Alumina-boron catalysts for oxidative dehydrogenation of ethylbenzene to styrene: Influence of alumina-boron composition and method of preparation on catalysts properties (original) (raw)
2019, Chinese Journal of Catalysis
Different mole ratio Al-B catalysts (Al-10B to Al-35B) were synthesized by using sol-gel (SG) method. Ethyl benzene (EB) dehydrogenation in the presence of oxygen and water steam was carried out on these catalysts at 450-500 °C with EB contact time of 0.54 gcat.s.cm-3. Acidity of Al-B catalysts was estimated by using NH3-TPD-mass spectral analysis studies. SEM-mapping images revealed fine distribution of boron up to 15% of its loading in alumina (Al-15B), whereas, boron aggregation was observed in higher boron content (Al-25B and Al-35B) catalysts. Essentially, acid sites of very weak strength (Tmax ≤ 125 °C) were observed for Al and Al-10B catalysts and resulted in low EB conversion and styrene yield. On the other hand, acid sites of weak strength (Tmax ≤ 180 °C) were observed for Al-25B and Al-35B catalysts and resulted in high EB conversion. However, greater styrene yield (43.2%) with reasonable EB conversion (46%) was obtained on acid sites of weak moderate strength in Al-15B catalyst. Further, Al-15B catalyst was synthesized by using co-precipitation (COP) and impregnation (IMP) methods. Acid sites related to NOx formation during the NH3-TPD-mass analysis on IMP and COP catalyst essentially improved the EB conversion to 66% and 63% respectively at 500 °C. However, these acid sites were diminished in Al-B SG catalyst and resulted in 50% of EB conversion at 500 °C. At 50% of EB conversion level, styrene selectivity of 73%, 82.5% and 84% were observed on Al-B IMP, Al-B COP and Al-SG catalysts, respectively. Hence, different method of preparation of Al-B catalyst generated acid sites of different strength and density and thereby influenced the styrene formation.
Sign up for access to the world's latest research.
checkGet notified about relevant papers
checkSave papers to use in your research
checkJoin the discussion with peers
checkTrack your impact
Loading Preview
Sorry, preview is currently unavailable. You can download the paper by clicking the button above.