Evaluation of Inhibitive Performance of Some Plants Extracts on Low Carbon Steel Corrosion (original) (raw)
2014, Studies in Engineering and Technology
The corrosion inhibitive potential of Plumeria Alba, Blighia Sapida and Secamone Afezeli plants extracts on heat-treated and non-heat-treated mild steel samples immersed in different concentrations of hydrochloric acid (HCl) were investigated using weight loss technique. The mild steel samples were cut and prepared for the corrosion test in the acid media mixed with the plant extracts obtained by natural drying, grinding and chemical extraction using hexane. The plants were collected from the botanical garden of University of Lagos, Nigeria. Samples of the mild steel were weighed before immersion and at regular interval of 7 days for a period of 56 days after immersion. The experiment was repeated using 0.1 M and 0.2 M of an inorganic inhibitor. Results obtained showed that the extract of Blighia Sapida exhibited the highest inhibitive power, while annealed samples have the least corrosion rate in the Hcl solution.
Loading Preview
Sorry, preview is currently unavailable. You can download the paper by clicking the button above.