Impact of Nanoparticles Additions on the Strength of Dental Composite Resin (original) (raw)

International Journal of Biomaterials

Objective. This study aimed to evaluate the effect of nanoparticles, zirconium dioxide (ZrO2), titanium dioxide (TiO2), and silicon dioxide (SiO2), on flexural strength (FS), hardness, and wear resistance of light cured dental composite resin. Materials and Methods. 210 rectangular and disc-shaped composite resin specimens were fabricated with dimensions (25 × 2 × 2 ± 0.03 mm) and (6×4 ± 0.03 mm) for FS, hardness, and wear resistance, respectively (70/test). Specimens of each test were divided according to nanofillers into four groups, unmodified as control, ZrO2 (Z), TiO2 (T), and SiO2 (S) groups; each one was further subdivided into two subgroups according to nanoparticles concentration, 3wt.% and 7wt.% (Z3, Z7, T3, T7, S3, and S7), 10 specimens of each subgroup. A3-point bending test and Vickers hardness test were used for FS and hardness measurements, respectively. Wear resistance was evaluated by the differences in surface roughness of tested specimens before and after wear tes...