On the stability of surface martensite in β-phase CuZn alloys (original) (raw)

Modification in Cu-Zn Alloy Properties by 2 MeV Ni + Ions Irradiation

2018

We investigate the effects of 2 MeV Ni+ ion beam irradiation with various fluence ranging from 15 × 1011 to 60 × 1014 ions/cm2 on the surface, structural and mechanical properties of Cu-Zn alloy. The modification in target properties after irradiation is confirmed by using various characterization techniques viz. SEM, XRD, UTM and Vickers micro-hardness tester. The SEM results illustrate the formation of nano sized craters with different diameters. Their average diameter decreases from 190 nm to 90 nm by increasing ion fluence. The XRD analysis of irradiated targets reveals that Ni+ ion irradiation enhances the growth of (111) phase and its peak position varies due to ion induced tensile stresses in target matrix. Tensile and Vickers micro-hardness tests verify the mechanical properties of Cu-Zn alloy reduce monotonically upon irradiation. Various mechanisms such as generation, recombination, augmentation and annihilation of ion induced defects are responsible for this reduction. Un...

Contribution to the knowledge of the Cu–Sn–Zn system for compositions close to brass alloys

The effect of tin content in the equilibrium phases of the Cu–Zn-based alloys, within the range of chemical compositions with interest to brass producers is described. For this purpose, ternary alloys with copper contents between 55.4 and 67.5 wt.% and tin contents up to 5.30 wt.% have been studied. The chemical composition of each alloy has been determined by X-ray fluorescence spectrometry (XRF). Isothermal homogenization, followed by rapid cooling, has been employed to determine the equilibrium phases at different temperatures. The homogenized alloys have been observed by scanning electron microscopy and the respective chemical analysis of the phases determined by electron probe microanalysis (EPMA). The statistical analysis of the obtained results enable to correlate the chemical composition of equilibrium phases with temperature. The chemical composition of the three-phase field, for the studied temperatures, has also been determined.