Papers by Riza Kara
2022 10th International Symposium on Digital Forensics and Security (ISDFS)
In this study, Hardox 500 steels, which draw attention with their wear resistance and mechanical ... more In this study, Hardox 500 steels, which draw attention with their wear resistance and mechanical properties, were subjected to box boring process at different temperatures and times. Boronizing process was carried out at 850, 900 and 950 C temperatures and for 2, 4, and 6 hours for each boring temperature. The morphology of the boron layer formed on the sample surfaces as a result of the boronization process was examined by SEM microscope. Boron phases formed by measuring the Vickers hardness values were analyzed by X-Ray diffraction technique (XRD). It was observed that the boride layer formed according to the XRD analysis consisted of a single phase Fe2B structure. It was observed that the boride layer thickness in Hardox 500 steel increased with the increasing boronization temperature and duration. The abrasion tests were carried out using the ball disc wear method at a sliding speed of 0.3 m / s under a load of 10 N in a dry environment and a sliding distance of 500 meters. As a...
El-Cezeri: Journal of Science and Engineering, Jan 31, 2017
Doğalgaz kullanımının yaygınlaşması ile birlikte tesisat işlemlerinde kaynaklı birleştirme kalite... more Doğalgaz kullanımının yaygınlaşması ile birlikte tesisat işlemlerinde kaynaklı birleştirme kalitesi önem kazanmıştır. Bu çalışmada çelik doğalgaz borularının kaynak kabiliyeti araştırılmıştır. Çalışmada API5L X52 kalite 1/2 inç yarıçapında 2,8 mm et kalınlığına sahip borular 100 mm boyutlarında hazırlanmıştır. Hazırlanan numuneler Oksi-Gaz, elektrik ark kaynağı ve MAG (Gaz altı) kaynak yöntemleriyle birleştirilmiştir. Farklı kaynak yöntemleriyle birleştirilen kaynaklı numuneler mikroyapı, sertlik, çekme ve yorulma deneyleri ile karakterize edilmiştir.
Page 1. www.teknolojikarastirmalar.com ISSN:1304-4141 Makine Teknolojileri Elektronik Dergisi 200... more Page 1. www.teknolojikarastirmalar.com ISSN:1304-4141 Makine Teknolojileri Elektronik Dergisi 2006 (4) 45-52 TEKNOLOJİK ARAŞTIRMALAR Kısa Makale Difüzyon Kaynağı İle Birleştirilen Fe-Cu Çiftinin Mekanik Özelliklerinin İncelenmesi ...
2022 10th International Symposium on Digital Forensics and Security (ISDFS)
In this study, Hardox 500 steels, which draw attention with their wear resistance and mechanical ... more In this study, Hardox 500 steels, which draw attention with their wear resistance and mechanical properties, were subjected to box boring process at different temperatures and times. Boronizing process was carried out at 850, 900 and 950 C temperatures and for 2, 4, and 6 hours for each boring temperature. The morphology of the boron layer formed on the sample surfaces as a result of the boronization process was examined by SEM microscope. Boron phases formed by measuring the Vickers hardness values were analyzed by X-Ray diffraction technique (XRD). It was observed that the boride layer formed according to the XRD analysis consisted of a single phase Fe2B structure. It was observed that the boride layer thickness in Hardox 500 steel increased with the increasing boronization temperature and duration. The abrasion tests were carried out using the ball disc wear method at a sliding speed of 0.3 m / s under a load of 10 N in a dry environment and a sliding distance of 500 meters. As a...
El-Cezeri: Journal of Science and Engineering, Jan 31, 2017
Doğalgaz kullanımının yaygınlaşması ile birlikte tesisat işlemlerinde kaynaklı birleştirme kalite... more Doğalgaz kullanımının yaygınlaşması ile birlikte tesisat işlemlerinde kaynaklı birleştirme kalitesi önem kazanmıştır. Bu çalışmada çelik doğalgaz borularının kaynak kabiliyeti araştırılmıştır. Çalışmada API5L X52 kalite 1/2 inç yarıçapında 2,8 mm et kalınlığına sahip borular 100 mm boyutlarında hazırlanmıştır. Hazırlanan numuneler Oksi-Gaz, elektrik ark kaynağı ve MAG (Gaz altı) kaynak yöntemleriyle birleştirilmiştir. Farklı kaynak yöntemleriyle birleştirilen kaynaklı numuneler mikroyapı, sertlik, çekme ve yorulma deneyleri ile karakterize edilmiştir.
Page 1. www.teknolojikarastirmalar.com ISSN:1304-4141 Makine Teknolojileri Elektronik Dergisi 200... more Page 1. www.teknolojikarastirmalar.com ISSN:1304-4141 Makine Teknolojileri Elektronik Dergisi 2006 (4) 45-52 TEKNOLOJİK ARAŞTIRMALAR Kısa Makale Difüzyon Kaynağı İle Birleştirilen Fe-Cu Çiftinin Mekanik Özelliklerinin İncelenmesi ...