Criteria for the preparation of cross-linked poly(meth)acrylate microparticles by solution free radical polymerization (original) (raw)
2007, European Polymer Journal
Cross-linked polymer microparticles (CPMs) with nanoscopic size were synthesized from the free radical polymerization of acrylate/diacrylate mixtures or of their methacrylate counterparts. The syntheses were carried out in solution, and the study of the influence of the solvent on the CPM characteristics led to the definition of reliable criteria for the obtention of true, soluble, individualized microgels and for avoiding macro-gelation, when starting from any desired monomer combination. Two main parameters could be pointed out: first, the probability of propagation of the growing radicals, q, (or the kinetic chain length k = 1/1 À q) that must be kept below a certain threshold value in order to prevent macrogelation; q may be adjusted by playing on the monomer, initiator and transfer agent concentrations. The second essential criterion is the ability of the copolymer for auto-stabilization in the chosen solvent (that may be adjusted by the use of a suitable stabilizing co-monomer in case the quality of the solvent would not be sufficient), in order to avoid flocculation and interparticular reactions. By controlling these two parameters, the preparation of CPMs becomes possible over a wide range of concentration and composition.
Related papers
Synthesis and characterization of star-like microgels by one-pot free radical polymerization
Polymer, 2005
A one-pot free radical polymerization process was used to prepare methyl acrylate/ethylene glycol dimethacrylate (MA/EGDMA) and methyl methacrylate/ethylene glycol dimethacrylate (MMA/EGDMA) polymers. The role of monomer and crosslinker reactivity ratios in producing different network structures was demonstrated. While both systems produced branched polymers that exhibited low intrinsic viscosities with little variation across a wide range of molecular weights, the star-like microgels formed between a less reactive monomer (MA) with a more reactive crosslinker (EGDMA) gave lower bulk solution viscosities than the more statistical polymers formed between similarly reactive monomers and crosslinkers (MMA and EGDMA). This paper presented a simple and cost-effective synthetic route for the production of polymers with high molecular weight and low viscosity with considerable potential for industrial-scale processing.
Polymer, 2008
It is known that the preferential solvation and conformation of a polymer in a solvent mixture are functions of the polymer's molecular weight and the solvent qualities. This paper demonstrates that these relationships can be exploited to delay the onset of macrogelation for branched poly(methyl methacrylate/ethylene glycol dimethacrylate) (p(MMA/EGDMA)) polymers and star-like poly(methyl acrylate/ethylene glycol dimethacrylate) (p(MA/EGDMA)) polymers synthesised via conventional freeradical polymerisation (CFRP) in a binary solvent mixture (consisting of a good solvent and a precipitant for the polymer). The gelation limits of the MMA/EGDMA and MA/EGDMA polymerisations in a methyl ethyl ketone (MEK)/heptane binary solvent mixture can be extended to regions of higher monomer concentration with increases in polymer yield between 13 and 50 AE 5 w/w% for the p(MMA/EGDMA) system and between 8 and 19 AE 6 w/w% for the p(MA/EGDMA) system across the gelation boundary. Thus, a facile method of increasing the concentration of batch reaction mixtures by the simple addition of small amounts of precipitant into the reaction solutions is presented. Furthermore, the gelation limits of both polymerisation systems in the binary solvent mixtures were further extended with increases in polymer yield between 11 and 17 AE 4%w/w for the p(MMA/ODA/EGDMA) system and between 8 and 20 AE 5%w/w for the p(MA/VS/EGDMA) system by the respective incorporation of octadecyl acrylate (ODA) and vinyl stearate (VS) surfmers into the polymers, demonstrating the application of steric hinderance to shield the propagating polymers from excessive cross-linking reactions.
The synthesis and characterization of star-microgels by atom transfer radical polymerization
A one-pot free radical polymerization process was used to prepare methyl acrylate/ethylene glycol dimethacrylate (MA/EGDMA) and methyl methacrylate/ethylene glycol dimethacrylate (MMA/EGDMA) polymers. The role of monomer and crosslinker reactivity ratios in producing different network structures was demonstrated. While both systems produced branched polymers that exhibited low intrinsic viscosities with little variation across a wide range of molecular weights, the star-like microgels formed between a less reactive monomer (MA) with a more reactive crosslinker (EGDMA) gave lower bulk solution viscosities than the more statistical polymers formed between similarly reactive monomers and crosslinkers (MMA and EGDMA). This paper presented a simple and cost-effective synthetic route for the production of polymers with high molecular weight and low viscosity with considerable potential for industrial-scale processing.
Journal of Polymer Science Part B Polymer Physics
Physically crosslinked hydrogels based on N-vinylcaprolactam/acrylic acid and N-vinylcaprolactam/methacrylic acid were prepared via free radical polymerization. These temperature responsive hydrogels were characterized in terms of glass transition, phase separation temperature, potentiometric titration and swelling properties. Results showed that phase transition temperature was dependent on the pH value of the solution; increasing pH led to higher lower critical solution temperature (LCST) values which was related to the dissociative behaviors of the carboxylic group of MAc in the buffered solutions. Additionally, with the incorporation of N,N-dimethylacrylamide into the system, cloud point measurements and MDSC showed an increased in the LCST. This increase was based on hydrophilicity, the hydrophilic-hydrophobic balance was disturbed, and consequently, the LCST behavior was shifted. The pKa of the copolymers ranged between 5.6 and 6.5, while for the terpolymers pKa ranged between...
Loading Preview
Sorry, preview is currently unavailable. You can download the paper by clicking the button above.