2O4:Cr³⁺) over the continuous range from 701 to 818 nm. The tunable emission was observed at room temperature and above in a homogeneously broadened, vibronic, four-level mode of laser action. In this mode the laser gain cross section increases from7 \times 10^{-21}cm²at 300K to2 \times 10^{-20}cm²at 475K, which results in improved laser performance at elevated temperatures. Efficient 2.5 percent, low-threshold (10 J) operation has been obtained with xenon-flashlamp excitation of the 6 mm diameter × 76 mm length laser rods. Output pulses of greater than 5 J and average power outputs of 35 W have been demonstrated, limited by the available power supply. The emission is strongly polarizedE\parallelb, with a gain that is 10 times that in the alternate polarization. The 262 μs, room-temperature fluorescence lifetime permits effective energy storage andQ-switched operation. TunableQ-switched pulses as large as 500 mJ have been obtained with pulsewidths ranging between 33 and 200 ns depending on the laser gain. Laser action has also been demonstrated on the high-gain (3 \times 10^{-19}cm²emission cross section)Rline at 680.4 nm and is also polarizedE\parallelb. This three-level mode is analogous to the lasing in ruby except that the stimulated emission cross section in alexandrite is ten times larger than for ruby.">

Tunable alexandrite lasers (original) (raw)

IEEE Account

Purchase Details

Profile Information

Need Help?

A not-for-profit organization, IEEE is the world's largest technical professional organization dedicated to advancing technology for the benefit of humanity.
© Copyright 2025 IEEE - All rights reserved. Use of this web site signifies your agreement to the terms and conditions.