Optimization of nucleation and buffer layer growth for improved GaN quality (original) (raw)
2007, Journal of Crystal Growth
By accurately optimizing the growth conditions for an oxygen doped AlN nucleation layer and for the subsequent epitaxial process the crystal quality of our GaN layers could be improved drastically. In X-ray diffraction analyses we observed FWHM values of 39 and 114 arcsec for the symmetric (0 0 4)-and asymmetric (1 1 4)-reflection, respectively. Consequently, the nominally undoped samples showed semi-insulating behavior in Hall measurements. By in situ deposition of a SiN interlayer, the dislocation density could be reduced by more than a factor of 2, reaching a value of 4 Â 10 8 cm À2 as confirmed by transmission electron microscopy and etch pit density counting. Samples with this low dislocation density showed an extremely narrow X-ray FWHM of 71 arcsec for the asymmetric (1 1 4)reflection along with a narrow linewidth of 870 meV in photoluminescence (PL) for the donor bound exciton (D 0 X) at a temperature of 10 K. Atomic force microscopy yielded a very low rms roughness value of about 0.14 nm across a 4 mm 2 scan area. Finally the excellent crystal quality could be confirmed by growing AlGaN/AlN/GaN high electron mobility transistor structures with reverse breakdown voltages X1000 V and a very low sheet resistance of 330 O=&.
Sign up for access to the world's latest research.
checkGet notified about relevant papers
checkSave papers to use in your research
checkJoin the discussion with peers
checkTrack your impact
Related papers
MRS Proceedings, 2005
An alternative scheme to the growth of crack free, dislocation reduced III-Nitride layers on Silicon substrate has been previously introduced that relies on formation of an ion implanted defective layer in the substrate with implantation taking place in the presence of AlN buffer layer. Here, the effects of N+ ion implantation of AlN/Si (111) substrate on the structural and optical properties of the overgrown GaN epilayers have been investigated. Temperature dependent photoluminescence has been used to investigate the impact of the implantation conditions (energy and dose) on optical and structural quality of the GaN overgrown layers. A correlation between PL and high resolution x-ray diffraction (XRD) of the overgrown GaN layers show that the lowest FWHM of bandedge, the highest bandedge to deep defect blue luminescence band ratio, and the lowest symmetric rocking curve FWHM are achieved for the optimized implantation conditions. This correlates well with the results of etch pit de...
2010
GaN and AlGaN epitaxial layers are grown by a metalorganic chemical vapour deposition (MOCVD) system. The crystalline quality of these epitaxially grown layers is studied by different characterization techniques. PL measurements indicate band edge emission peak at 363.8 nm and 312 nm for GaN and AlGaN layers respectively. High resolution XRD (HRXRD) peaks show FWHM of 272 and 296 arcsec for the (0 0 0 2) plane of GaN and GaN in GaN/AlGaN respectively. For GaN buffer layer, the Hall mobility is 346 cm 2 /V-s and carrier concentration is 4.5 × 10 16 /cm 3. AFM studies on GaN buffer layer show a dislocation density of 2 × 10 8 /cm 2 by wet etching in hot phosphoric acid. The refractive indices of GaN buffer layer on sapphire at 633 nm are 2.3544 and 2.1515 for TE and TM modes respectively.
Studies of Defect Structure in Epitaxial AlN/GaN Films Grown on (111) 3C-SiC
Nanomaterials
Several aspects such as the growth relation between the layers of the GaN/AlN/SiC heterostructure, the consistency of the interfaces, and elemental diffusion are achieved by High Resolution Transmission Electron Microscopy (HR-TEM). In addition, the dislocation densities together with the defect correlation lengths are investigated via High-Resolution X-ray Diffraction (HR-XRD) and the characteristic positron diffusion length is achieved by Doppler Broadening Spectroscopy (DBS). Moreover, a comparative analysis with our previous work (i.e., GaN/AlN/Si and GaN/AlN/Al2O3) has been carried out. Within the epitaxial GaN layer defined by the relationship F4¯3m (111) 3C-SiC || P63mc (0002) AlN || P63mc (0002) GaN, the total dislocation density has been assessed as being 1.47 × 1010 cm−2. Compared with previously investigated heterostructures (on Si and Al2O3 substrates), the obtained dislocation correlation lengths (Le = 171 nm and Ls =288 nm) and the mean distance between two dislocation...
Low-dislocation-density GaN and AlxGa1−xN (x⩽0.13) grown on grooved substrates
Journal of Crystal Growth, 2002
We proposed the heteroepitaxial lateral overgrowth technique using grooved sapphire (0 0 0 1) and ð1 1 % 2 0Þ SiC(0 0 0 1) Si and Si(1 1 1) substrates to prepare Al x Ga 1Àx N single crystalline films with low dislocation density. Straight grooves of these substrates were aligned parallel to the /1 % 10 0S or /1 1 % 2 0S direction of Al x Ga 1Àx N. In this technique, neither a selective growth mask nor patterned GaN single crystal film was used. Dislocation densities lower than about 10 6 cm À2 were ascertained via plan-view TEM. This technique is promising for growing low-dislocationdensity nitride-based semiconductors.
Advances in GaN Crystals and Their Applications
Crystals
This special issue looks at the potential applications of GaN-based crystals in both fields of nano-electronics and optoelectronics. The contents will focus on the fabrication and characterization of GaN-based thin films and nanostructures. It consists of six papers, indicating the current developments in GaN-related technology for high-efficiency sustainable electronic and optoelectronic devices, which include the role of the AlN layer in high-quality AlGaN/GaN heterostructures for advanced high-mobility electronic applications and simulation of GaN-based nanorod high-efficiency light-emitting diodes for optoelectronic applications. From the results, one can learn the information and experience available in the advanced fabrication of nanostructured GaN-based crystals for nano-electronic and optoelectronic devices.
High temperature AlN intermediate layer in GaN grown by molecular beam epitaxy
Journal of Crystal Growth, 2000
High-temperature AlN intermediate layers with di!erent thicknesses were deposited during the growth of wurtzite GaN on (0 0 0 1) sapphire substrates by plasma-assisted molecular beam epitaxy. When using a 3.5 nm AlN intermediate layer temperature-dependent Van-der-Pauw Hall measurements revealed a mobility enhancement by a factor of 2.5 at room temperature and by a factor of 32 at 30 K. Transmission electron microscopy con"rmed that the better material quality was due to a reduction of dislocation density by about one order of magnitude. Photoluminescence measurements indicate a decrease of full-width at half-maximum of the main emission peak for GaN samples with AlN intermediate layer.