Fine-grained magnetoelectric Sr0.5Ba0.5Nb2O6–CoFe2O4 composites synthesized by a straightforward one-pot method (original) (raw)

Fine-grained magnetoelectric Sr0.5Ba0.5Nb2O6–CoFe2O4 composites synthesized by a straightforward one-pot method

Magnetoelectric (Sr0.5Ba0.5Nb2O6)1x(CoFe2O4)x (x = 0.2–0.6) composites were prepared by a one-pot softchemistrysynthesis using PEG400. Calcining at 700 ◦C resulted in nanocrystalline composite powders (dcryst. =24–30 nm) which were sintered between 1050 and 1200 ◦C to ceramic bodies with relative densities up to 98%.SEM investigations confirm the formation of composite ceramics with a 0–3 connectivity and variable grain sizesfrom 0.2 to 3.6 μm for sintering up to 1150 ◦C, while sintering at 1200 ◦C leads both to a change in themicrostructure and a considerable grain growth. Magnetic measurements at 300 K reveal ferrimagnetic behaviourwith saturation magnetization values smaller than bulk CoFe2O4 and coercivities between 790 and 160 Oe.Temperature-dependent impedance spectroscopy showed that the relative permittivities decrease both withrising frequency and CoFe2O4 fraction. The frequency dependence of the impedance can be well described usinga single RC circuit. Magnetoelectric meas...