Enhanced superconducting properties of rare-earth oxides and graphene oxide added MgB2 (original) (raw)

Physica C: Superconductivity and its Applications

Abstract

ABSTRACT In this paper, the effects of addition of (i) graphene oxide (GO), (ii) a series of rare-earth (RE, RE = La, Sm, Eu, Gd, Tb and Ho) oxides (REO) and (iii) a mixture of GO and rare-earth oxides (GO + REO) on the superconducting properties of MgB2, have been studied with the help of electrical transport and magnetic measurements. All the samples have been prepared following the standard solid-state reaction route. We have used an optimum value of 1 wt% REO and 3 wt% GO for addition on the basis of previous studies. X-ray diffraction studies confirm the formation of hexagonal crystal structure (space group P6/mmm) of MgB2 with small amounts of REBx (x = 4 and 6) and MgO impurity phases in all the synthesized samples. We observe that the critical current density, Jc and upper critical field Hc2(0) improve significantly in the REO-added and GO-added samples with no significant change in critical temperature, Tc. A substantial enhancement in Jc(H) and Hc2(0) is observed with the GO + REO addition in MgB2. The different flux pinning mechanisms in all the samples are studied and it is found that the point pinning is the dominant mechanism in the GO-added samples and grain boundary pinning is the dominant one in the REO added samples. We have seen the combined effect of both types of flux pinning mechanisms in GO + REO added MgB2.

Sudesh Bhalothia hasn't uploaded this paper.

Let Sudesh know you want this paper to be uploaded.

Ask for this paper to be uploaded.