Metals
In this paper, Inconel 718 (IN718) superalloy was processed by laser powder-bed fusion additive m... more In this paper, Inconel 718 (IN718) superalloy was processed by laser powder-bed fusion additive manufacturing (L-PBFAM), followed by heat treatment. High-resolution nanoindentation was used to investigate the complex deformation mechanisms that occurred at various length scales in both conditions. The nanoindentation elastoplastic maps show a strong crystal orientation dependency of modulus and hardness, which is attributed to the high mechanical anisotropy of IN718. The hardness map effectively resolves complex microscale strength variation imparted due to the hierarchical heat distribution associated with the thermal cycles of L-PBFAM. The disproportionately high hardening effect of Nb, Mo-rich chemical segregations and Laves phases in dendritic structures is also observed. The heat treatment resulted in a 67% increase in yield strength (from 731 MPa in the L-PBFAM condition to 1217 MPa in the heat-treated condition) due to the activation of multiple precipitation-strengthening me...
Metals
In this paper, Inconel 718 (IN718) superalloy was processed by laser powder-bed fusion additive m... more In this paper, Inconel 718 (IN718) superalloy was processed by laser powder-bed fusion additive manufacturing (L-PBFAM), followed by heat treatment. High-resolution nanoindentation was used to investigate the complex deformation mechanisms that occurred at various length scales in both conditions. The nanoindentation elastoplastic maps show a strong crystal orientation dependency of modulus and hardness, which is attributed to the high mechanical anisotropy of IN718. The hardness map effectively resolves complex microscale strength variation imparted due to the hierarchical heat distribution associated with the thermal cycles of L-PBFAM. The disproportionately high hardening effect of Nb, Mo-rich chemical segregations and Laves phases in dendritic structures is also observed. The heat treatment resulted in a 67% increase in yield strength (from 731 MPa in the L-PBFAM condition to 1217 MPa in the heat-treated condition) due to the activation of multiple precipitation-strengthening me...