Photocatalytic activity of CaTaO 2 N nanocrystals obtained from a hydrothermally synthesized oxide precursor (original) (raw)

N-Loaded TiO2 for Photocatalytic Degradation of Methyl Orange under Visible Light Irradiation

Advanced Materials Research, 2012

Nitrogen-loaded TiO2 (N-loaded TiO2), a visible-light driven catalyst, was successfully synthesized by the modified sol-gel method. Physical characterizations of the as-prepared catalysts have been performed by using X-ray diffraction (XRD), Diffuse reflectance UVvisspectroscopy(DRUVvis), Raman spectroscopyand BETspecific surface areain order to obtain structure-activity relationship. Results from Raman spectroscopy clearly suggested that N atoms were incorporated into the TiO2 crystal lattice as evidenced by the vibrational peak of TiN in TiO2-xNx.DR UVvis results also suggested that the nitrogen dopant might be responsible for narrowing the TiO2band gap energy, thus resulting in a shift towards the visiblelight region. Photocatalytic activity of N-loaded TiO2 evaluated through the degradation of methyl orange (MO)under visible light irradiation (l> 400 nm) indicated that all N-loaded photocatalysts exhibited significantly higher activities than the unloaded TiO2 and Degussa...

Design, synthesis and Chemical-physical characterization of photocatalytic inorganic nanocrystals for technological applications

2013

This work was based on the synthesis and characterization of innovative crystals for biomedical and technological applications. Different types of syntheses were developed in order to obtain crystals with high photocatalytic properties. A hydrothermal synthesis was also processed to correlate the chemical-physical characteristics with synthesis parameters obtaining synthesis of nanoparticles of titanium dioxide with different morphology, size and crystalline phase depending on the variation of the synthesis parameters. Also a synthesis in water at 80 °C temperature and low pressure was developed from which anatase containing a small percentage of brookite nanoparticles were obtained, presenting a high photocatalytic activity. These particles have been used to obtain the microcrystals formed by an inorganic core of hydroxyapatite surface covered by TiO2 nanoparticles. Micrometer material with higher photocatalytic has been produced. The same nanoparticles have been functionalized wit...