In Situ Electron Microscopy Four-Point Electromechanical Characterization of Freestanding Metallic and Semiconducting Nanowires (original) (raw)
Related papers
Failure mechanisms and electromechanical coupling in semiconducting nanowires
EPJ Web of Conferences, 2010
One dimensional nanostructures, like nanowires and nanotubes, are increasingly being researched for the development of next generation devices like logic gates, transistors, and solar cells. In particular, semiconducting nanowires with a nonsymmetric wurtzitic crystal structure, such as zinc oxide (ZnO) and gallium nitride (GaN), have drawn immense research interests due to their electromechanical coupling. The designing of the future nanowire-based devices requires component-level characterization of individual nanowires. In this paper, we present a unique experimental setup to characterize the mechanical and electromechanical behaviour of individual nanowires. Using this setup and complementary atomistic simulations, mechanical properties of ZnO nanowires and electromechanical properties of GaN nanowires were investigated. In ZnO nanowires, elastic modulus was found to depend on nanowire diameter decreasing from 190 GPa to 140 GPa as the wire diameter increased from 5 nm to 80 nm. Inconsistent failure mechanisms were observed in ZnO nanowires. Experiments revealed a brittle fracture, whereas simulations using a pairwise potential predicted a phase transformation prior to failure. This inconsistency is addressed in detail from an experimental as well as computational perspective. Lastly, in addition to mechanical properties, preliminary results on the electromechanical properties of gallium nitride nanowires are also reported. Initial investigations reveal that the piezoresistive and piezoelectric behaviour of nanowires is different from bulk gallium nitride. 1 In situ testing of nanostructures Semiconducting nanowires (NWs) are potential building blocks for future electronic devices like logic circuits, transistors, and solar cells. NWs made of materials like zinc oxide (ZnO) and gallium nitride (GaN) are interesting for the research community due to their piezoelectric behaviour, offered by the non-symmetric wurtzite crystal structure. For example, ZnO NWs has been conceptually shown to generate electrical output when mechanically deformed [1-3]. To optimize the potential performance of piezoelectric NW-based devices, characterization of individual NWs at the component level is crucial. In this paper, a microelectromechanical system (MEMS)-based
NUMERICAL CHARACTERIZATION OF THE MECHANICAL PROPERTIES OF METAL NANOWIRES
Nanowires (NWs) have attracted appealing and broad application owing to their remarkable mechanical, optical, electrical, thermal and other properties. To unlock the revolutionary characteristics of NWs, a considerable body of experimental and theoretical work has been conducted. However, due to the extremely small dimensions of NWs, the application and manipulation of the in situ experiments involve inherent complexities and huge challenges. For the same reason, the presence of defects appears as one of the most dominant factors in determining their properties. Hence, based on the experiments' deficiency and the necessity of investigating different defects' influence, the numerical simulation or modelling becomes increasingly important in the area of characterizing the properties of NWs. viii Numerical Characterization of the Mechanical Properties of Metal Nanowires
1995
Measurements of room-temperature electronic transport in pulled metallic nanowires are presented, demonstrating that the conductance characteristics depend on the length, lateral dimensions, state and degree of disorder, and elongation mechanism of the wire. Conductance during elongation of short wires, lϳ50 Å, exhibits periodic quantization steps with characteristic dips, correlating with the order-disorder states of layers of atoms in the wire, predicted via molecular dynamics simulations. The resistance of longer wires, lտ100 Å, exhibits localization characteristics with ln R(l)ϳl 2 . Effects of disorder and variations in wire geometry, exhibited via their influence on the transmittivity of the conductance channels and/or the quantization conditions, are demonstrated.
Strengthening mechanisms and dislocation dynamics in twinned metal nanowires
JOM, 2008
We demonstrate that the microstructure strengthening effects are still valid in nanoscale materials, which can be used as potential strategies to design materials with these structures. …describe this work to a materials science and engineering professional with no experience in your technical specialty? This work highlights that the strengthening mechanism of the twinned nanowires is due to the stress redistribution along the wire axis, requiring larger external stress to make them yield as compared to twin-free wire. The simulation results show that twin boundaries mainly serve as a barrier for dislocation movements, which contribute to some hardening effects. …describe this work to a layperson? Twinned metal nanowire has different mechanical behavior than bulk metals. This study demonstrates that the mechanical properties of metal nanowires can be controlled by tailoring interior growth twin structures. Microtwins are frequently observed in face-centered-cubic (fcc) metal nanowires with low stacking fault energy. The authors have previously reported that the tensile yield strength of copper nano wires can be increased by the presence of twin boundaries. In this work simulations are carried out under both uniaxial tension and compression loading, to demonstrate that the strengthening effects are inherent to these nanowires, independent of the loading condition (tensile/compressive). It appears that the strengthening mechanism of the twinned nanowires can be attributed to stress redistribution due to the change of crystallographic orientations across twin boundaries, which requires larger external stress to make them yield as compared to the twin-free wire. A.J. Cao (graduate student) and Y.G. Wei (professor) are with the
Mechanics of Crystalline Nanowires
MRS Bulletin, 2009
Nanowires are among the most exciting one-dimensional nanomaterials because of their unique properties, which result primarily from their chemical composition and large surface area to volume ratio. These properties make them ideal building blocks for the development of next generation electronics, opto-electronics, and sensor systems. In this article, we focus on the unique mechanical properties of nanowires, which emerge from surface atoms having different electron densities and fewer bonding neighbors than atoms lying within the nanowire bulk. In this respect, atomistic simulations have revealed a plethora of novel surface-driven mechanical behavior and properties, including both increases and decreases in elastic stiffness, phase transformations, shape memory, and pseudoelastic effects. This article reviews such atomistic simulations, as well as experimental data of these phenomena, while assessing future challenges and directions.
Universal behaviour in the final stage of the breaking process for metal nanowires
Nanotechnology, 2005
The gentle control of the nanometric distance between two materials has paved the way for the recent experimental studies on the formation and breaking of metal nanocontacts. In this work, the evolution of Al nanowires along the stretching process up to the final breaking is simulated with density functional calculations. This massive computational work involves the breaking of thick wires (with and orientations and 145 and 136 atoms respectively), and the influence of O, C and H impurities on their mechanical and electrical properties. These simulations show that, close to the breaking point, Al nanowires always develop a dimer geometry irrespective of the initial configuration, crystallographic orientation and the presence of point defects, explaining the universal behaviour of the force and the conductance found in the last stages of the stretching process in all the experiments.
Mechanical properties of bimetallic crystalline and nanostructured nanowires
Faraday Discussions, 2008
Nanowires are basic components of interconnects at the nanoscale level in electronic as well as in electromechanical devices. Presently, there is a fast growing interest in their synthesis as well as in their mechanical testing. Focused ion beams now allow machining pillars with diameters as small as a few tens of nanometres and nanoindenter systems allow measuring strains at the atomic scale and compressive stresses up to the 10 GPa range. Such pillars typically contain less than millions of atoms, which makes their modelling and the modelling of their mechanical properties at the atomic scale realistic. A few Molecular Dynamics studies are presently available, discussing deformation mechanisms in thin narrow crystalline nanowires, but the literature about nanoalloy wires and nanostructured wires, as they can be synthesized from clusters, is almost non-existent. In the latter, the dislocation activity may be inhibited, leading to specific mechanical properties. By means of large scale computations, we use Ni 3 Al to discuss the mechanical properties of crystalline and nanostructured nanowires. We also compare wires to their bulk counterparts. Both isothermal and isoenergetic-whereby mechanical work converts into heat in the systemdeformation mechanisms are considered. The comparison between pair correlation functions, stress distributions, configuration analysis and strain stress relations capture most of the stress-induced evolution mechanisms of nanowires with different diameters and structures, including elastic properties, dislocation activity, grain rotation and boundary motion, local melting, superplasticity and fracture. A structural transition which may be martensitic is predicted for the first time at the nanoscale level, suggesting possible shape memory properties of nanoalloy nanowires.