Vacancy Type Defects in Oxide Dispersion Strengthened Steels (original) (raw)

Materials Science Forum, 2013

Abstract

This study was focused on commercial oxide-dispersion strengthened (ODS) steels - MA 956 (20%Cr), PM 2000 (19%Cr), ODM 751 (16%Cr) and MA 957 (14%Cr) developed for fuel cladding of GEN IV reactors. The ODS steels are described in order to comparison of their microstructure features. Vacancy defects were observed by Doppler Broadening Spectroscopy (DBS) and Positron Annihilation Lifetime Spectroscopy (PALS). Residual stress proportional to all kinds of defects was investigated by Magnetic Barkhausen Noise (MBN) measurement. The highest presence of open volume defects was found in MA 956 and the lowest defect concentration in MA 957, although this steel contains the largest defects (six-vacancies together with dislocations). Other investigated steels demonstrated probably three- or four-vacancy clusters. Further, results from positron technique indicated proportionality of chromium content to defect concentration. Magnetic Barkhausen noise results also showed that Hpeak value (describ...

V. Krsjak hasn't uploaded this paper.

Let V. know you want this paper to be uploaded.

Ask for this paper to be uploaded.