Electrochemistry of poly(pyrrole chloride) films: a study of polymerization efficiency, ion transport during redox and doping level assay by electrochemical quartz crystal microgravimetry, pH and ion-selective electrode measurements (original) (raw)
1992, The Journal of Physical Chemistry
This study concerns the growth, redox behavior, and analysis of poly(pyrro1e chloride) films ranging in thickness from -0.5 to -1.5 pm. Changes in the electrolyte pH from radical-coupling reactions during the oxidation of pyrrole lead to estimates of the polymerization efficiency in 0.1 M KCI which vary from 82% to 92% depending on the charge consumed. These values are compared with the Coulombic efficiency computed earlier in this laboratory using electrochemical quartz crystal microgravimetry (EQCM). The EQCM technique was combined with coulometry and in situ pH and K-ion-selective elactrode measurements for reexamining the extent of permselectivity of polypyrrole with respect to the chloride ion in aqueous elcctrolyta. Chloride ions contribute -75-8596 to the transport of the total charge during the redox of polypyrrole in 0.1 M KC1. The residual charge is partitioned between H+ and K+ depending on the initial pH of the electrolyte, which was varied from -1 to -7 in this study. Potassium ion transport was further verified by X-ray photoelectron spectroscopy. The extent of permselectivity is also dependent on the nature of the electrolyte cation, the bulky tetraethylammonium ion showing the most ideal behavior in this regard. Redox cycling of polypyrrole in 0.1 M CsCl and 0.1 M HCl was accompanied by a m b l e cation movement especially at potentials below ~-3 0 0 mV (vs Ag/AgCl). Finally, the ion transport during the redox of poly(pyrro1e chloride) was found to be intrinsically asymmetric in two related respects: first, the redox charge monitored via chronocoulometry in the two switch directions, i.e., oxidized/reduced, was not identical. Second, the measured redox charge was only 27-3596 of that theoretically expected from the polymer doping level for the 0.1 M KCl electrolyte. These data underline the inadequacy of the chronocoulometry/voltammetry procedure for assay of the doping level in conducting polymers such as polypyrrole, especially for rather thick (>a few hundred nanometers) polymer films.
Sign up for access to the world's latest research.
checkGet notified about relevant papers
checkSave papers to use in your research
checkJoin the discussion with peers
checkTrack your impact
Loading Preview
Sorry, preview is currently unavailable. You can download the paper by clicking the button above.