Effects of Waste Glass Powder on Properties of Self-Compacting Repair Mortars (original) (raw)

International Journal of Engineering Research in Africa

Abstract

This paper studies the effects of fine waste glass powder content (WGP) on fresh and hardened properties of self-compacting repair mortar mixes (SCRMs). For this purpose, mortar mixes were prepared to replace cement with waste glass powder ranging from 0 to 30% at 10% interval and tested. Fresh properties were assessed using mini-slump flow and mini V-funnel. Hardened properties assessed for all mixes were water absorption (at 28-days of age), compressive and flexural strengths (at 7, 28 and 56-days of age). In addition, the adhesion between the repair mortar mixes and substrate was conducted using a 3-point flexural test on a composite prism (half mortar/half substrate) at 28 and 56-days of age. The results showed that glass powder had a negative effect on the workability of mortars. However, in the hardened state, it had a good influence on the strength development after 28 days, durability and adhesion of mortars with the substrate for a waste glass powder content not exceeding 20%.

Toufik Boubekeur hasn't uploaded this paper.

Let Toufik know you want this paper to be uploaded.

Ask for this paper to be uploaded.