Polymeric hydrogels obtained using a redox initiator: Application in Cu(II) ions removal from aqueous solutions (original) (raw)

Poly(acrylic acid-co-acrylamide) hydrogels were prepared via free-radical solution polymerization, crosslinked with ethylene-glycol-dimethacrylate, potassium persulfate/ammonium bisulfite as the initiator, and applied in the removal of Cu(II) ions from aqueous solutions. Molar ratios of acrylamide/acrylic acid moieties and the amount of crosslinking agent were varied to determine the swelling capacities of hydrogels and maximum metal uptake. Polymerization kinetics was investigated by 1 H-NMR. Hydrogel physicochemical properties were characterized by nitrogen sorption measurements, elemental analysis, FTIR, and X-ray photoelectron spectroscopy (XPS). Swelling results indicated that hydrogels were swollen up to 27,500%. Hydrogels showed equilibrium Cu(II) adsorption capacities of 211.7 mg g 21 and fast kinetics ($20 min). Langmuir isotherm fitted adsorption equilibrium data. FTIR and XPS results helped in elucidating the presence of monodentate copper complex on the surface of hydrogels. A simple synthesis route of hydrogels using the redox initiator suggests the potential application in the removal of toxic metals from aqueous streams. V C 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014, 131, 39933.

Sign up for access to the world's latest research.

checkGet notified about relevant papers

checkSave papers to use in your research

checkJoin the discussion with peers

checkTrack your impact