Synthetic filament yarn - Weblio 英和・和英辞典 (original) (raw)
例文
In the airbag base fabric obtained by coating the surface of a fabric of a thermoplastic synthetic filament yarn with a silicone, the filament yarn has a raw yarn strength of ≥7.5 cN/dtex, a fineness of the filament yarn of 280-325 dtex and a cover factor of the fabric of 1,800-2,200.例文帳に追加
熱可塑性合成フィラメント糸の織布の表面にシリコーンコーティングを施してなるエアバッグ用基布において、該フィラメント糸の原糸強度が７．５ｃＮ／ｄｔｅｘ以上であり、該フィラメント糸の繊度が２８０〜３２５ｄｔｅｘであり、織布のカバーファクターが１８００〜２２００であるエアバッグ用基布。 - 特許庁
This warp-knitted pile fabric uses a thermoplastic synthetic fiber multi-filament yarn obtained by combining crimping fibers having different crimping rates with a pile yarn of the warp-knitted pile fabric.例文帳に追加
経編パイル布帛のパイル糸に捲縮率の異なる捲縮性繊維を混繊した熱可塑性合成繊維マルチフィラメント糸を使用する。 - 特許庁
To prevent an end part of a synthetic fiber filament yarn from being protruded from a draining bag for kitchen, and a finger nail from being hooked to the end part of the synthetic filament yarn.例文帳に追加
台所用水切り袋から合成繊維フィラメント糸の端部が切りっぱなしの状態で飛び出すのをなくし、指の爪が合成繊維フィラメント糸の端部に引っ掛かるなどしてほつれることがないようにする。 - 特許庁
This synthetic fiber cord for reinforcing rubbers, comprising the twisted union yarn of synthetic filament yarns not having a fuzz or loop on the surfaces with synthetic filament yarns having fuzz or loops on the surfaces, is characterized in that the tensile strength of the synthetic filament yarns having the fuzz or loops on the surfaces is ≥5.0 cN/dtex.例文帳に追加
その表面に毛羽又はループを有さない合成繊維連続フィラメント糸と、その表面に毛羽又はループを有する合成繊維連続フィラメント糸との合撚糸であって、該毛羽又はループを有する合成繊維連続フィラメント糸の引張強度が５．０ｃＮ／ｄｔｅｘ以上である。 - 特許庁
The core yarn filaments consist of a thermoplastic synthetic fiber having 10-50 decitex single fiber fineness, and the fine filament yarn consists of fine filaments or a spun yarn consisting of a thermoplastic synthetic fiber having <10 decitex single fiber fineness.例文帳に追加
芯糸フィラメントは単糸繊度が１０〜５０デシテックスの熱可塑性合成繊維からなり、華糸は単糸繊度が１０デシテックス未満の熱可塑性合成繊維よりなる華糸フィラメント又は紡績糸からなる。 - 特許庁
The method for drawing a thermoplastic synthetic yarn on a hot plate to produce the synthetic yarn is characterized by drawing the thermoplastic synthetic yarn on the hot plate wherein the maximum depth of a cross-sectional curve showing a surface roughness on a fiber-contacting surface of the hot plate is in a range of 20% to 90% based on the single filament diameter of the yarn after drawn.例文帳に追加
熱可塑性合成繊維を熱板上で延伸して合成繊維を製造するに際し、該熱板における接糸面における表面粗度をあらわす断面曲線の最大深さが延伸後の繊維の単糸径の２０％〜９０％の範囲にある熱板上で延伸する。 - 特許庁
This covered filament yarn including a metallized raw yarn is characterized by being obtained by covering a metallized raw yarn as metallized synthetic fiber with a covering yarn at the number of twists of 300-1,000 t/m.例文帳に追加
合成繊維に金属をメッキした金属メッキ原糸にカバリング糸を３００〜１０００ｔ／ｍの撚り数でカバリングしたことを特徴とする金属メッキ糸のカバリング糸条である。 - 特許庁
例文
The sliding surface material comprises a multi-woven fabric (25-50 wt.%) formed by a spun yarn of synthetic fiber and a filament yarn of ethylene tetra-fluoride resin fiber or a twisted yarn with the spun yarn; and a thermosetting synthetic resin (25-50 wt.%) containing an ethylene tetra-fluoride resin (25-35 wt.%) impregnated in it.例文帳に追加
合成繊維の紡績糸と四ふっ化エチレン樹脂繊維のフィラメント糸又は紡績糸との交撚糸から形成された多重織織布（２５〜５０重量％）とそれに含浸された四ふっ化エチレン樹脂（２５〜３５重量％）を含有した熱硬化性合成樹脂（２５〜５０重量％）とからなる。 - 特許庁