Temperature Dependence of Pd Thin-Film Cryoresistors (original) (raw)
Related papers
NiCr based thin film cryo resistors
2008 Conference on Precision Electromagnetic Measurements Digest, 2008
ABSTRACT Thin film resistors, based on the NiCr alloys, have been fabricated and studied at temperatures down to 50 mK. Resistivity of the films varied within (7-11) Ohm*square depending on additions of Cu, Al and Ge. The resistors demonstrate Kondo minimum at 20 K - 30 K. Power dependence measurements at sub Kelvin temperatures showed an electron overheating at the power level above 10 pW for the Ni75Cr20Cu2.5Al2.5 (Evanohm) 500 kOhm film resistor.
Electrical properties of thin-film resistors in a wide temperature range
Circuit World, 2015
Purpose -The purpose of this paper is to characterise electrical properties of Ni-P thin-film resistors made on FR-4 laminate in a wide range of temperature (fro m -180 to 20ºC). Design/methodolog y/approach -The study was performed using resistors made of nickel-phosphorus (Ni-P) foil with two different thicknesses (0.1 μm or 0.05 μm) and the same different sheet resistances (100 oh m/sq or 250 ohm/sq). The resistance rectangular resistors had length and width fro m the range between 0.59 and 5.91 mm. The resistance vs temperature characteristics and their distribution as well as resistors durability to low-temperature thermal shocks were investigated.
Low-temperature specific heat and resistivity of single-crystallinePd2Si
Physical review, 1990
We present specific-heat (0.2 K~T 7.5 K) and resistivity (4.2 K~T 300 K) measurements on well-characterized, high-quality, single crystals of Pd&Si. The anisotropy of the electronic band structure reflects on the electronic conductivity and on the strong variation of the Debye temperature at low temperature.
Implementation of RuO 2 -glass based thick film resistors in cryogenic thermometry
Measurement Science and Technology, 2006
In the work we analyse the results of investigations of RuO 2 -glass based compounds, with regard to their implementation in low temperature thermometry. Based on measurements made down to 0.3 K we have shown that the sensitivity, S = dR/dT, of our sensors is comparable to the sensitivity of commercial sensors. The influence of the magnetic field on the investigated sensors in the range up to 10 T was checked. The magnetoresistance MR = (R 0 − R B )/R 0 of our v = 10% sample is approximately five times smaller than for the Rox RX-202A Lake Shore sensor (B = 7 T, T = 0.47 K). We present results of investigations of the stability during thermal cycling: resistance changes during cycling lead to differences in temperature indication after a period of time.
Low-temperature properties of thin films
Physica D: Nonlinear Phenomena, 1992
It is shown that phonons in this films, "cut off" from a simple lattice, possess a gap whose magnitude depends upon the thickness of the film. Due to the presence of the gap, the specific heat of the film for T~-0 changes approximately as T l exp(-const/T). This behaviour of the specific heat can be used for experimental verification of the existence of the phonon gap.
Baghdad Science Journal, 2008
The electrical properties of polycrystalline cadmium telluride thin films of different thickness (200,300,400)nm deposited by thermal evaporation onto glass substrates at room temperature and treated at different annealing temperature (373, 423, 473) K are reported. Conductivity measurements have been showed that the conductivity increases from 5.69X10-5 to 0.0011, 0.0001 (?.cm)-1 when the film thickness and annealing temperature increase respectively. This increasing in ?d.c due to increasing the carrier concentration which result from the excess free Te in these films.
Defect structure of high resistive CdTe:In prepared by vertical gradient freeze method
IEEE Transactions on Nuclear Science, 2004
High resistive and photosensitive CdTe doped with In aimed for fabrication of X-and gamma-ray detectors was produced by Vertical Gradient Freeze method. A complex investigation of defects and compensation by a number of optical and photoelectrical mapping methods was performed. A model of energy levels dominating the recombination processes in the material was elaborated, where the role of In, and related complexes as well as native defects (Cd vacancy and its compexes) is discussed.