Structural and Optical Properties of Gold Nanoparticles Formed by Wet-Chemical Method (original) (raw)
Related papers
Synthesis and optical properties of colloidal gold nanoparticles
Journal of Physics: Conference Series, 2009
Colloidal gold nanoparticles (spheres) have been prepared from HAuCl4 containing aqueous solution by using X-ray irradiation and by chemical reduction method. Gold nanorods were synthesized according to the seed-mediated growth method. The colloidal gold nanoparticles were characterized by using transmission electron microscopy, X-ray diffraction, and UV-VIS absorption spectroscopy. It was found that the concentration of the precursors affects the size of the nanoparticles. In the chemical reduction approach the size of nanoparticles can be controlled by varying amount of trisodium citrate, but in the photochemical method the size of nanoparticles can been controlled by varying the ratio of HAuCl4 to TX-100 and X-ray irradiation duration. Gold nanorods have been synthesized according to the seed-mediated growth method with two steps. The effect of silver acetate and CTAB on formation of gold nanorods has been studied.
Gold Nanoparticles: Synthesis, Optical Properties, and Application
Inorganic Materials: Applied Research, 2018
The four mostly frequently used gold nanoparticle species-nanospheres, nanorods, nanoshells, and nanocells-whose surface plasmonic resonance peaks lie in the visible to near-infrared range are considered. Their synthesis, optical properties, and some fields of practical application of the relevant materials are analyzed.
Synthesis and Characterization of Gold Nanoparticles
Various methodologies are currently available for synthesis of gold nanoparticles; chemical reduction method is among the interesting ones. Gold chlorauric acid (H[AuCl4]) could be reduced by sodium hydroxide (NaOH) in aqueous solution. Within this work, poly diallyl dimethyl ammonium chloride (PDDA) was used as a capping agent for synthesis of gold nanoparticles. Characterization techniques including scanning electron microscopy (SEM), atomic force microscopy (AFM) and UV-visible spectroscopy approved the obtained gold nanoparticles.
Optical Properties of Gold Nanoparticles: Shape and Size Effects
International Journal of Optics and Photonics, 2021
Nobel metal nanoparticles (NPs) are widely used in various applications including optical and biological sensors, biomedicine, photocatalysts, electronics, and photovoltaic cells. The optical properties of gold NPs are surveyed in this paper under the Localized Surface Plasmon Resonance (LSPR) effect, which increases the light absorption and scattering at the LSPR wavelength. This LSPR frequency depends on various factors, including the shape and size of the particles as well as incident electromagnetic polarization. Here, the optical response of gold NPs with different shapes and sizes are investigated using the finite element method (FEM). The results show that the bandwidth, amplitude, and LSPR wavelength depend on the shape and dimensions of the NPs as well as the polarization of the incident light. The LSPR wavelength changes from 500 to 650 nm for different shapes of the gold NPs including sphere, octahedral, cube, ellipsoid, triangle, and with identical volume. To study the N...
Determination of Size and Concentration of Gold Nanoparticles from UV-Vis Spectra
The dependence of the optical properties of spherical gold nanoparticles on particle size and wavelength were analyzed theoretically using multipole scattering theory, where the complex refractive index of gold was corrected for the effect of a reduced mean free path of the conduction electrons in small particles. To compare these theoretical results to experimental data, gold nanoparticles in the size range of 5 to 100 nm were synthesized and characterized with TEM and UV-vis. Excellent agreement was found between theory and experiment. It is shown that the data produced here can be used to determine both size and concentration of gold nanoparticles directly from UV-vis spectra. Equations for this purpose are derived, and the precision of various methods is discussed. The major aim of this work is to provide a simple and fast method to determine size and concentration of nanoparticles.
The Effect of Gold Salt Concentration in the Production of Gold Nanospheres
Journal of Applied Mathematics and Physics, 2020
The optical, electrical and chemical properties of the gold nanospheres synthesized by different gold concentrations in deionized water through a simple chemical reduction method (Turkevich method) were studied. They were dependent on the variation of the gold salt concentration. The peaks of the surface Plasmon resonance (SPR) absorption band and their wavelengths were detected by a UV-visible spectrophotometer. The diameters of the spherical gold nanoparticles were measured theoretically using UV-visible absorption spectrum analysis of the synthesized gold nanoparticles in colloidal form by calculating the ratio of the absorbance at the surface Plasmon resonance (SPR) peak to the absorbance at the lowest peak closed to SPR peak. The values of the gold nanoparticles diameters were (23 nm) and decreased to (13 nm) as the function of molarity changed in the range (0.1-0.3 mM). They were compared with the results of the transmission electron microscopy (TEM), which was about (15-20 nm) measured by the reference images of Sigma-Aldrich values. The conductivity measurements showed increasing the conductivity with molarity increased. The total dissolved solids (TDS) exhibited increase by linear relation with molarity increasing. The pH-value of the gold nanoparticles solutions varied with the molarity and recorded a bowing value of pH-value at (0.2 mM).
Gold Nanoparticles: Preparation, Characterization and Its Stability in Buffer
Among the colorimetric detection tactics, metallic nanoparticle based detection is gaining more attention due to quickness and less resource requirement at the point of use. Unique chemical inertness, shape, size and optical attributes of gold nanoparticles (GNPs) make them ideal for various diagnostic tools. In this approach synthesized GNPs were stabilized by citrate counter ions. These GNPs were characterized for their optical properties, shape, size, zeta potential, and dynamic light scattering. Absorption maxima (λmax) was observed at 519.8 nm with the average particle size of 34.8 nm. Transmission electron microscopy also revealed that the average size of GNPs were about 35 nm. Negative zeta potential (–43.2 mV) indicates presence of negative charge at the surface of GNPs. To find the stability of GNPs in buffer, two buffers (borate and phosphate) having different pH (6.5, 7.5 and 8.5) and same molarity (0.1 M) were evaluated with a purpose to determine the suitable buffer req...
Journal of Nanoparticle Research, 2010
We developed a rapid and non-toxic method for the preparation of colloidal gold nanoparticles (GNPs) by using tryptophan (Trp) as reducing/stabilizing agent. We show that the temperature has a major influence on the kinetics of gold ion reduction and the crystal growth, higher temperatures favoring the synthesis of anisotropic nanoparticles (triangles and hexagons). The as-synthesized nanostructures were characterized by UV-Vis absorption spectroscopy, transmission electron microscopy (TEM), X-ray diffraction (XRD), fluorescence, and surface-enhanced Raman scattering (SERS) spectroscopy. The UV-Vis measurements confirmed that temperature is a critical factor in the synthesis process, having a major effect on the shape of the synthesized GNPs. Moreover, fluorescence spectroscopy was able to monitor the quenching of the Trp fluorescence during the in situ synthesis of GNPs. Using Trp as molecular analyte to evaluate the SERS efficiency of as-prepared GNPs at different temperatures, we demonstrated that the Raman enhancement of the synthesized gold nanoplates is higher than that of the gold spherical nanoparticles.
Comparative Study on Methods for Preparation of Gold Nanoparticles
Green and Sustainable Chemistry, 2012
The gold nanoparticles were prepared in many methods, differed in reducing and dispersion agents and stability. The first solution was prepared by using potassium bitartrate as reducing agent and Polyethylene glycol as a dispersion factor. We got a solution of colloid gold with wine-red color that has been measured the particle size; it was between 50-200 nanometers. The second gold colloidal solution was prepared by using sodium citrate as a reducing agent and without adding a dispersion agent, the color of the final solution is dark grey, but this solution did not remain stable, deposition happened quickly and crystals separated from the solution. The third one was prepared by using sodium citrate as a reducing agent and the solution was heated to a certain temperature, and the color of the solution became dark red after several minutes. Either the fourth method has been prepared gold colloid solution by using potassium bitartrate as a reductant for the gold ion. We have noted that no reaction under normal conditions, while the reaction by heating the solution to high temperature, and when added poly vinyl pyrrolidone will lead to a solution of colloild gold with dark purple-red color and stable under normal conditions for a long time. We measured the particles size in this experiment; it was less than 100 nanometers. We conclude from the above that all the reducing agent needs to appropriate conditions to complete the process of reduction of gold ion, and to get the nano gold particles, therefore; these particles in the colloid solution need to dispersion factor to the survival of the particles widespread so that the solutions with certain concentrations of poly vinyl pyrrolidone can be proven in the process of stability of the gold colloid solution.