Improving the mechanical properties of natural fibre fabric reinforced epoxy composites by alkali treatment (original) (raw)

In this article, three bio-composites, i.e. flax, linen and bamboo fabric reinforced epoxy resin, were manufactured using a vacuum bagging technique. The influence of alkali treatment (with 5 wt% NaOH solution for 30 min) on tensile properties of flax, linen and bamboo single-strand yarns, surface morphology and mechanical properties (with respect to tensile and flexural properties) of the composites were investigated. It was found that the failure mechanism of single-strand fibres under tension consists of fibre breakage and slippage simultaneously. The alkali treatment had a negative effect on the tensile strength and modulus of the flax, linen and bamboo single-strand yarns. However, after the treatment, the tensile and flexural properties of all the composites increased, e.g. the tensile and flexural strength of the treated flax/epoxy composite increased 21.9% and 16.1%, compared to the untreated one. After the treatment in all the composites, the tensile fractured surfaces exhibited an improvement of fibre/epoxy interfacial adhesion.

Sign up for access to the world's latest research.

checkGet notified about relevant papers

checkSave papers to use in your research

checkJoin the discussion with peers

checkTrack your impact