Slip-System-Related Dislocation Study from In-Situ Neutron Measurements (original) (raw)

2008, Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science

A combined experimental/computational approach is employed to study slip-system-related dislocation-substructure formation during uniaxial tension of a single-phase, face-centered-cubic (fcc), nickel-based alloy. In-situ neutron-diffraction measurements were conducted to monitor the peak-intensity, peak-position, and peak-broadening evolution during a displacement-controlled, monotonic-tension experiment at room temperature. The measured lattice-strain evolution and the macrostress/macrostrain curves were used to obtain the material parameters required for simulating the texture development by a visco-plastic self-consistent (VPSC) model. The simulated texture compared favorably with experimentally-determined texture results over a range of 0 to 30 pct engineering strain. The grain-orientation-dependent input into the Debye-intensity ring was considered. Grains favorably oriented relative to the two detector banks in the geometry of the neutron experiment were indicated. For the favorably oriented grains, the simulated slip-system activity was used to calculate the slip-system-dependent, dislocation-contrast factor. The combination of the calculated contrast factor with the experimentally-measured peak broadening allows the assessment of the parameters of the dislocation arrangement within the specifically oriented grains, which has a quantitative agreement with the transmission-electron-microscopy results.

Sign up for access to the world's latest research.

checkGet notified about relevant papers

checkSave papers to use in your research

checkJoin the discussion with peers

checkTrack your impact