Effect of air-abrasion regimens and fine diamond bur grinding on flexural strength, Weibull modulus and phase transformation of zirconium dioxide (original) (raw)

Journal of applied biomaterials & functional materials, 2015

Abstract

This study evaluated the effect of air abrasion and polishing regimens on the flexural strength of yttrium stabilized polycrystalline tetragonal zirconia (Y-TZP). From Y-TZP blocks (InCeram 2000 YZ Cubes; Vita Zahnfabrik, Bad Säckingen, Germany) 120 bars (25 mm × 4 mm × 1.2 mm) were obtained according to ISO 6872:2008 and randomly divided into 4 groups: Group C: (control) without surface treatment (n = 30); Group APA: Air abrasion with aluminum oxide (44 µm) (n = 30); Group SC: Silica-coating (CoJet, 30 µm) (n = 30); Group FD: Fine diamond bur (n = 30). Subsequently, all specimens were subjected to 4-point bending test (in distilled water at 37°C) in a universal testing machine (EMIC DL 1000; São José dos Pinhais, Paraná, Brazil); cross-head speed: 0.5 mm/min). The characteristic strength (σ0) of each specimen was obtained from the flexural strength test and evaluated using Weibull analysis. X-ray diffraction analysis was utilized to quantity the monoclinic phase. The surface topogr...

Marco Antonio Bottino hasn't uploaded this paper.

Let Marco Antonio know you want this paper to be uploaded.

Ask for this paper to be uploaded.