Characterization and Prevention of Metal Overflow in Ultra-Thin Au-Sn Eutectic Chip Bonding for Packaging and Integration of Extreme Heat Flux Micro-Coolers (original) (raw)
Related papers
Au-Sn Eutectic Chip-Bonding for High Heat-Flux Vapor-Chamber Applications
2018
Chip-level bonding between components has been a widely studied subject for decades in the electronics industry, where several bonding methods like high temperature hydrophilic/hydrophobic, fusion, anodic and intermediate metal layer bonding have been investigated. Eutectic bonding, which leverages the diffusion between metal layers at relatively low temperature has gained popularity because of its superior strength, hermeticity and significantly relaxed restrictions on substrate type, roughness and flatness.
Intermetallic Compounds - Formation and Applications, 2018
Solid-liquid interdiffusion (SLID) bonding for microelectronics and microsystems is a bonding technique relying on intermetallics. The high-melting temperature of intermetallics allows for system operation at far higher temperatures than what solder-bonded systems can do, while still using similar process temperatures as in common solder processes. Additional benefits of SLID bonding are possibilities of fine-pitch bonding, as well as thin-layer metallurgical bonding. Our group has worked on a number of SLID metal systems. We have optimized wafer-level Cu-Sn SLID bonding to become an industrially feasible process, and we have verified the reliability of Au-Sn SLID bonding in a thermally mismatched system, as well as determined the actual phases present in an Au-Sn SLID bond. We have demonstrated SLID bonding for very high temperatures (Ni-Sn, having intermetallics with melting points up to 1280°C), as well as SLID with low process temperatures (Au-In, processed at 180°C, and Au-In-Bi, processed at 90-115°C). We have verified experimentally the high-temperature stability for our systems, with quantified strength at temperatures up to 300°C for three of the systems: Cu-Sn, Au-Sn and Au-In.
Journal of Electronic Materials, 2009
A fluxless process of bonding large silicon chips to ceramic packages has been developed using a Au-Sn eutectic solder. The solder was initially electroplated in the form of a Au/Sn/Au multilayer structure on a ceramic package and reflowed at 430°C for 10 min to achieve a uniform eutectic 80Au-20Sn composition. A 9 mm × 9 mm silicon chip deposited with Cr/Au dual layers was then bonded to the ceramic package at 320°C for 3 min. The reflow and bonding processes were performed in a 50-mTorr vacuum to suppress oxidation. Therefore, no flux was used. Even without any flux, high-quality joints were produced. Microstructure and composition of the joints were studied using scanning electron microscopy with energy-dispersive x-ray spectro- scopy. Scanning acoustic microscopy was used to verify the joint quality over the entire bonding area. To employ the x-ray diffraction method, samples were made by reflowing the Au/Sn/Au structure plated on a package. This was followed by a bonding process, without a Si chip, so that x-rays could scan the solder surface. Joints exhibited a typical eutectic structure and consisted of (Au,Ni)Sn and (Au,Ni)5Sn phases. This novel fluxless bonding method can be applied to packaging of a variety of devices on ceramic packages. Its fluxless nature is particularly valuable for packaging devices that cannot be exposed to flux such as sensors, optical devices, medical devices, and laser diodes.
Au-Sn SLID Bonding: A Reliable HT Interconnect and Die Attach Technology
Metallurgical and Materials Transactions B, 2013
Au-Sn solid-liquid interdiffusion (SLID) bonding is an established reliable high temperature (HT) die attach and interconnect technology. This article presents the life cycle of an optimized HT Au-Sn SLID bond, from fabrication, via thermal treatment, to mechanical rupture. The layered structure of a strong and uniform virgin bond was identified by X-ray diffraction to be Au/f (Au 0.85 Sn 0.15 )/Au. During HT exposure, it was transformed to Au/b (Au 1.8 Sn 0.2 )/Au. After HT exposure, the die shear strength was reduced by 50 pct, from 14 Pa to 70 MPa, which is still remarkably high. Fractographic studies revealed a change in fracture mode; it was changed from a combination of adhesive Au/Ni and cohesive SiC fracture to a cohesive b-phase fracture. Design rules for high quality Au-Sn SLID bonds are given.
AlN-AlN Wafer Bonding and Its Thermal Characteristics
ECS Transactions, 2014
Homogeneous bonding was successfully demonstrated on 150 mm Si wafers by face-to-face fusion bonding of two clean and smooth aluminum nitride (AlN) layers. Characterization result from XPS confirms the layer composition and reveals that approximately 5 nm of the layer surface was partially oxidized during processing. The as-bonded wafer pair is nearly void and particle free with a high bonding strength of 1263.0 mJ/m2, enabling it to withstand the subsequent process steps. In addition, the AlN-AlN bonded wafers appear to have the best heat dissipation capability when compared with other bonded wafers, which used SiO2 or Al2O3 as the bonding layer.
Au-Sn Solders Applied in Transient Liquid Phase Bonding: Microstructure and Mechanical Behavior
Social Science Research Network, 2019
Transient liquid phase bonding offers one option to generate a robust lead-free die attach with sound thermal and electrical conductivity in microelectronic packages. However, it is a challenge to characterize the microstructure and mechanical behavior of the bonding layer because of its ultra-thin thickness and its nano-sized constituents. We show that microstructures and local mechanical properties of such a modern solder systems are accessible with state-of-the-art methods including transmission electron microscope, synchrotron X-ray nano-beam diffraction as well as micro-scale mechanical testing. Three sub-regions with different morphologies have been identified within the bonding area, and their contained phases have been mapped. Two of the sub-regions contain nanosized intermetallic compounds (IMC) while the third one is mostly composed of an FCC Au-Cu solid solution with a Cu concentration gradient. On top of that, micro-cantilever bending testing has been conducted to investigate the mechanical behavior of the bonding region. The two IMC sub-regions show brittle behavior while the Au-Cu sub-region is ductile.
Characterization of Wafer-Level Thermocompression Bonds
Journal of Microelectromechanical Systems, 2004
Thermocompression bonding joins substrates via a bonding layer. In this paper, silicon substrates were bonded using gold thin films. Experimental data on the effects of bonding pressure (30 to 120 MPa), temperature (260 and 300 C), and time (2 to 90 min) on the bond toughness, measured using the four-point bend technique, are presented. In general, higher temperature and pressure lead to higher toughness bonds. Considerable variation in toughness was observed across specimens. Possible causes of the nonuniform bond quality were explored using finite element analysis. Simulation results showed that the mask layout contributed to the pressure nonuniformity applied across the wafer. Finally, some process guidelines for successful wafer-level bonding using gold thin films are presented. [1170] Index Terms-Bond characterization, thermocompression bonding, wafer bonding. I. INTRODUCTION W AFER bonding has enhanced fabrication capabilities for microelectromechanical systems (MEMS). While Si fusion and anodic bonding may be the most prominent wafer bonding methods, they are not the only options for joining substrates. Wafers can be effectively bonded together by using bonding layers such as polymers, solders and thin film metals. The incorporation of metals, especially those that are conductive, in conjunction with through-wafer via technology, also presents opportunities for packaging applications. Hybrid structures consisting of devices fabricated separately on different substrates can also be created by wafer-level bonding. Metallic bonds form when the distances between the two substrates are so small that it becomes energetically favorable for surfaces to coalesce in order to eliminate the interfacial energy. The surfaces can be brought together by the application of pressure. Due to surface roughness, bonds initially form where the surfaces touch at asperity contacts. As the materials deform under pressure, the asperity heights decrease, and more areas are brought into contact. At room temperature, relatively high pressures are needed for interatomic attraction to overcome surface Manuscript