond. However, as a result of rotational twinning, the HRTEM images exhibit new non-crystallographic symmetry elements. For example, the grains in Figs 1b and 2a have pentagonal and dodecagonal symmetries. Pentagonal and decagonal symmetries are common in gold nanoparticles46,47 and five-fold twins occur in nanodiamonds25,45,48. The nanodiamond grain with dodecagonal symmetry (Fig. 2), in which the domains are rotated 30° to each other, is a new example of non-crystallographic symmetry in nanoparticles.

Figure 1

figure 1

Twinned nanodiamonds from the Murchison and Orgueil meteorites.

(a) Grain with multiple {111} twins along <011>. (b) Grain with <011> rotation twins exhibiting pentagonal symmetry. White dotted lines indicate the {111} twin planes.

Full size image

Figure 2

figure 2

Nanodiamond grain exhibiting dodecagonal symmetry.

(a) HRTEM image along <11> Nanodiamond grain from the Orgueil meteorite exhibiting dodecagonal symmetry. Black arrow points towards a hexagonal ring of carbon atoms (black). (b) FFT calculated from the area marked by white corners in (a) shows multiple sets of 0.206-nm {111} diffraction spots (white arrows). We interpret these spots as evidence for twin domains that are rotated around <11> by 30°, i.e., for a grain displaying dodecagonal symmetry. Domains with different sizes account for the uneven intensity distribution of diffraction spots (cf. the intensities of the 111 diffraction spot for domains i, ii, iii, iv). (c) Structure model, deduced from the FFT, of an idealized 30° rotation twin containing 12 equal-sized domains (<11> projection). The interface of the twin domains consists of five- and six-member carbon rings (the central ring is indicated by a black arrow). (d) Sketch of the diffraction pattern of the 30° rotation twins. Domains and their corresponding diffraction spots are illustrated by the balls having different patterns. The grain is a new example of non-crystallographic symmetry in nanoparticles.

Full size image

Figure 3

figure 3

Nanodiamonds with hexagonal 0.206-nm fringes.

(a) Grain from the Orgueil meteorite. (b,c) Grains from the Murchison meteorites. These grains contain sub-nanometer regions that exhibit hexagonal fringes when viewed along <11> (white rhombuses). (d) FFT calculated from (c) shows hexagonally arranged diffraction spots (white arrows). (e) Background-filtered image calculated from (c). (f) Structure model of the region marked with white corners in (e). The model consists of large regions (domain i: black balls) with rectangular {111} and {202} cross-fringes and a small region (domain ii: white balls) with hexagonally arranged {111} fringes (black lines) resulting from two adjacent {113} twins (black dotted lines). The hexagonally arranged carbon atoms give rise to the hexagonally arranged diffraction spots. The intensity of these spots is a function of the width of the area with hexagonally arranged carbon atoms; i.e., layers of domain ii can be coherent with other ii layers even if separated by i layers, with a resulting increase in diffraction intensity.

Full size image

Figure 4

figure 4

Diamond nanocrystals with rectangular 0.206-nm fringes (white lines).

(a) HRTEM image of a grain from the CVD-produced sample. Corresponding FFT (insert) shows two sets of 0.206-nm {111} diffraction spots that indicate domains (i, ii) that are rotated 90° with respect to each other along <011>. (b) Structure model showing two domains of a 90º rotation twin. Black lines mark perpendicular {111} planes. The domain boundaries of the twin structure consist of five-, six- and seven-member carbon rings. The sketch of the diffraction pattern of the 90° rotation twin (insert) shows two sets of {111} diffraction spots. Domain i and ii as well as their corresponding diffraction spots are marked with grey and black balls, respectively. (c) Grain from the CVD-produced sample (d,e) Grains from the the Orgueil meteorite. Domain misorientation (tilt from <011> zone axis) results in one set of 111 diffraction spots in FFTs (c,d,e). The FFT suggests that (d) consists of three domains (white arrow) from which two are related to 90° rotation.

Full size image

Figure 5

figure 5

Rectangular 0.206-nm fringes (white lines) of a diamond nanocrystal from the Gujba sample and its interpretation with domains that are rotated 90° with respect to each other.

(a) HRTEM image and its corresponding FFT (bottom left). (b,c) Amplitude images calculated from the 111 set of diffraction spots of the FFT. Bright areas correspond to twin domains i and ii, respectively.

Full size image

Grains exhibiting hexagonal- and square-fringe patterns having 0.206-nm spacings corresponding to c-diamond {111} planes (Figs 3, 4, 5) are prominent in each sample. The fast Fourier transforms (FFTs) calculated from these patterns show c-diamond diffraction spots that are related through two types of twins. The diffraction spots calculated from the hexagonal-fringe pattern (Fig. 3d) can be interpreted as arising from {113} reflection twins. This type of twin is especially abundant in the shock-formed Canyon Diablo diamond and in synthetic samples prepared under conditions in which lonsdaleite was reported19. The FFTs calculated from the square-fringe pattern exhibit rows of perpendicular diffraction spots with 0.206-nm spacings corresponding to c-diamond {111} planes and additional diffraction spots with the same spacings (Figs 4, 5a). This diffraction-spot arrangement is consistent with <011> rotation twins, in which the twin domains are rotated 90° with respect to each other around <011>. In order to clarify details of this twin type, we modeled its structure (Fig. 4b) and generated amplitude images from the {111} diamond diffraction spots (Fig. 5b,c). The intensity maxima of these images occur where the selected sets of fringes occur. They show the {111} lattice fringes occur in different regions and do not overlap completely (Fig. 5b,c), as is characteristic of twin domains. Thus, although the hexagonal and square-fringe patterns exhibit symmetries not expected for c-diamond, twinned c-diamond provides an explanation.

Explanation for the diffraction features of the polymorphs

The twinned nanodiamonds described above display HRTEM images and spacings that match those used to recognize the reported diamond polymorphs. For example, nanosized grains of h-diamond have been identified from HRTEM images with hexagonal and square fringe-patterns25,27,29,30,31,32,33 showing 0.21-nm spacings. However, simulations of HRTEM images at different experimental conditions suggest the observed patterns are incompatible with this interpretation (Supplementary Fig. 3). The reported hexagonal and square-fringe patterns match those of Figs 3, 4, 5, i.e., they are consistent with the {113} twins and <011> rotation twins mentioned above. As such, the structural features attributed to h-diamond can be explained by twinned c-diamond. The case for i-diamond is more problematic as there is no consensus regarding its structure and reports of its unit-cell dimension range between 0.250 and 0.428 nm, with primitive or i-centered symmetry (Table 1). Assuming the most commonly reported9,18,22 unit-cell parameter of 0.428 nm and i-centering with an a glide22, the HRTEM image of i-diamond matches the square fringe-pattern having 0.21-nm spacings. However, our analysis shows this pattern is consistent with <011> rotation twins of c-diamond. The proposed m-diamond, which was recently reported from HRTEM images and corresponding FFTs based on a 0.63-nm d-spacing23, can be explained by {111} c-diamond twins (Supplementary Fig. 4). These twins in thick crystals (electron is scattered more than 1) can give rise to the spacings and diffraction spots attributed to m-diamond. Therefore, the diffraction patterns and HRTEM images used to identify h-, i- and m-diamond are compatible with twinned c-diamond.

The issue of n-diamond is ambiguous because its diagnostic d-spacings are not unique (Supplementary Fig. 1). For example, it is commonly identified using the 0.178-nm spacing (assigned as the 200 diffraction spots) from HRTEM images and their corresponding FFTs10,11,12,13,17,30,31,32,33. However, diffraction from dynamically scattered electrons for c-diamond yields the same spacing. Images show the intensity of the 200 diffraction spot, which violates the crystallographic selection rules for Fd-3m symmetry, arises with increasing sample thickness even in nanosized crystals (Supplementary Fig. 5). Identification from SAED ring patterns is similarly nondiagnostic because they are from areas large enough (>20-nm wide) to include grains of other nanomaterials. For example, graphite, whose d-spacings closely match those of n-diamond, is a common byproduct of synthesis and also occurs in natural samples together with c-diamond nanocrystals.

Conclusions

The literature contains numerous reports of diamond polymorphs, including h-, i-, m- and n- diamond8,9,10,11,12,13,14,15,16,17,18,23,25,27,28,29,30,31,32,33,35,49. However our ultra-high-resolution TEM data show that nanodiamonds are intimately twinned and these defects give rise to the image and diffraction features used to identify h-, i-, m- and n- diamond. This interpretation calls for reevaluation of previous reports and leads to a rethinking of materials and planetary science implications based on these polymorphs. For example, the reported exceptional material properties10,18,19,20,23 attributed to these polymorphs need to be reexamined. Furthermore, since nanosized diamond polymorphs reported in28,29,30,31,32,33 are not necessarily a marker for cosmic impact and therefore inappropriate for inferring the YD impact origin, the question of that origin is worth reconsidering as also proposed in34,36,37,38,39.

Twinning is common in c-diamond nanocrystals, produces grains with intricate patterns of structure fringes in HRTEM images and results in nanometer to sub-nanometer domains. Of the samples we studied, the twin domains are largest (>5 nm wide) in the Gujba meteorite, in which the crystals are also large (>10 nm wide) and which were reported to form as a result of shock metamorphism43. In contrast, the small twin domains (<1 nm wide) of Murchison and Orgueil are comparable in size to those of the CVD-produced diamond. Our findings imply that defective structure is favored for 1- to 5-nm diamond crystals, many of which contain abundant twin boundaries. These boundaries affect the mechanical, electronic and optical properties of c-nanodiamonds and promote the implantation of foreign elements (dopants), which are used to prepare semiconductors, electron-field emitters and quantum dots2,4,5.

Methods

Materials and Methods

Small droplets (ca. 2 ml) of Gujba, Murchison and Orgueil nanodiamond residues in suspension with water were dried on Cu grids coated with lacy-C. We also prepared TEM samples from (1) synthetic material provided by Andriy Sherehiy and Mahendra Sunkara (University of Louisville), grown in a chamber that was inadvertently contaminated with Cu; and (2) CVD-produced nanodiamonds provided by Robert Nemanich (Arizona State University). TEM data were acquired from electron-transparent areas of the residues protruding into the holes of the carbon-support film. HRTEM and bright-field STEM images were acquired with a JEOL 4000EX TEM (400 keV, 0.17-nm point resolution) and a JEOL ARM200F aberration-corrected scanning TEM (200 keV, 0.08-nm point resolution), respectively.

FFTs obtained from the HRTEM images were calculated using Gatan Digital Micrograph (DM) 3.5 software. The amplitude images of Fig. 5 were generated following the method described in50,51, using routines written for DM software and applying 0.2 nm−1 Lorentzian masks for the {−111} set of diamond diffraction spots. We performed this analysis on the Gujba sample, where the domains were sufficiently large (>5 nm wide). We set the upper and lower contrast limits to the same values for both images.

Additional Information

How to cite this article: Németh, P. et al. Twinning of cubic diamond explains reported nanodiamond polymorphs. Sci. Rep. 5, 18381; doi: 10.1038/srep18381 (2015).

References

Download references

Acknowledgements

We thank Gary Huss for the Murchison and Orgueil nanodiamond residues and Andriy Sherehiy, Mahendra Sunkara and Robert Nemanich for the synthetic material. We acknowledge use of the facilities in the John M. Cowley Center for High Resolution Electron Microscopy at Arizona State University and thank John Mardinly and Toshihiro Aoki for helping obtain the STEM images, István Dódony for helpful discussions and Csilla Molnár for helping prepare the structure models of the 30° and 90° twins. P.N. acknowledges support from the János Bolyai Research Scholarship. L.A.J.G. and P.R.B. were supported by NASA Origins of Solar Systems grant NNX11AK58G.

Author information

Authors and Affiliations

  1. Institute of Materials and Environmental Chemistry, Research Center for Natural Sciences, Hungarian Academy of Sciences, H-1117 Budapest, Magyar Tudósok Körútja 2, Hungary
    Péter Németh
  2. Center for Meteorite Studies, Arizona State University, Tempe, 85287-6004, Arizona, USA
    Laurence A. J. Garvie
  3. School of Earth and Space Exploration, Arizona State University, Tempe, 85287-6004, Arizona, USA
    Laurence A. J. Garvie & Peter R. Buseck
  4. School of Molecular Sciences, Arizona State University, Tempe, 85287-1604, AZ, USA
    Peter R. Buseck

Authors

  1. Péter Németh
    You can also search for this author inPubMed Google Scholar
  2. Laurence A. J. Garvie
    You can also search for this author inPubMed Google Scholar
  3. Peter R. Buseck
    You can also search for this author inPubMed Google Scholar

Contributions

P.N., L.A.J.G. and P.R.B. conceived the project and P.N. took the lead on data analysis and manuscript writing. All authors contributed to interpreting the data and writing of the paper.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Electronic supplementary material

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

Reprints and permissions

About this article

Cite this article

Németh, P., Garvie, L. & Buseck, P. Twinning of cubic diamond explains reported nanodiamond polymorphs.Sci Rep 5, 18381 (2016). https://doi.org/10.1038/srep18381

Download citation