The International Journal of Advanced Manufacturing Technology, Dec 2, 2008
Dicle üniversitesi mühendislik fakültesi mühendislik dergisi, Mar 15, 2019
Dicle üniversitesi mühendislik fakültesi mühendislik dergisi, Apr 4, 2018
DergiPark (Istanbul University), May 1, 2008
In this study, the effect on the connecting characteristic of welding temperatures on the joining... more In this study, the effect on the connecting characteristic of welding temperatures on the joining with the diffusion bonding using Ni and Cu interlayer of Ni-Ti-Cu composites manufactured by powder metallurgy method has been investigated. Composite materials have been produced with proportions by mixing 44±5µm Ni-Ti and 37-105±5 µm Cu powders. Diffusion bonding experiments have been carried out in argon atmosphere at the temperatures 910-940 and 970 ºC and 5 MPa under a dynamic load for at 60 min. constant holding time. The properties of microstructure occurred in the interface zone of the bonds of the joints have been examined by optic analysis, EDS and X-Ray. The strength of the joint has been tested by lap-shear and microhardness tests. The result of all observations has been indicated a homogenous Ni-Ti-Cu distribution and the quality of the coalescence at interfaces at elevated temperatures.
Advanced Composites Letters, 2020
The stainless steel 304L (commercially supplied) and Monel K-500 that was prepared through cold p... more The stainless steel 304L (commercially supplied) and Monel K-500 that was prepared through cold pressing of metal matrix composite materials powder mixtures were joined by diffusion welding. Welding was performed under uniaxial compression using the 50 mm-thick nickel (Ni) and aluminum (Al) 2024 interlayers under 3 MPa at 950-980 C for 60 min in an argon gas atmosphere. After welding, the diffusion and intermediate zones of the samples were characterized using X-ray diffraction, optical microscopy, scanning electron microscopy, and energy-dispersive spectrometry analysis. As evaluating the diffusion zone with interlayer, it was determined that different interlayers expanded due to increasing temperature of the diffusion area. Interlayers expanded more on the K-500 side and relatively less on the 304L side. On the other hand, when samples with Ni interlayers were examined, high amount of Ni contained by both base material (304L) and interlayer led to the formation of rich Ni phases in the diffusion side. The brittle FeNi,
Dicle üniversitesi mühendislik fakültesi mühendislik dergisi, Sep 1, 2017
MP MATERIALPRUEFUNG - MP MATERIALS TESTING, Dec 20, 2019
In this study, the weldability of P460 and S355 steel was investigated by application of the subm... more In this study, the weldability of P460 and S355 steel was investigated by application of the submerged arc welding (SAW) process. In the analyses, the effects of various parameters were handled at different welding speeds, the two levels of the current values of 475 A to 525 A and 525 A to 575 A, commercial submerged additive metals, and commercial aglomera welding powders. A notch impact test was carried on to determine the strength of the joints. Microhardness measurements were made at a Vickers load of 500 g. Optical microscopy and EDS analyses were utilized in the weld zone to investigate the microstructure changes which depend on the welding parameters. The results of this study indicate that P460 steel maintained sufficiently good weldability by application of the submerged welding process.
Industrial Lubrication and Tribology, Jun 15, 2012
DÜMF Mühendislik Dergisi
GR5 (Ti6Al4V) is a material commonly used in aerospace and space, biomedical and automobile secto... more GR5 (Ti6Al4V) is a material commonly used in aerospace and space, biomedical and automobile sectors, consisting of pure titanium at a minimum of 99% purity. Besides being lightweight, GR5 is separate from similar materials with its ability to resist corrosion at high levels and show high strength. SX steel is high silicon-content austenitic stainless steel with the ability of good quality of welding and excellent corrosion resistance in high concentration sulfuric acid and nitric acid. SX is used in areas such as acid coolers, acid piping systems, acid distributors, acid towers and tanks, pumps, nozzles, internals, strainers and mesh pads. With improving technology, the need for steel-titanium materials that are resisted to acid and made with welded joint is increasing. In this study, the effect of GR and SX materials of welding temperature on the connection is examined with diffusion welding method using copper intermediary layer. The material pairs are combined with a pressure of ...
Dicle üniversitesi mühendislik fakültesi mühendislik dergisi, Dec 6, 2022
Paslanmaz çelikler mimari yapılarda, inşaat, otomotiv, ulaşım, gıda ve medikal gibi birçok sektör... more Paslanmaz çelikler mimari yapılarda, inşaat, otomotiv, ulaşım, gıda ve medikal gibi birçok sektörde geniş bir kullanım ağına sahip bir malzemedir. Bu malzemelerin korozyon direncinin yüksek olması, bakım maliyetlerinin düşük olması, mükemmel süneklikleri, kırılmadan önemli darbeleri emebilmeleri ve estetik görüntü sunması bu malzemeleri cazip kılmaktadır. Paslanmaz çeliklerin metalürjisi karmaşıktır ve üretim sürecinin nihai özellikleri üzerinde daha yüksek bir etkisi vardır. Üretim süreçlerinde kazandırılan bu özellikler, östenitik 304 kalite malzemeler kaynak yapılabilirliği yüksek, 430 kalite ferritik paslanmaz çelikler ise kaynaklanma kabiliyetlerini azaltan etkiye neden olur. Bu çalışmada farklı kaynaklanma kabiliyetine sahip 304 ve 430 kalite paslanmaz çeliklerin katı faz difüzyon kaynağı ile birleştirilebilirliği ve birleşmeye ara tabakanın etkisi araştırılmıştır. Numuneler 960, 980 ve 1000ºC sıcaklıkta ve 45, 60 ve 75 dakika sürelerde, 1, 2 ve 3 MPa basınç altında atmosfer kontrollü fırında bakır ara tabaka kullanılarak difüzyon kaynağı tekniğiyle birleştirilmiştir. Numunelerin kaynak bölgesi mikroskopla, incelenmiş ve difüzyon alanındaki bakır ara tabakanın ana malzemelere dağılımı gözlenmiştir. Malzemelerin mekanik mukavemetlerini belirlemek için mikro sertlik ve çekme testleri uygulanmıştır, deneylerde Taguchi optimizasyon yöntemi ile Varyans (Anova) analizleri yapılıp en etkili parametreler bulunmuş ve deneyin güvenilirlik seviyesi tespit edilmeye çalışılmıştır.
Materials Testing, 2019
In this study, the weldability of P460 and S355 steel was investigated by application of the subm... more In this study, the weldability of P460 and S355 steel was investigated by application of the submerged arc welding (SAW) process. In the analyses, the effects of various parameters were handled at different welding speeds, the two levels of the current values of 475 A to 525 A and 525 A to 575 A, commercial submerged additive metals, and commercial aglomera welding powders. A notch impact test was carried on to determine the strength of the joints. Microhardness measurements were made at a Vickers load of 500 g. Optical microscopy and EDS analyses were utilized in the weld zone to investigate the microstructure changes which depend on the welding parameters. The results of this study indicate that P460 steel maintained sufficiently good weldability by application of the submerged welding process.
Industrial Lubrication and Tribology, 2012
PurposeThe purpose of this paper is to investigate interface characterization of CO2 laser welded... more PurposeThe purpose of this paper is to investigate interface characterization of CO2 laser welded AISI 304 austenitic stainless steel and AISI 1010 low carbon steel couple. Laser welding experiments were carried under argon and helium atmospheres at 2000, 2250 and 2500 W heat inputs and 200‐300 cm/min welding speeds.Design/methodology/approachThe microstructures of the welded joints and the heat affected zones (HAZ) were examined by optical microscopy, SEM, EDS and X‐Ray analysis. The tensile strength of the welded joints was measured.FindingsThe result of this study indicated that the width of welding zone and HAZ became much thinner depending on the increased welding speed. On the other hand, this width widened depending on the increased heat input. Tensile strength values also confirmed this result. The best properties were observed at the specimens welded under helium atmosphere, at 2500 W heat input and at 200 cm/min welding speed.Originality/valueThere are many reports which d...
DÜMF Mühendislik Dergisi, 2019
Toz metalurjisi ile elde edilen urunler son yillarda ozellikle otomobil ve havacilik olmak uzere ... more Toz metalurjisi ile elde edilen urunler son yillarda ozellikle otomobil ve havacilik olmak uzere bircok alanda yaygin olarak kullanilmaktadir. Toz metalurjisi uretim yontemi tum dunyada oldugu gibi ulkemizde de hizla gelismektedir. Bununla birlikte artan rekabet ve kalite ihtiyaci ureticileri hem ekonomik hem de dayanikli urunler uretmeye zorlamaktadir. Bu calismada, toz metalurjisinde sicakligin ekstruzyon edilebilirlige etkisi incelenerek yuksek dayanima sahip urunlerin elde edilmesi amaclanmaktadir. Toz metalurjisi ile uretilen aluminyum biyetler farkli sicaklikta ekstruzyon edilmis ve sonrasinda elde edilen numunelerin mikro yapilari incelenmistir. Mikro yapi incelemesi ile ekstruzyon kalip giris bolgesinde ve kalip cikisinda olusan yapi gozlenmistir. Bununla birlikte, farkli sicakliklarda ekstruzyon edilmis numunelerin sertlik degisimi ve kesme mukavemeti degerleri karsilastirilmistir.
GR2 ve GR5 (Ti6Al4V) titanyum alaşımları üstün mühendislik özellikleri nedeniyle özellikle biyome... more GR2 ve GR5 (Ti6Al4V) titanyum alaşımları üstün mühendislik özellikleri nedeniyle özellikle biyomedikal (ortopedi, cerrahi malzemeler ve implantlar), uçak gövde iskeletlerinde, uzay ve metal-malzeme endüstrisinde sıklıkla kullanılmaktadır. Titanyum malzemelerin yüksek süperplastik deformasyon özelliği, çeliğe göre korozyona daha dayanıklı olması, düşük yoğunluğu, yüksek korozyon direnci istenen yerlerde manyetik olmayan bu alaşımların mükemmel yapısı malzeme teknolojisinin gelişmesiyle önemini daha da artırmıştır. Bu çalışmada GR2 ve GR5 (Ti6Al4V) çubuk malzemeler alüminyum ara tabaka kullanılarak difüzyon yöntemiyle kaynaklanmış ve kaynak sıcaklığının bağlantı üzerindeki etkisi incelenmiştir. Malzeme çiftleri 5 MPa basınçla silisyum çubuklu fırında argon gaz ortamında 55 dk'lık sabit kaynak süresi ve 850-900 ve 950 °C'lik sıcaklıklarda birleştirilmişlerdir. Birleştirilen numunelerin SEM-EDS analizleri yapılmış difüzyondan etkilenen bölgedeki aratabakanın optik mikroskopla metalografik yapısı incelenmiş ve XRD analizi yapılarak olası fazlar belirlenmeye çalışılmıştır. Bağlantı bölgesinin bindirme-kayma mukavemet ve mikro sertlik değerleri incelenmiş en yüksek mekanik özellikler T3 numunesinde elde edilmiştir.
In this study, the effect of welding temperatures on the TLP diffusion bonding of Ni-Ti-Cu compos... more In this study, the effect of welding temperatures on the TLP diffusion bonding of Ni-Ti-Cu composites manufactured by cold pressing method was investigated. Composite materials have been produced with proportions by mixing 44±5µm Ni-Ti-Cu powders. Diffusion bonding experiments were carried out in argon atmosphere at 910-940 and 970 oC and 5 MPa under a dynamic load for at 60 constant durations. The microstructure of the join was examined by optic analysis, SEM and X-Ray. The strength of the joint tested by shear-lap and microhardness tests. The result of all observations, tests and measurements indicated that the quality of the coalescence at interfaces a homogenous Ni-Ti-Cu distribution and high interlayer diffusion. The result of all observations, tests and measurements indicated that the quality of the coalescence at interfaces at elevated temperatures.
Titanyum ve magnezyum gibi hafif malzemelerin, havacilik, tibbi implantlar ve hafif yapi gibi ces... more Titanyum ve magnezyum gibi hafif malzemelerin, havacilik, tibbi implantlar ve hafif yapi gibi cesitli teknik uygulamalarda cok onemli oldugu iyi bilinmektedir. Magnezyum otomotiv, uzay ve havacilik sektorunde, dusuk yogunlugu ve yuksek ozgul isi kapasitesi nedeniyle kullanimi gittikce artmaktadir. Butun stabil metallerin en hafiflerinden biri olmasi nedeniyle ozellikle tercih edilmektedir. Magnezyum ve alasimlarinin kaynagi, endustrilerdeki artan uygulamalari nedeniyle onemli bir konudur. Bu calismada toz metalurjisi yontemi ile uretilmis Mg-Ti alasiminin kati faz difuzyon kaynagi ile birlestirilebilirligi ve birlesmeye ara tabakanin etkisi arastirilmistir. Difuzyon kaynagi ile birlestirilmis numuneler mikroskop ile incelenmis ve birlesme bolgesinde olusabilecek difuzyon analiz edilmistir. Elde edilen numuneler argon atmosferli firinda 450 oC sicaklikta 60 dk. sinterlenerek difuzyon kaynagina uygun hale getirilmistir. Numuneler; 500, 520 ve 540 oC sicakliklarda, 75 dakika sureyle, 5...
DÜMF Mühendislik Dergisi, Mar 15, 2019
Bu calismada, toz metalurjisi yontemiyle uretilmis Ni-Ti-Cu kompozitlerinin difuzyon kaynaginda s... more Bu calismada, toz metalurjisi yontemiyle uretilmis Ni-Ti-Cu kompozitlerinin difuzyon kaynaginda sicaklik, sure ve aratabaka degerlerinin bindirme-kayma degerlerine etkisi istatistiki olarak arastirildi. Ni-Ti-Cu kompoziti ortalama 45±5µm Ni-Ti ve 37–105±5 µm Cu tozlarindan uretildi. Difuzyon kaynaklari argon koruyucu gaz atmosferinde, 5 MPa'lik dinamik yukleme ile 40 ve 60 dk.'lik surelerde ve 910-940 ve 970oC'lik sicakliklarda Ni ve Cu aratabaka kullanilarak yapildi. Deneyler sonucunda mikroyapi ozellikleri optik mikroskop, SEM-EDS ve X-Ray analizleri ile incelendi. Numunelerin birlesme mukavemetini incelemek icin bindirme-kayma testleri yapildi. Test sonuclari, Cok Degiskenli Iki Yonlu Varyans Analizi (MANOVA) yontemi ile degerlendirildi. Sonuc olarak, sicaklik, sure ve aratabaka degerleri ile bindirme-kayma degerlendirmeleri arasinda %85 oraninda anlamli bir farkliligin oldugu tespit edilmistir. Bu farklilik Ni ve Cu aratabaka kullaniminin bindirme-kayma acisindan anl...
The International Journal of Advanced Manufacturing Technology, Dec 2, 2008
Dicle üniversitesi mühendislik fakültesi mühendislik dergisi, Mar 15, 2019
Dicle üniversitesi mühendislik fakültesi mühendislik dergisi, Apr 4, 2018
DergiPark (Istanbul University), May 1, 2008
In this study, the effect on the connecting characteristic of welding temperatures on the joining... more In this study, the effect on the connecting characteristic of welding temperatures on the joining with the diffusion bonding using Ni and Cu interlayer of Ni-Ti-Cu composites manufactured by powder metallurgy method has been investigated. Composite materials have been produced with proportions by mixing 44±5µm Ni-Ti and 37-105±5 µm Cu powders. Diffusion bonding experiments have been carried out in argon atmosphere at the temperatures 910-940 and 970 ºC and 5 MPa under a dynamic load for at 60 min. constant holding time. The properties of microstructure occurred in the interface zone of the bonds of the joints have been examined by optic analysis, EDS and X-Ray. The strength of the joint has been tested by lap-shear and microhardness tests. The result of all observations has been indicated a homogenous Ni-Ti-Cu distribution and the quality of the coalescence at interfaces at elevated temperatures.
Advanced Composites Letters, 2020
The stainless steel 304L (commercially supplied) and Monel K-500 that was prepared through cold p... more The stainless steel 304L (commercially supplied) and Monel K-500 that was prepared through cold pressing of metal matrix composite materials powder mixtures were joined by diffusion welding. Welding was performed under uniaxial compression using the 50 mm-thick nickel (Ni) and aluminum (Al) 2024 interlayers under 3 MPa at 950-980 C for 60 min in an argon gas atmosphere. After welding, the diffusion and intermediate zones of the samples were characterized using X-ray diffraction, optical microscopy, scanning electron microscopy, and energy-dispersive spectrometry analysis. As evaluating the diffusion zone with interlayer, it was determined that different interlayers expanded due to increasing temperature of the diffusion area. Interlayers expanded more on the K-500 side and relatively less on the 304L side. On the other hand, when samples with Ni interlayers were examined, high amount of Ni contained by both base material (304L) and interlayer led to the formation of rich Ni phases in the diffusion side. The brittle FeNi,
Dicle üniversitesi mühendislik fakültesi mühendislik dergisi, Sep 1, 2017
MP MATERIALPRUEFUNG - MP MATERIALS TESTING, Dec 20, 2019
In this study, the weldability of P460 and S355 steel was investigated by application of the subm... more In this study, the weldability of P460 and S355 steel was investigated by application of the submerged arc welding (SAW) process. In the analyses, the effects of various parameters were handled at different welding speeds, the two levels of the current values of 475 A to 525 A and 525 A to 575 A, commercial submerged additive metals, and commercial aglomera welding powders. A notch impact test was carried on to determine the strength of the joints. Microhardness measurements were made at a Vickers load of 500 g. Optical microscopy and EDS analyses were utilized in the weld zone to investigate the microstructure changes which depend on the welding parameters. The results of this study indicate that P460 steel maintained sufficiently good weldability by application of the submerged welding process.
Industrial Lubrication and Tribology, Jun 15, 2012
DÜMF Mühendislik Dergisi
GR5 (Ti6Al4V) is a material commonly used in aerospace and space, biomedical and automobile secto... more GR5 (Ti6Al4V) is a material commonly used in aerospace and space, biomedical and automobile sectors, consisting of pure titanium at a minimum of 99% purity. Besides being lightweight, GR5 is separate from similar materials with its ability to resist corrosion at high levels and show high strength. SX steel is high silicon-content austenitic stainless steel with the ability of good quality of welding and excellent corrosion resistance in high concentration sulfuric acid and nitric acid. SX is used in areas such as acid coolers, acid piping systems, acid distributors, acid towers and tanks, pumps, nozzles, internals, strainers and mesh pads. With improving technology, the need for steel-titanium materials that are resisted to acid and made with welded joint is increasing. In this study, the effect of GR and SX materials of welding temperature on the connection is examined with diffusion welding method using copper intermediary layer. The material pairs are combined with a pressure of ...
Dicle üniversitesi mühendislik fakültesi mühendislik dergisi, Dec 6, 2022
Paslanmaz çelikler mimari yapılarda, inşaat, otomotiv, ulaşım, gıda ve medikal gibi birçok sektör... more Paslanmaz çelikler mimari yapılarda, inşaat, otomotiv, ulaşım, gıda ve medikal gibi birçok sektörde geniş bir kullanım ağına sahip bir malzemedir. Bu malzemelerin korozyon direncinin yüksek olması, bakım maliyetlerinin düşük olması, mükemmel süneklikleri, kırılmadan önemli darbeleri emebilmeleri ve estetik görüntü sunması bu malzemeleri cazip kılmaktadır. Paslanmaz çeliklerin metalürjisi karmaşıktır ve üretim sürecinin nihai özellikleri üzerinde daha yüksek bir etkisi vardır. Üretim süreçlerinde kazandırılan bu özellikler, östenitik 304 kalite malzemeler kaynak yapılabilirliği yüksek, 430 kalite ferritik paslanmaz çelikler ise kaynaklanma kabiliyetlerini azaltan etkiye neden olur. Bu çalışmada farklı kaynaklanma kabiliyetine sahip 304 ve 430 kalite paslanmaz çeliklerin katı faz difüzyon kaynağı ile birleştirilebilirliği ve birleşmeye ara tabakanın etkisi araştırılmıştır. Numuneler 960, 980 ve 1000ºC sıcaklıkta ve 45, 60 ve 75 dakika sürelerde, 1, 2 ve 3 MPa basınç altında atmosfer kontrollü fırında bakır ara tabaka kullanılarak difüzyon kaynağı tekniğiyle birleştirilmiştir. Numunelerin kaynak bölgesi mikroskopla, incelenmiş ve difüzyon alanındaki bakır ara tabakanın ana malzemelere dağılımı gözlenmiştir. Malzemelerin mekanik mukavemetlerini belirlemek için mikro sertlik ve çekme testleri uygulanmıştır, deneylerde Taguchi optimizasyon yöntemi ile Varyans (Anova) analizleri yapılıp en etkili parametreler bulunmuş ve deneyin güvenilirlik seviyesi tespit edilmeye çalışılmıştır.
Materials Testing, 2019
In this study, the weldability of P460 and S355 steel was investigated by application of the subm... more In this study, the weldability of P460 and S355 steel was investigated by application of the submerged arc welding (SAW) process. In the analyses, the effects of various parameters were handled at different welding speeds, the two levels of the current values of 475 A to 525 A and 525 A to 575 A, commercial submerged additive metals, and commercial aglomera welding powders. A notch impact test was carried on to determine the strength of the joints. Microhardness measurements were made at a Vickers load of 500 g. Optical microscopy and EDS analyses were utilized in the weld zone to investigate the microstructure changes which depend on the welding parameters. The results of this study indicate that P460 steel maintained sufficiently good weldability by application of the submerged welding process.
Industrial Lubrication and Tribology, 2012
PurposeThe purpose of this paper is to investigate interface characterization of CO2 laser welded... more PurposeThe purpose of this paper is to investigate interface characterization of CO2 laser welded AISI 304 austenitic stainless steel and AISI 1010 low carbon steel couple. Laser welding experiments were carried under argon and helium atmospheres at 2000, 2250 and 2500 W heat inputs and 200‐300 cm/min welding speeds.Design/methodology/approachThe microstructures of the welded joints and the heat affected zones (HAZ) were examined by optical microscopy, SEM, EDS and X‐Ray analysis. The tensile strength of the welded joints was measured.FindingsThe result of this study indicated that the width of welding zone and HAZ became much thinner depending on the increased welding speed. On the other hand, this width widened depending on the increased heat input. Tensile strength values also confirmed this result. The best properties were observed at the specimens welded under helium atmosphere, at 2500 W heat input and at 200 cm/min welding speed.Originality/valueThere are many reports which d...
DÜMF Mühendislik Dergisi, 2019
Toz metalurjisi ile elde edilen urunler son yillarda ozellikle otomobil ve havacilik olmak uzere ... more Toz metalurjisi ile elde edilen urunler son yillarda ozellikle otomobil ve havacilik olmak uzere bircok alanda yaygin olarak kullanilmaktadir. Toz metalurjisi uretim yontemi tum dunyada oldugu gibi ulkemizde de hizla gelismektedir. Bununla birlikte artan rekabet ve kalite ihtiyaci ureticileri hem ekonomik hem de dayanikli urunler uretmeye zorlamaktadir. Bu calismada, toz metalurjisinde sicakligin ekstruzyon edilebilirlige etkisi incelenerek yuksek dayanima sahip urunlerin elde edilmesi amaclanmaktadir. Toz metalurjisi ile uretilen aluminyum biyetler farkli sicaklikta ekstruzyon edilmis ve sonrasinda elde edilen numunelerin mikro yapilari incelenmistir. Mikro yapi incelemesi ile ekstruzyon kalip giris bolgesinde ve kalip cikisinda olusan yapi gozlenmistir. Bununla birlikte, farkli sicakliklarda ekstruzyon edilmis numunelerin sertlik degisimi ve kesme mukavemeti degerleri karsilastirilmistir.
GR2 ve GR5 (Ti6Al4V) titanyum alaşımları üstün mühendislik özellikleri nedeniyle özellikle biyome... more GR2 ve GR5 (Ti6Al4V) titanyum alaşımları üstün mühendislik özellikleri nedeniyle özellikle biyomedikal (ortopedi, cerrahi malzemeler ve implantlar), uçak gövde iskeletlerinde, uzay ve metal-malzeme endüstrisinde sıklıkla kullanılmaktadır. Titanyum malzemelerin yüksek süperplastik deformasyon özelliği, çeliğe göre korozyona daha dayanıklı olması, düşük yoğunluğu, yüksek korozyon direnci istenen yerlerde manyetik olmayan bu alaşımların mükemmel yapısı malzeme teknolojisinin gelişmesiyle önemini daha da artırmıştır. Bu çalışmada GR2 ve GR5 (Ti6Al4V) çubuk malzemeler alüminyum ara tabaka kullanılarak difüzyon yöntemiyle kaynaklanmış ve kaynak sıcaklığının bağlantı üzerindeki etkisi incelenmiştir. Malzeme çiftleri 5 MPa basınçla silisyum çubuklu fırında argon gaz ortamında 55 dk'lık sabit kaynak süresi ve 850-900 ve 950 °C'lik sıcaklıklarda birleştirilmişlerdir. Birleştirilen numunelerin SEM-EDS analizleri yapılmış difüzyondan etkilenen bölgedeki aratabakanın optik mikroskopla metalografik yapısı incelenmiş ve XRD analizi yapılarak olası fazlar belirlenmeye çalışılmıştır. Bağlantı bölgesinin bindirme-kayma mukavemet ve mikro sertlik değerleri incelenmiş en yüksek mekanik özellikler T3 numunesinde elde edilmiştir.
In this study, the effect of welding temperatures on the TLP diffusion bonding of Ni-Ti-Cu compos... more In this study, the effect of welding temperatures on the TLP diffusion bonding of Ni-Ti-Cu composites manufactured by cold pressing method was investigated. Composite materials have been produced with proportions by mixing 44±5µm Ni-Ti-Cu powders. Diffusion bonding experiments were carried out in argon atmosphere at 910-940 and 970 oC and 5 MPa under a dynamic load for at 60 constant durations. The microstructure of the join was examined by optic analysis, SEM and X-Ray. The strength of the joint tested by shear-lap and microhardness tests. The result of all observations, tests and measurements indicated that the quality of the coalescence at interfaces a homogenous Ni-Ti-Cu distribution and high interlayer diffusion. The result of all observations, tests and measurements indicated that the quality of the coalescence at interfaces at elevated temperatures.
Titanyum ve magnezyum gibi hafif malzemelerin, havacilik, tibbi implantlar ve hafif yapi gibi ces... more Titanyum ve magnezyum gibi hafif malzemelerin, havacilik, tibbi implantlar ve hafif yapi gibi cesitli teknik uygulamalarda cok onemli oldugu iyi bilinmektedir. Magnezyum otomotiv, uzay ve havacilik sektorunde, dusuk yogunlugu ve yuksek ozgul isi kapasitesi nedeniyle kullanimi gittikce artmaktadir. Butun stabil metallerin en hafiflerinden biri olmasi nedeniyle ozellikle tercih edilmektedir. Magnezyum ve alasimlarinin kaynagi, endustrilerdeki artan uygulamalari nedeniyle onemli bir konudur. Bu calismada toz metalurjisi yontemi ile uretilmis Mg-Ti alasiminin kati faz difuzyon kaynagi ile birlestirilebilirligi ve birlesmeye ara tabakanin etkisi arastirilmistir. Difuzyon kaynagi ile birlestirilmis numuneler mikroskop ile incelenmis ve birlesme bolgesinde olusabilecek difuzyon analiz edilmistir. Elde edilen numuneler argon atmosferli firinda 450 oC sicaklikta 60 dk. sinterlenerek difuzyon kaynagina uygun hale getirilmistir. Numuneler; 500, 520 ve 540 oC sicakliklarda, 75 dakika sureyle, 5...
DÜMF Mühendislik Dergisi, Mar 15, 2019
Bu calismada, toz metalurjisi yontemiyle uretilmis Ni-Ti-Cu kompozitlerinin difuzyon kaynaginda s... more Bu calismada, toz metalurjisi yontemiyle uretilmis Ni-Ti-Cu kompozitlerinin difuzyon kaynaginda sicaklik, sure ve aratabaka degerlerinin bindirme-kayma degerlerine etkisi istatistiki olarak arastirildi. Ni-Ti-Cu kompoziti ortalama 45±5µm Ni-Ti ve 37–105±5 µm Cu tozlarindan uretildi. Difuzyon kaynaklari argon koruyucu gaz atmosferinde, 5 MPa'lik dinamik yukleme ile 40 ve 60 dk.'lik surelerde ve 910-940 ve 970oC'lik sicakliklarda Ni ve Cu aratabaka kullanilarak yapildi. Deneyler sonucunda mikroyapi ozellikleri optik mikroskop, SEM-EDS ve X-Ray analizleri ile incelendi. Numunelerin birlesme mukavemetini incelemek icin bindirme-kayma testleri yapildi. Test sonuclari, Cok Degiskenli Iki Yonlu Varyans Analizi (MANOVA) yontemi ile degerlendirildi. Sonuc olarak, sicaklik, sure ve aratabaka degerleri ile bindirme-kayma degerlendirmeleri arasinda %85 oraninda anlamli bir farkliligin oldugu tespit edilmistir. Bu farklilik Ni ve Cu aratabaka kullaniminin bindirme-kayma acisindan anl...