Synthesis and photoluminescence study of rare earth activated phosphor Na2La2B2O7 (original) (raw)

2012, Journal of Luminescence

The photoluminescence properties in UV and N-UV excitable range for the phosphors of Na 2 La 2 B 2 O 7 : RE (RE ¼ Eu, Tb, Ce, Sm, Gd) are investigated. The solution combustion synthesis technique was employed for the synthesis of the phosphors Na 2 La 2 B 2 O 7 : RE. The photoluminescence measurements of the phosphors were carried out on a HITACHI F7000 Fluorescence Spectrophotometer. The PL and PL excitation (PLE) spectra indicate that the main emission wavelength of Na 2 La 2 B 2 O 7 : Eu are 591 and 615 nm, Na 2 La 2 B 2 O 7 : Ce shows dominating emission peak at 387 nm and Na 2 La 2 B 2 O 7 : Tb displays green emission at 493, 544, 593 and 620 nm at 254 nm excitation, while Na 2 La 2 B 2 O 7 : Sm shows the main emission peak wavelengths 566 and 604 nm at 405 nm excitation and Na 2 La 2 B 2 O 7 : Gd shows dominating emission peak at 312 nm at 274 nm excitation. These phosphors may provide a new kind of luminescent materials under ultraviolet and near ultraviolet excitation for various applications.

Sign up for access to the world's latest research.

checkGet notified about relevant papers

checkSave papers to use in your research

checkJoin the discussion with peers

checkTrack your impact