Experimental Study of 3D printing Density Effect on the Mechanical Properties of the Carbon-Fiber and Polylactic Acid Specimens (original) (raw)
Related papers
Mechanical Behaviour of 3D Printed Composite Materials
Fiabilitate şi Durabilitate, 2017
A fused deposition modelling 3D printer device was employed to fabricate 3D polymeric composite structures in order to evaluate their mechanical properties. Several experimental test methodswere used in the current workto characterize the mechanicalbehaviour ofneat polyethylene terephthalate glycol (PETG) and PETG reinforced with carbon fibres. To determine the static compression stiffness and hysteresis of the specimens, compression and cyclic tests were conducted. Considering the obtained results,PETG's stiffness was improved with the embedded ofcarbon fibres,while its damping capacity wasmoderately reduced.
Brazilian Journal of Development
Fused filament fabrication is one of the most widely used additive manufacturing methods due to its low cost, easy postprocessing and wide variety of thermoplastic materials that can be used in this technique. The application of this method for functional parts manufacturing requires knowing the mechanical properties of the material depending on the process parameters. This work determines the effect of layer thickness, filling angle, infill density, and position on the table on the mechanical properties under tension of modulus of elasticity and ultimate tensile strength of polylactic acid reinforced with carbon fiber fabricated by this method. Stress tests were performed using ISO 527-1 standards. The modulus of elasticity varies between 3138 MPa and 3095 MPa, while the maximum effort is between 28.62 MPa and 28.56 MPa. Finally, analysis of variance showed that infill density is the parameter that affects the most mechanical properties.
3D printing of composites: design parameters and flexural performance
Rapid Prototyping Journal, 2020
Purpose 3D printing of composites has a high degree of design freedom, which allows for the manufacture of complex shapes that cannot be achieved with conventional manufacturing processes. This paper aims to assess the design variables that might affect the mechanical properties of 3D-printed fibre-reinforced composites. Design/methodology/approach Markforged Mark-Two printers were used to manufacture samples using nylon 6 and carbon fibres. The effect of fibre volume fraction, fibre layer location and fibre orientation has been studied using three-point flexural testing. Findings The flexural strength and stiffness of the 3D-printed composites increased with increasing the fibre volume fraction. The flexural properties were altered by the position of the fibre layers. The highest strength and stiffness were observed with the reinforcement evenly distributed about the neutral axis of the sample. Moreover, unidirectional fibres provided the best flexural performance compared to the o...
CHARACTERIZATION AND ANALYSIS OF MECHANICAL PROPERTIES FOR 3D PRINTING MATERIALS
IRJET, 2022
Abstract - The recent developments in the 3D printing technology enables the digital manufacturing In mass-scale distribution and also the ready availability of 3D printers for the public at lowcostsand high mechanical properties makes the scientists to look at the properties of the 3Dprintingmaterials.However, to make 3D objects polymers are mainly used which generally have low mechanical properties. So, that there is an urgent need to charecterise and analyze the mechanical properties to assess which 3D printing materials have better properties. This work is aimed to find the best 3D printing material from existing materials. In this work, initially the mechanical properties of the 3D printing polymers like polylactic acid (PLA), Lay Wood have been analyzed. This work would propose the best 3D printing material from current basic 3D printing materials with improved mechanical properties
Composite Structures, 2021
Fused deposition modelling (FDM) is one of the most popular additive manufacturing (AM) technique which is used to investigate the elastic properties of 3D printed polyamide-based polymer composites structures. The aim of this work is to study the mechanical properties of continuous carbon fibre reinforced polyamide polymer composite samples using tensile and flexural testing by varying the fibre volume contents with applying pressure, temperature and holding the samples for 60 minutes in the platen press. The results showed that the strength and stiffness increased with the increase in fibre volume content (fraction). Hot pressed samples exhibited the increase in tensile strength by about 27 % and elastic modulus by 11 % because of increasing the fibre volume fraction from 29 % to 35%. Synergetic effect of both short and continuous carbon fibre was also studied, and it was observed that the tensile properties were higher for the samples reinforced with short and continuous fibre than only continuous fibre polymer composites. Effects of voids on 3D printed continuous carbon fibre-reinforced polymer composites were quantified. A microstructure study of the 3D printed polymer composites was carried out using scanning electron microscope (SEM). Following SEM analysis on the tested specimens, it was observed that there was a strong correlation between the mechanical properties and the microstructure. Fibre volume fraction was measured using acid digestion method to determine the amount of fibre contents before and after hot pressing (compaction). From Micro-Computed Tomography (µCT) it was confirmed that hot pressing reduced the void content which in return increased the strength and modulus.
Materials
This paper introduces novel research into specific mechanical properties of composites produced by 3D printing using Continuous-Fiber Fabrication (CFF). Nylon (Onyx) was used as the composite base material, while carbon constituted the reinforcement element. The carbon fiber embedment was varied in selected components taking values of 0°, 45°, 90°, and 135° for parts undergoing tensile testing, while one specific part type was produced combining all angles. Carbon-fiber-free components with 100% and 37% fillings were also produced for comparison purposes. Parts undergoing the Charpy impact test had the fibers deposited at angles of 0° and 90°, while one part type was also produced combining the four angles mentioned before. Carbon-fiber-free parts with 100% and 37% fillings were also produced for comparison purposes as with the first part. The Markforged MARK TWO 3D printer was used for printing the parts. These were subsequently scanned in the METROTOM 1500 computed tomography and ...
Materials and Manufacturing Processes, 2020
Continuous carbon-fiber-reinforced acrylonitrile butadiene styrene (ABS) has been manufactured by a method based on fused deposition modeling (FDM). Before 3D printing, the carbon fibers pass through an ABS-acetone bath to prepare solution impregnated fibers (prepregs). Continuous fiber-reinforced thermoplastic composites (CFRTCs) were printed by feeding carbon fiber prepregs and ABS filament, simultaneously into a special single port nozzle. By varying print conditions such as nozzle diameter, layer height, and print speed, composite specimens were printed with different qualities. The visual evaluation of printed composites was used to determine a process window for stable or unstable CFRTC printing. In the obtained process window, four regions were observed including fiber fuzzing or tearing instability, fiber twisting instability, low quality stable print and high quality stable print. The optimum condition to print CFRTCs was found and then specimens were printed to investigate mechanical properties under the optimal printing condition. The mechanical and morphological properties of visual-optimized 3D-printed composites, without any fiber fuzzing, tearing or twisting were investigated. The results showed that tensile, flexural, and interlaminar shear strength of 3D-printed ABS-carbon CFRTCs have increased 313%, 121%, and 54%, respectively, when compared with the neat ABS 3D-printed samples.
Tensile Behavior of 3D Printed Polylactic Acid (PLA) Based Composites Reinforced with Natural Fiber
Polymers
Natural fiber-reinforced composite (NFRC) filaments for 3D printing were fabricated using polylactic acid (PLA) reinforced with 1–5 wt% henequen flour comprising particles with sizes between 90–250 μm. The flour was obtained from natural henequen fibers. NFRCs and pristine PLA specimens were printed with a 0° raster angle for tension tests. The results showed that the NFRCs’ measured density, porosity, and degree of crystallinity increased with flour content. The tensile tests showed that the NFRC Young’s modulus was lower than that of the printed pristine PLA. For 1 wt% flour content, the NFRCs’ maximum stress and strain to failure were higher than those of the printed PLA, which was attributed to the henequen fibers acting as reinforcement and delaying crack growth. However, for 2 wt% and higher flour contents, the NFRCs’ maximum stress was lower than that of the printed PLA. Microscopic characterization after testing showed an increase in voids and defects, with the increase in f...
Mechanical characterization of Polymer matrix composites produced by 3D printing
2017
In the last decade, additive manufacturing (AM) technology has undergone exponential growth and gained more and more importance in the recent research, mainly due to the freedom of creating sophisticated geometries that are impossible to produce using either one or a combination of several alternative production techniques. AM technology has mostly been used for prototyping application during the product design and development phase in many different industrial sectors. However, 3D printed prototypes have limited mechanical properties and the printed parts usually cannot fulfil mechanical requirements for functional applications. As a consequence, this problem has given rise to a new concept of 3D printing technique based on adding fibers to the polymeric material matrix. By means of this technique, the mechanical properties of the printed parts can be enhanced. The current thesis has researched in carbon fiber reinforcement for nylon specimens printed by the Mark One printer from M...
Mechanical characterization of FDM 3D printing of continuous carbon fiber reinforced PLA composites
Composites Part B: Engineering, 2019
Additive manufacturing of fiber reinforced composites is of great interest in various industrial applications. In this study, an innovative extruder is designed and manufactured for fused deposition modeling (FDM) 3D printers in order to produce continuous fiber reinforced thermoplastic (CFRT) composites. There are some challenges along this way such as making tension in fiber, fiber surface preparation, printing temperature and feed rate to produce a composite part with good quality. These challenges are discussed in detail. The main advantage of this extruder is that it can be mounted on the available FDM 3D printers and consequently there is no need to design a new chassis. In order to assess the quality of products, standard tensile and three-point bending specimens made of pure poly lactic acid (PLA) and carbon fiber reinforced PLA are printed and tested under quasi-static loading. Experimental results show significant improvements of tensile and bending properties of PLA. Morphological analysis is also conducted to study the bonding between the carbon fiber and PLA.