Polypropylene Degradation on Co-Rotating Twin-Screw Extruders (original) (raw)
Related papers
The Impact of Reprocessing with a Quad Screw Extruder on the Degradation of Polypropylene
Polymers
During mechanical recycling, polypropylene typically is reprocessed using a single- or twin-screw extruder. The degradation of polypropylene during this reprocessing reduces the polymer’s molecular weight and, consequently, limits the performance of the recycled resin. This work investigated the impact of a quad screw extruder (QSE), which has greater free volume, on the reprocessing of an impact copolymer polypropylene. To mimic the recycling process, the polypropylene was subjected to three processing cycles using a QSE and a comparable twin-screw extruder (TSE) operated at three screw speeds. The reprocessed materials were characterized for their rheological, morphological, and mechanical properties. For both extruders, increasing the number of reprocessing cycles and the screw speed resulted in higher melt flow indices, decreases in zero-shear viscosity, and shifting of the crossover points for the storage and loss moduli, which indicate reductions in the molecular weight and na...
Polymer Testing, 2007
The effects of repetitive extrusion cycles at different die temperatures in a single screw extruder were investigated by thermal analysis (degree of crystallinity (w c ), heat of fusion (DH m ), melting temperature (T m ) and the onset melting temperature (T onset,m )) and mechanical properties (tensile and impact strength). Also, analysis of variance (ANOVA) and response surface methodology (RSM) were employed for modeling and analysis of the mechanical property results. Thermal analysis verified an increase for w c and DH m with a continuous reduction in the T m and T onset,m values with increase of die temperature and/or cycles of extrusion. For mechanical properties, the observed degradation process only slightly affects the small strain properties (yield stress and modulus) and impact strength. Break properties (break stress, break strain and energy to break) were reduced significantly by the experimental conditions adopted. According to ANOVA and RSM, the degradation process was occasioned more by high shear rate (repetitive number of cycles) than by high processing temperatures. r
Journal of Plastic Film & Sheeting
The process dynamics of single-screw extrusion on mixtures of polypropylene (PP) and recycled PP were studied using a statistical, design of experiments (DoE) approach. For a conventional screw design, barrel temperature, screw speed and two vastly different melt viscosity PP mixtures were selected as the independent factors, whilst melt pressure, mass output, screw torque and temperature rise at the die due to shear heating, were the dependent responses. A central composite design (CCD) in the framework of response surface methodology (RSM) was constructed, and an analysis of variance (ANOVA) was carried out to determine the significance of the response surface models. The resulting statistical and response surface predictions have demonstrated that the low viscosity component concentration in the blend is a dominating factor on melt pressure and screw torque, apart from the expected effect of screw speed on output. Viscous heating is affected only by screw speed and recycled PP concentration. Furthermore, the predictions have identified a wider process operating window with increased low viscosity component concentration. The data confirms that statistical tools make quantitative predictions for the effects of experimental process variables, in accordance with the expected qualitative trends towards process optimisation, providing scope towards its application in scaled-up industrial processes.
Polymer Engineering & Science, 1999
Blends of high-density polyethylene (HDPE) and polypropylene (PP) were prepared in different twin-screw extruders. Two additives, a peroxide initiator and a polymerizable monomer, were added to the polymeric feed components. A large influence on the physical properties, such as toughness and impact strength,. and on the morphology was observed. Reactive extrusion substantially improves mechanical properties: a threefold increase of elongation at break and doubling of the impact strength. Variation of extruder settings also had a large influence on the product; the f i n a l properties were improved when the shear rate was raised, but sufficient residence time is necessary in reactive compatibilization. Scanning electron micrographs of the fracture surfaces of blends indicate a refinement of the surface structure.
Journal of Applied Polymer Science, 2006
An experimental study of the peroxide-induced degradation of polypropylene in a corotating twinscrew extruder, operating under various conditions, was reported. Runs were performed without and with peroxide in different concentrations. The evolution of the chemical reactions along the extruder was characterized by on-line rheological measurements and by determination of the molecular weight of samples collected at the same locations. The results evidenced the relationships between peroxide concentration and processing conditions with rheological properties and molecular structure of the modified materi-als. The concept of chain-scission distribution function elucidated the mechanisms involved in the thermomechanical degradation of PP, which is by chain scission and is dependent on the level of stress imposed by the screw elements, temperature, and concentration of hydrogen-abstracting agents.
Rheological properties of polypropylene during multiple extrusion
Polymer Testing, 2005
Polypropylene (PP) degradation during multiple extrusion at different temperatures was studied by following changes in rheological properties. Dynamic and transient experiments were carried out in a rheometer with parallel plate geometry. In addition, a statistical experimental design (2 2 , with replicates) was employed using die zone temperature (X 1) and number of extrusion cycles (X 2) varying at two levels. The system degradation was modeled using melt flow index (MFI) as a control variable. A rapid increase of chain scissions of the PP macromolecules and, consequently, a molecular weight reduction, was observed through abrupt increase of MFI and reduction of properties such as complex viscosity (h*) and elasticity of the molten polymer.
Melting of PP/PA6 Polymer Blends in Single Screw Extruders – An Experimental Study
Materials Science Forum, 2008
A prototype modular single screw extruder fitted with a screw extracting device is used to monitor melting of an immiscible polymer blend (PP/PA6, with different weight ratios) in this popular type of processing equipment. As anticipated, the observed phenomena are much more complex than those involved in extruding PP or PA6, when the well known Maddock/Tadmor mechanism is valid. Consequently a hybrid melting mechanism, involving Maddock/Tadmor and Dispersive melting sequences, is proposed.
The effect of cold and hot extrusion on the structure and mechanical properties of polypropylene
Journal of Materials Science, 1975
The direct extrusion of isotactic polypropylene through a 90 ~ die at 23, 65, 95 and 120~ has been studied. As a result of extrusion, the tensile strength and the elastic modulus of the material are considerably increased whereas the ductility is decreased. Owing to the deformation of the material occurring in the extrusion process, the c-axis of the monoclinic unit cell aligns itself parallel to the extrusion direction and the lamellar structure is orderly arranged. The tensile strength and the orientation of the material extruded at higher temperatures are much higher than those obtained by extrusion at room temperature. The changes in the density and the mechanical properties resulting from extrusion have been explained in terms of the structural changes occurring in the material. A method has been suggested for estimating the spring back of extruded material.