Investigation Of Formation Kinetics Of CrSi2, TaSi2 And Pt2Si By Ion Beam Mixing (original) (raw)

1985

Abstract

Bilayers of Si/metal (metal on top) and metal/Si (Si on top) were annealed in vacuum to produce the Si/silicide/metal and metal/silicide/Si configurations, respectively. The sandwich structures were then irradiated with Xe ions of energies ranging from 125 to 300 keV such that the Xe ions traverse only one of the two interfaces (metal-silicide or silicide-Si). In the case of CrSi2, irradiation above 150°C induces further and laterally uniform growth of a stoichiometric layer of silicide, but only when the Cr/CrSi2 interface is traversed, not when the other interface is traversed. We conclude that the formation of CrSi2 is an interface-limited process, which is consistent with the linear time dependence of the growth of CrSi2 under thermal annealing, and that the limiting reaction occurs at the Cr/ CrSi2 interface. On the other hand, in TaSi2 for temperatures up to 500°C, and in Pt2Si at room temperature, Xe ions penetrating through only one of either of the two interfaces does not i...

Uri Shreter hasn't uploaded this paper.

Create a free Academia account to let Uri know you want this paper to be uploaded.

Ask for this paper to be uploaded.