Laboratory study to determine the critical moisture level for mould growth on building materials (original) (raw)
2012, International Biodeterioration & Biodegradation
The susceptibility of building materials to mould growth varies. Some are tolerant to high relative humidity in the ambient air without mould growth occurring, while others are less tolerant, and mould can grow in relative humidity as low as 75%. Within a building, constructions are exposed to different temperatures and relative humidities. To minimise the risk of microbial growth, building materials should be chosen that are tolerant to the expected conditions. In this study, the critical moisture levels for ten building materials with a range of expected critical moisture levels (wood-based materials, gypsum boards and inorganic boards) were evaluated. Samples of the building materials were inoculated with spores from six species of mould fungi (Eurotium herbariorum, Aspergillus versicolor, Penicillium chrysogenum, Aureobasidium pullulans, Cladosporium sphaerospermum, Stachybotrys chartarum) and incubated in test cabinets at specified temperature (10 C and 22 C) and relative humidity conditions (75e95%); growth of mould was analysed weekly for at least 12 weeks. One of the conclusions is that two similar building materials or products may have considerably different resistance to mould growth, and so the results from one type of building material cannot be applied to the other. Also, in order to compare results from different tests, it is important to use the same test method. It is also important to state the temperature at which the critical moisture level applies and how long the material is exposed to the temperature and relative humidity conditions during the test.
Related papers
Validation of critical moisture conditions for mould growth on building materials
Building and Environment, 2013
Materials that are stored or used in damp conditions may be subject to mould growth. However, all materials are not equally susceptible; for each specific material, there is a critical moisture level for mould growth. If this is exceeded, there is a risk that mould fungi will develop on the material. This level can be determined in accelerated laboratory tests, at constant temperatures and relative humidity (RH) favourable to mould growth. Within a building however, these parameters are expected to vary from one part of the construction to another, and are seldom constant; there is fluctuation in temperature and RH due to seasonal or shorter-term variations. In this study, test pieces of the same materials tested in a laboratory environment were placed in three outdoor ventilated crawl spaces and three outdoor ventilated attics, where the temperature and RH varied, and mould growth on the test pieces was studied over 2.5 years. Material-specific mould growth curves were produced based on critical moisture levels, as determined in laboratory experiments under constant temperature and RH. When the actual conditions of RH and temperature exceeded these curves, there was mould growth on the test pieces if the time was sufficiently long. The conclusion from the study is that although conditions in laboratory studies are simplified and accelerated, the results serve well to indicate mould growth within a building construction.
Building and Environment, 2009
We report the results of a study to evaluate the growth rate of three species of mould on plasters, finishes and paints typically used in structures with heavy weight building envelopes. The aim was to determine the influence of the chemical composition (in terms of organic fraction of the materials) on the growth rate of moulds. The study was carried out in the following steps: -characterization of materials;inoculation of mould spores (3 species) on 7 types of material (2 plasters, 3 finishes, 2 paints); -growth in a climatic chamber (23 C and 90% RH); -analysis of the mould growth rate using various experimental techniques (fluorescence microscopy analysis, thermogravimetric analysis, etc.). Results show a clear correlation between the organic substances contained in paints, plasters and finishes and the growth rate of the mould. This study is part of a more general research program which addresses the effects on indoor environment air quality based on the European directive 2002/91/EC. This directive specifically indicates that energy consumption in buildings should be limited and sets threshold values for the thermal resistance of the building walls and windows. As a consequence window manufacturers are improving the thermal property of windows by reducing the air permeability, which may increase the indoor and surface relative humidity percentage (RH%) and lead to the development of mould in the indoor environments.
Comparison of test methods for mould growth in buildings
2016
The purpose of this work is to compare a range of test methods and kits for assessing whether a building structure is infested by mould fungi. A further purpose of this work is to evaluate whether air-based methods for sampling fungal emissions provide information qualifying decisions concerning renovation needs. This is of importance when hidden surface testing would require destructive measures and subsequent renovation. After identifying available methods on the Danish market for assessing mould growth in dwellings, a case study was conducted to test the usefulness of the methods in four dwellings of different typology and with or without known mould infestations. In each dwelling seven methods were used in parallel. The criteria for choosing the different methods were that they had to be nondestructive, relatively quick and easy, and frequently used by building professionals. The chosen methods measure different aspects relating to mould growth and vary in selectivity and precis...
PERFORMANCE CRITERIA FOR THE AVOIDANCE OF MOULD GROWTH IN DWELLINGS
2000
The avoidance of mould growth in dwellings is of worldwide concern. In England and Wales, the relevant Building Regulations guidance document recommends ventilation provisions to control both moisture and other pollutants in buildings. The performance criterion for moisture states that there should be no visible mould on external walls in a properly heated dwelling with typical moisture production. The relevant guidance document (ADF) further states that this moisture criterion will be met if the Relative Humidity (RH) in a room does not exceed 70% for more than 2 hours in any 12 hour period, and does not exceed 90% for more than 1 hour in any 12 hour period during the heating season. This paper presents initial exploratory results on the investigation of these performance criteria, which is a part of a much larger study relating to RH in dwellings. A number of experiments in a tightly controlled environmental chamber programmed to maintain suitable profiles of RH levels and temperatures which relate to typical surface conditions in dwellings in England and Wales have been carried out.
2008
A review on mould growth in buildings in a subtropical climate and the characteristics of moulds in a subtropical Central Queensland University (CQU), Rockhampton campus, Australia, buildings are presented and analysed. The mould (fungal spore) concentrations indoors and outdoors are compared and correlations between mould concentrations and environmental parameters such as temperature and humidity are developed. Specific genera of moulds and total spores were identified and recovered colonies were counted from the airborne samples. The SPSS (Statistical Product and Service Solutions) software was used for nonparametric data analysis. Total airborne mould concentrations were found highest in the dry season and lowest in the wet season and were positively correlated with relative humidity and temperature. Further studies are recommended for controlling mould growth in buildings in a subtropical climate.
Conditions Influencing Mould Growth for Effective Prevention of Wood Deterioration Indoors
Applied Sciences
Effective prevention of mould growth indoors is still an important topic considering that mould growth is frequently observed in buildings, it causes serious health hazards and can irreversibly damage infected objects. Several studies have been conducted and mould growth models developed. Despite that, some potentially important aspects such as water damage and spore contamination have received only little attention. The objective of the present study was to investigate the effect of the initial moisture content of wood and spore contamination on mould development indoors. The mould tests were performed in constant temperature (10, 20 and 30 °C) and relative humidity (91% and 97%) conditions. The results show that wetting of wood specimens prior to the test significantly accelerates mould growth at a temperature of 10 °C. For the other temperatures, the effect was insignificant. Similar results were obtained for the test involving dry (conditioned at RH 50%) and conditioned specimen...
The Role of Transient Wetting on Mould Growth on Wooden Claddings
Energy Procedia, 2015
Mold growth on the surface of wooden façades is usually dealt with by using surface treatment such as paint with fungicides. However, new developments in architecture are moving towards less use of coating, and more use of untreated wooden claddings. Mould growth is well understood and described, and several models for predicting mould growth on building materials exist. It is commonly known that mould growth is directly controlled by the climate which the wood is exposed to. Several authors identify humidity, temperature and time as the main drivers of mould growth. However, most of the current growth models developed are based on laboratory measurements at stable climatic conditions. Consequently, these models are less suitable for prediction of mould growth on exterior surfaces exposed to rapidly changing weather conditions. This paper analyses the effect of variations of meteorological data on the mould growth on wooden claddings. An experimental setup of wood samples was exposed to outdoor conditions and hourly weather conditions as well as the mould growth at different intervals were measured. The measurements were supplied with 1-D Heat And Moisture (HAM) simulations to provide a more accurate estimate of the conditions on the surface of the samples. The purpose of the analysis was to evaluate if an existing mould growth model might be applicable also for predicting outdoor mould growth. Several profiles of temperature and moisture were continuously monitored on different locations of an eight-story building made from Cross Laminated Timber (CLT). The results from the analysis of the samples of wood cladding were used to model the mould growth on different locations of the building. Also the drying effect of wind around the building was studied. The study shows that there is large variation of potential mould growth on the façade of the building.
Loading Preview
Sorry, preview is currently unavailable. You can download the paper by clicking the button above.