Partial substitution of Zn Effects on the Structural and Electrical Properties of High Temperature Hg0.95Ag0.05Ba2Ca2Cu3O8+δ Superconductors (original) (raw)

2018, Journal of Physics: Conference Series

The effect of the Ag partial substitution at Hg site in HgO δ layer and Zn partial substitution at Ca site in CaO layer on the structure ,T c ,electrical properties , and oxygen content for Hg-1223 have been studied. Bulk polycrystalline Hg 1-x Ag x Ba 2 Ca 2-y Zn y Cu 3 O 8+δ compound samples with x=0.05 and y =0.0, 0.05, 0.1, 0.15, 0.2, 0.25, and 0.3, are synthesized by a solid state reaction process. Structural properties are studied by using X-ray powder pattern, the high temperature phase superconductor (Hg-1223) of the tetragonal structure didn't change with the partial substitution of Zn and Ag ions , lattice parameters c ,c/a are established to vary with Ag and Zn-substitution. The surface morphology has been studied by using atomic force microscopes (AFM), showed that all specimens have good crystalline and homogeneous surface. Also give a best nano size value is 75.72 nm at x=0.05 and y=0.3. Four probe technique is used to measure T c. The T c were found to be increases from 129 K to 147 K and oxygen content were found to be increases with increasing Zn. In addition, dielectric properties (dielectric constant, dielectric loss factor, and the alternating electrical conductivity) are characterized directly by relating with Ag and Zn concentration.