Rapid synthesis of interconnected CuCrO 2 nanostructures: A promising electrode material for photoelectrochemical fuel generation (original) (raw)
Related papers
Sains Malaysiana
The process of carbon dioxide (CO 2 ) reduction by using efficient non-precious-metal catalyst to make the process be economical has brought a comprehensive research in the area. In this study, graphene layer in copper foil was easily synthesized using hydrothermal method at temperature 200°C in 3 h duration. Diffraction peaks in XRD at around 29°, 36°, 42° and 74° in the composites correlate to the (110), (111), (200) and (311) crystalline planes of cubic cuprous oxide (Cu 2 O), while peak at 27° showed the carbon graphitic peak. Raman confirms the presence of the graphene layer on Cu 2 O. Photoelectrochemical performance test of Graphene/Cu 2 O demonstrated that the photoelectrocatalyst showing the photocurrent density 9.6 mA cm -2 at -0.8V vs Ag/AgCl. This study demonstrated a potential of semiconductor-based hybrid electrode for an efficient photoelectrocatalytic of CO 2 reduction. ABSTRAK Proses penurunan karbon dioksida (CO 2 ) dengan menggunakan pemangkin bukan logam berharga yang berkesan untuk menghasilkan proses yang lebih berekonomi telah membawa kepada penyelidikan yang komprehensif dalam bidang tersebut. Dalam kajian ini, lapisan grafen pada kerajang tembaga disintesis dengan mudah menggunakan kaedah hidroterma pada suhu 200°C dalam tempoh masa 3 jam. Puncak belauan XRD pada sudut 29°, 36°, 42° dan 74° menunjukkan satah hablur kubik oksida (Cu 2 O) (110), (111), (200) dan (311) dan puncak grafit karbon ditunjukkan pada sudut 27°. Raman mengesahkan kehadiran lapisan grafen pada Cu 2 O. Ujian prestasi fotopemangkinan grafen/ Cu 2 O menunjukkan bahawa fotomangkin tersebut mempunyai ketumpatan fotokimia 9.6 mA cm -2 pada -0.8V vs Ag / AgCl. Kajian ini menyumbang kepada penghasilan elektrod hibrid berasaskan semikonduktor sebagai fotomangkin yang berkesan untuk penurunan CO 2 .