GaN: C multi-heterostructure at different temperature (original) (raw)

Chinese Physics B, 2020

Abstract

The graded AlGaN:Si back barrier can form the majority of three-dimensional electron gases (3DEGs) at the GaN/graded AlGaN:Si heterostructure and create a composite two-dimensional (2D)–three-dimensional (3D) channel in AlGaN/GaN/graded-AlGaN:Si/GaN:C heterostructure (DH:Si/C). Frequency-dependent capacitances and conductance are measured to investigate the characteristics of the multi-temperature trap states of in DH:Si/C and AlGaN/GaN/GaN:C heterostructure (SH:C). There are fast, medium, and slow trap states in DH:Si/C, while only medium trap states exist in SH:C. The time constant/trap density for medium trap state in SH:C heterostructure are (11 μs–17.7 μs)/(1.1 × 1013 cm−2·eV−1–3.9× 1013 cm−2·eV−1) and (8.7 μs–14.1 μs)/(0.7× 1013 cm−2·eV−1–1.9× 1013 cm−2·eV−1) at 300 K and 500 K respectively. The time constant/trap density for fast, medium, and slow trap states in DH:Si/C heterostructure are (4.2 μs–7.7 μs)/(1.5× 1013 cm−2·eV−1–3.2× 1013 cm−2·eV−1), (6.8 μs–11.8 μs)/(0.8× 1013 ...

Jie Zhu hasn't uploaded this paper.

Let Jie know you want this paper to be uploaded.

Ask for this paper to be uploaded.