Dedifferentiated Human Articular Chondrocytes Redifferentiate to a Cartilage-Like Tissue Phenotype in a Poly(ε-Caprolactone)/Self-Assembling Peptide Composite Scaffold (original) (raw)
Related papers
Biomaterials, 2010
The goal of this study was to determine material effects on cartilage regeneration for scaffolds with the same controlled architecture. The 3D polycaprolactone (PCL), poly (glycerol sebacate) (PGS), and poly (1,8 octanediol-co-citrate) (POC) scaffolds of the same design were physically characterized and tissue regeneration in terms of cell phenotype, cellular proliferation and differentiation, and matrix production were compared to find which material would be most optimal for cartilage regeneration in vitro. POC provided the best support for cartilage regeneration in terms of tissue ingrowth, matrix production, and relative mRNA expressions for chondrocyte differentiation (Col2/Col1). PGS was seen as the least favorable material for cartilage based on its relatively high de-differentiation (Col1), hypertrophic mRNA expression (Col10) and high matrix degradation (MMP13, MMP3) results. PCL still provided microenvironments suitable for cells to be active yet it seemed to cause de-differentiation (Col1) of chondrocytes inside the scaffold while many cells migrated out, growing cartilage outside the scaffold.
Biomaterials, 2008
Compressive mechanical stimuli are crucial in regenerating cartilage with tissue engineering, which creates a need for scaffolds that can maintain their mechanical integrity while delivering mechanical signals to adherent cells during strain applications. With these goals in mind, the aim of this study was to develop a mechano-active scaffold that facilitated effective cartilaginous tissue formation under dynamic physiological environments. Using a gel-pressing method, we fabricated a biodegradable and highlyelastic scaffold from poly(L-lactide-co-3-caprolactone) (PLCL; 5:5), with 85% porosity and a 300-500-mm pore size, and we compared it to control scaffolds made of rigid polylactide (PLA) or poly(lactide-coglycolide) (PLGA). After tensile mechanical tests and recovery tests confirmed the elasticity of the PLCL scaffolds, we seeded them with rabbit chondrocytes, cultured them in vitro, and subcutaneously implanted them into nude mice for up to eight weeks. The PLCL scaffolds possessed a completely rubberlike elasticity, were easily twisted and bent, and exhibited an almost complete (over 97%) recovery from applied strain (up to 500%); the control PLA scaffolds showed little recovery. In vitro and in vivo accumulations of extracellular matrix on the cell-PLCL constructs demonstrated that they could not only sustain but also significantly enhance chondrogenic differentiation. Moreover, the mechanical stimulation of the dynamic in vivo environment promoted deposition of the chondral extracellular matrix onto the PLCL. In contrast, on the PLA scaffolds, most of the chondrocytes had de-differentiated and formed fibrous tissues. In a rabbit defect model, the groups treated with PLCL scaffolds exhibited significantly enhanced cartilage regeneration compared to groups harboring an empty control or PLGA scaffolds. These results indicated that the mechano-active PLCL scaffolds effectively delivered mechanical signals associated with biological environments to adherent chondrocytes, suggesting that these elastic PLCL scaffolds could successfully be used for cartilage regeneration.
Tissue Engineering and Regenerative Medicine, 2017
In this paper we report the differentiating properties of platelet-rich plasma releasates (PRPr) on human chondrocytes within elastomeric polycaprolactone triol-citrate (PCLT-CA) porous scaffold. Human-derived chondrocyte cellular content of glycosaminoglycans (GAGs) and total collagen were determined after seeding into PCLT-CA scaffold enriched with PRPr cells. Immunostaining and real time PCR was applied to evaluate the expression levels of chondrogenic and extracellular gene markers. Seeding of chondrocytes into PCLT-CA scaffold enriched with PRPr showed significant increase in total collagen and GAGs production compared with chondrocytes grown within control scaffold without PRPr cells. The mRNA levels of collagen II and SOX9 increased significantly while the upregulation in Cartilage Oligomeric Matrix Protein (COMP) expression was statistically insignificant. We also report the reduction of the expression levels of collagen I and III in chondrocytes as a consequence of proximity to PRPr cells within the scaffold. Interestingly, the pre-loading of PRPr caused an increase of expression levels of following extracellular matrix (ECM) proteins: fibronectin, laminin and integrin b over the period of 3 days. Overall, our results introduce the PCLT-CA elastomeric scaffold as a new system for cartilage tissue engineering. The method of PRPr cells loading prior to chondrocyte culture could be considered as a potential environment for cartilage tissue engineering as the differentiation and ECM formation is enhanced significantly. Keywords Cartilage tissue engineering Á PCLT-CA scaffolds Á PRPr cells Á Human chondrocytes Á ECM formation 1 Introduction Cartilage healing is a slow and sensitive process that often leads to a permanent cartilage defect. Cartilage repair is commonly suppressed by factors such as avascular condition of articular cartilage, limited chondrocytes in mature and aged tissue and inability of chondrocytes to migrate to the damaged site. In most cases, the fibro-cartilage would replace the damaged cartilage, which does not provide sustained repair and desirable mechanical support & Hussin A. Rothan
Chondroitin Sulfate- and Decorin-Based Self-Assembling Scaffolds for Cartilage Tissue Engineering
PloS one, 2016
Cartilage injury and degenerative tissue progression remain poorly understood by the medical community. Therefore, various tissue engineering strategies aim to recover areas of damaged cartilage by using non-traditional approaches. To this end, the use of biomimetic scaffolds for recreating the complex in vivo cartilage microenvironment has become of increasing interest in the field. In the present study, we report the development of two novel biomaterials for cartilage tissue engineering (CTE) with bioactive motifs, aiming to emulate the native cartilage extracellular matrix (ECM). We employed a simple mixture of the self-assembling peptide RAD16-I with either Chondroitin Sulfate (CS) or Decorin molecules, taking advantage of the versatility of RAD16-I. After evaluating the structural stability of the bi-component scaffolds at a physiological pH, we characterized these materials using two different in vitro assessments: re-differentiation of human articular chondrocytes (AC) and in...
Biomaterials, 2010
Three-dimensionally woven poly(ε-caprolactone)(PCL) scaffolds were combined with adult human mesenchymal stem cells (hMSC) to engineer mechanically functional cartilage constructs in vitro. The specific objectives were to: (i) produce PCL scaffolds with cartilage-like mechanical properties, (ii) demonstrate that hMSCs formed cartilage after 21-days of culture on PCL scaffolds, and (iii) study effects of scaffold structure (loosely vs. tightly woven), culture vessel (static dish vs. oscillating bioreactor), and medium composition (chondrogenic additives with or without serum). Aggregate moduli of 21-day constructs approached normal articular cartilage for tightly woven PCL cultured in bioreactors, were lower for tightly woven PCL cultured statically, and lowest for loosely woven PCL cultured statically (p<0.05). Construct DNA, total collagen, and glyocosaminoglycans (GAG) increased in a manner dependent on time, culture vessel, and medium composition. Chondrogenesis was verified histologically by rounded cells within a hyaline-like matrix that immunostained for collagen type II but not type I. Bioreactors yielded constructs with higher collagen content (p<0.05) and more homogenous matrix than static controls. Chondrogenic additives yielded constructs with higher GAG (p<0.05) and earlier expression of collagen II mRNA if serum was not present in medium. These results show feasibility of functional cartilage tissue engineering from hMSC and 3D woven PCL scaffolds. a Significant effect due to scaffold structure b Significant effect due to culture vessel c Significant effect due to presence of FBS in culture medium d Significant effect due to presence of chondrogenic additives in culture medium
Biomaterials, 2010
Three-dimensionally woven poly(ε-caprolactone)(PCL) scaffolds were combined with adult human mesenchymal stem cells (hMSC) to engineer mechanically functional cartilage constructs in vitro. The specific objectives were to: (i) produce PCL scaffolds with cartilage-like mechanical properties, (ii) demonstrate that hMSCs formed cartilage after 21-days of culture on PCL scaffolds, and (iii) study effects of scaffold structure (loosely vs. tightly woven), culture vessel (static dish vs. oscillating bioreactor), and medium composition (chondrogenic additives with or without serum). Aggregate moduli of 21-day constructs approached normal articular cartilage for tightly woven PCL cultured in bioreactors, were lower for tightly woven PCL cultured statically, and lowest for loosely woven PCL cultured statically (p<0.05). Construct DNA, total collagen, and glyocosaminoglycans (GAG) increased in a manner dependent on time, culture vessel, and medium composition. Chondrogenesis was verified histologically by rounded cells within a hyaline-like matrix that immunostained for collagen type II but not type I. Bioreactors yielded constructs with higher collagen content (p<0.05) and more homogenous matrix than static controls. Chondrogenic additives yielded constructs with higher GAG (p<0.05) and earlier expression of collagen II mRNA if serum was not present in medium. These results show feasibility of functional cartilage tissue engineering from hMSC and 3D woven PCL scaffolds. a Significant effect due to scaffold structure b Significant effect due to culture vessel c Significant effect due to presence of FBS in culture medium d Significant effect due to presence of chondrogenic additives in culture medium
Engineered articular cartilage: influence of the scaffold on cell phenotype and proliferation
Journal of materials science. Materials in medicine, 2003
Articular cartilage defects do not heal. Biodegradable scaffolds have been studied for cartilage engineering in order to implant autologous chondrocytes and help cartilage repair. We tested some new collagen matrices differing in collagen type, origin, structure and methods of extraction and purification, and compared the behavior of human chondrocytes cultured on them. Human chondrocytes were grown for three weeks on four different equine type I collagen matrices, one type I, III porcine collagen matrix and one porcine type II collagen matrix. After 21 days, samples were subjected to histochemical, immunohistochemical and histomorphometric analysis to study phenotype expression and cell adhesion. At 7, 14 and 21 days cell proliferation was studied by incorporation of [3H]-thymidine. Our data evidence that the collagen type influences cell morphology, adhesion and growth; indeed, cellularity and rate of proliferation were significantly higher and cells were rounder on the collagen I...
Biomaterials, 2013
An important tenet in designing scaffolds for regenerative medicine consists in mimicking the dynamic mechanical properties of the tissues to be replaced to facilitate patient rehabilitation and restore daily activities. In addition, it is important to determine the contribution of the forming tissue to the mechanical properties of the scaffold during culture to optimize the pore network architecture. Depending on the biomaterial and scaffold fabrication technology, matching the scaffolds mechanical properties to articular cartilage can compromise the porosity, which hampers tissue formation. Here, we show that scaffolds with controlled and interconnected pore volume and matching articular cartilage dynamic mechanical properties, are indeed effective to support tissue regeneration by co-cultured primary and expanded chondrocyte (1:4). Cells were cultured on scaffolds in vitro for 4 weeks. A higher amount of cartilage specific matrix (ECM) was formed on mechanically matching (M) scaffolds after 28 days. A less protein adhesive composition supported chondrocytes rounded morphology, which contributed to cartilaginous differentiation. Interestingly, the dynamic stiffness of matching constructs remained approximately at the same value after culture, suggesting a comparable kinetics of tissue formation and scaffold degradation. Cartilage regeneration in matching scaffolds was confirmed subcutaneously in vivo. These results imply that mechanically matching scaffolds with appropriate physico-chemical properties support chondrocyte differentiation.
Cartilage Tissue Engineering Using Self-Assembling Peptides Composite Scaffolds
2019
Adult articular cartilage presents poor intrinsic capacity for regeneration, and after injury, cellular or biomaterial-based therapeutic platforms are required to assist repair promotion. Cartilage tissue engineering (CTE) aims to produce cartilage-like tissues that recreate the complex mechanical, biophysical and biological properties found in vivo. In terms of biomaterials used for CTE, threedimensional (3D) self-assembling peptide scaffolds (SAPS) are very attractive for their unique properties, such as biocompatibility, optional possibility of rationally design cell-signaling capacity, biodegradability and modulation of its biomechanical properties. The most attractive cell types currently used for CTE are autologous chondrocytes and adult stem cells. The use of chondrocytes in cell-based therapies for cartilage lesions is limited by quantity and requires an in vitro 2D expansion, which leads to cell dedifferentiation. In the present chapter, we report the development of heparin-, chondroitin sulfate-, decorin-, and poly(ε-caprolactone)-based self-assembling peptide composite scaffolds to promote re-differentiation of expanded human articular chondrocytes and induction of adipose-derived stem cells to chondrogenic commitment.
Regenerative Engineering and Translational Medicine, 2015
Articular cartilage remains a significant clinical challenge to repair because of its limited selfhealing capacity. Interest has grown in the delivery of autologous chondrocytes to cartilage defects, and combining cell-based therapies with scaffolds that capture aspects of native tissue and allow cell-mediated remodeling could improve outcomes. Currently, scaffold-based therapies with encapsulated chondrocytes permit matrix production; however, resorption of the scaffold often does not match the rate of matrix production by chondrocytes, which can limit functional tissue regeneration. Here, we designed a hybrid biosynthetic system consisting of poly (ethylene glycol) (PEG) endcapped with thiols and crosslinked by norbornene-functionalized gelatin via a thiol-ene photopolymerization. The protein crosslinker was selected to facilitate chondrocyte-mediated scaffold remodeling and matrix deposition. Gelatin was functionalized with norbornene to varying degrees (~4-17 norbornenes/gelatin), and the shear modulus of the resulting hydrogels was characterized (<0.1-0.5 kPa). Degradation of the crosslinked PEG-gelatin hydrogels by chondrocyte-secreted enzymes was confirmed by gel permeation chromatography. Finally, chondrocytes encapsulated in these biosynthetic scaffolds showed significantly increased glycosaminoglycan deposition over just 14 days of culture, while maintaining high levels of viability and producing a distributed matrix. These results indicate the potential of a hybrid PEGgelatin hydrogel to permit chondrocyte-mediated remodeling and promote articular cartilage