weblio英語例文検索 (original) (raw)
MJを含む例文一覧と使い方
該当件数 : 234件
例文
The method for manufacturing the cell layer constituting the display cells of the electronic display surface having a number of the display cells capable of electrically changing the display includes a process (a) of irradiating a film material 10 to constitute the cell layer with laser light L for the irradiation time of 1 to 10 μsec irradiation intensity of 0.1 to 10 mJ/shot to allow the cell spaces 12 to eliminate and form.例文帳に追加
電気的に表示変更できる多数の表示セルを有する電子表示面の、表示セルを構成するセル層を製造する方法であって、セル層となる膜材料１０に、レーザ光Ｌを０．１〜１０ｍＪ／ショットの照射強度、１〜１０μｓｅｃの照射時間で照射してセル空間１２を消失形成する工程（ａ）を含む。 - 特許庁
The resin composition for the coating material comprising a resin and a curing agent as main components, is regulated so that an organic coated film obtained only from the resin and the curing agent, or optionally with a curing catalyst added thereto has ≤35 mJ/mm^2 elastic strain energy at 100°C, or ≤60% proportion of the elastic strain energy.例文帳に追加
主として樹脂、硬化剤が含まれる塗料用樹脂組成物のうち、樹脂と硬化剤のみ、あるいは必要に応じて硬化触媒をさらに加えた有機皮膜の１００℃における弾性歪みエネルギーが３５ｍＪ／ｍｍ^2以下、あるいは弾性歪みエネルギー比率が６０％以下であることを特徴とする塗料用樹脂組成物に関する。 - 特許庁
The method for manufacturing the resin-coated metal body is characterized in that a predetermined region of a resin film on the metal body on which the resin film with an orientation crystallinity is laminated at least on one face is irradiated with a laser beam which has a wavelength with an absorptivity coefficient of the resin film of ≤20 and an energy density of 10-100 mJ/mm^2.例文帳に追加
配向結晶性を有する樹脂フィルムが少なくとも一面に積層された金属体における前記樹脂フィルムの所定の領域に、前記樹脂フィルムの吸光係数が２０以下となる波長であってエネルギー密度が１０〜１００ｍＪ／ｍｍ^2のレーザ光を照射することを特徴とする樹脂被覆金属体の製造方法。 - 特許庁
On the basis of the power consumption information table 170 and the predicted time, a mode switching decision section 103 compares the power consumption (mJ) between the case that switching is performed into the power saving mode and the case that switching is not performed, and only if the former is far less than the latter, decides that switching should be executed into the power-saving mode.例文帳に追加
モード切替判定部１０３は、電力消費情報テーブル１７０と予測された時間とに基づいて、省電力モードへの切替えを行った場合と行わなかった場合との間で、電力消費量（ｍＪ）を比較し、前者が後者に比べて、電力消費量が十分に低い場合に限り、省電力モードへ切り替える旨の判定をする。 - 特許庁
例文
The ethylene oxide copolymer is a random copolymer that has a crystallization temperature of ≤20°C, a glass transition temperature of ≤-64°C and heat of crystallization of ≤60 mJ/mg, is obtained by polymerizing a monomer composition containing ≥10 mol% of copolymer, and has a weight-average molecular weight within the range of ≥20,000 and ≤500,000.例文帳に追加
エチレンオキシド系共重合体は、結晶化温度が２０℃以下であり、かつガラス転移温度が−６４℃以下であり、結晶化熱が６０ｍＪ/ｍｇ以下であり、かつコモノマーを１０モル％以上含むモノマー組成物を重合して得られ、重量平均分子量が２万以上５０万以下の範囲内であるランダム共重合体である。 - 特許庁
例文
In the heat-sensitive adhesive composition comprising a thermoplastic resin and a solid plasticizer as principal components, the solid plasticizer comprises at least two kinds of compounds, and a difference in solubility parameter between the at least two kinds of compounds according to the Fedors method is ≤3 (MJ/m^3)^1/2.例文帳に追加
熱可塑性樹脂と固体可塑剤とを主成分とする感熱性粘着剤組成物において、固体可塑剤が、少なくとも２種の化合物からなり、かつ該少なくとも２種の化合物間のＦｅｄｏｒｓの方法による溶解度パラメータの差が３（ＭＪ／ｍ^３）^１／２以下であることを特徴とする感熱性粘着剤組成物などを提供した。 - 特許庁
The skeleton part S of the punched plate W is passed between plural separation rollers 69 offset in series in the plate feeding direction and in the vertical direction, the micro-joint part MJ is broken by the vibration given to the plate by a simple device in the vertical direction, and the product G is automatically separated from the skeleton part S.例文帳に追加
パンチング加工された板材Ｗのスケルトン部Ｓが、板材送り方向に直列に且つ上下方向にオフセットされた複数の分離ローラ６９の間を通過することにより、簡単な装置で板材に対して上下方向に振動が与えられてミクロジョイント部ＭＪが破断し製品Ｇがスケルトン部Ｓから自動的に分離される。 - 特許庁
In the surface reforming method of the hard coating film 12, the surface of the hard coating film 12 is treated by ultraviolet rays, wherein oxygen concentration in an ultraviolet irradiation environment is 3 to 10% and integrated light amount of ultraviolet rays, directly under an ultraviolet ray lamp, is 800 to 2,000 mJ/cm^2.例文帳に追加
本発明のハードコート膜１２の表面改質方法は、ハードコート膜１２の表面に紫外線処理を施すハードコート膜１２の表面改質方法であって、紫外線照射雰囲気中の酸素濃度が３〜１０％、紫外線ランプ直下での紫外線の積算光量が８００〜２０００ｍＪ／ｃｍ^２であることを特徴とする。 - 特許庁
A metal thin film 110 is formed on the back face 1b with the irregularity formed thereon, and thereafter a drain electrode 11 including a silicide layer 111 is formed by irradiating the back face 1b side of the n^+ type substrate 1 with laser light in a condition where the product of photon energy and laser output is set to 1,000-8,000 eV mJ/cm^2.例文帳に追加
そして、凹凸が形成された裏面１ｂ上に金属薄膜１１０を形成した後、ｎ^+型基板１の裏面１ｂ側に光子エネルギーとレーザ出力の積が１０００ｅＶ・ｍＪ／ｃｍ^2以上かつ８０００ｅＶ・ｍＪ／ｃｍ^2以下となるような条件でレーザ光を照射することでシリサイド層１１１を含むドレイン電極１１を形成する。 - 特許庁
例文
In the method for forming a hard coat film, a sol liquid containing an inorganic compound of at least one kind of element selected from the group of silicon, aluminum, zirconium and hafnium prepared by a sol-gel method is applied on a base material and heat treated at a temperature no exceeding 200°C and irradiated with UV rays of at most 100 mJ/cm2 energy.例文帳に追加
ゾルゲル法により形成されたところの、ケイ素、アルミニウム、ジルコニウム、及びハフニウムより成る群から選択される少なくとも一種の元素の無機化合物を含有するゾル液を、基材上に塗布し、２００℃を超えない温度に加熱処理しながら、大きくとも１００ｍＪ／ｃｍ^2の紫外線を照射することを特徴とするハードコート膜形成方法。 - 特許庁
例文
The glossy black-colored packaging container comprises a sheet with intrinsic viscosity of 0.55 or more mainly comprising a polyethylene terephthalate which contains 0.3 to 10 wt.% of carbon, wherein a crystallization temperature with temperature raised of the sheet, which is measured by a thermal analyzer, is 128 degrees or higher and a calorific value of crystallization is 20 mJ/mg or higher.例文帳に追加
カーボンを０．３重量％から１０重量％含有するポリエチレンテレフタレートを主成分とする固有粘度が０．５５以上のシートからなり、前記シートの熱分析器の測定された昇温結晶化温度が１２８度以上、且つ、結晶化熱量が２０ｍＪ／ｍｇ以上のシートを用いた光沢黒色系の包装用容器。 - 特許庁
Lenses 12, 13, 14 and 22 for forming the stepper 1 are formed from a synthetic quartz glass member having a characteristic which is a dissipation factor of ≤0.0050 cm-1 at 193.4 nm, measured after irradiated with 1×104 pulses ArF excimer laser at an energy density of 0.1 μJ/cm2.p to 200 mJ/cm2.p.例文帳に追加
そして、ステッパー１を構成するレンズ類１２，１３，１４，２２を、ＡｒＦエキシマレーザを０．１μＪ／ｃｍ^2・ｐ以上２００ｍＪ／ｃｍ^2・ｐ以下のエネルギー密度で１×１０^4パルス照射したとき、照射後に測定される１９３．４ｎｍにおける損失係数が０．００５０ｃｍ^-1以下となる特性を有する合成石英ガラス部材により構成する。 - 特許庁
For the ink recording medium wherein the ink receptive layer containing a pigment and a binder is provided on at least one side surface of a paper backing, an image sharpness of the ink receptive layer is ≥50% and an internal bonding strength specified in paper pulp test method No. 18-2 of JAPAN TAPPI is 125-280 mJ.例文帳に追加
紙支持体の少なくとも片方の面に、顔料と結着剤とを含有するインク受理層を設けたインクジェット記録媒体であって、前記インク受理層の表面の像鮮明度が５０％以上であり、かつＪＡＰＡＮ ＴＡＰＰＩの紙パルプ試験法Ｎｏ．１８−２に規定する内部結合強さが１２５〜２８０ｍＪである。 - 特許庁
The heat curing die bond film for use in production of a semiconductor device principally comprises 15-30 wt.% of a thermoplastic resin component and 60-70 wt.% of a thermosetting resin component for an organic resin component wherein the surface free energy before heat curing is in the range of 37-40 mJ/m^2.例文帳に追加
本発明の熱硬化型ダイボンドフィルムは、半導体装置の製造の際に用いる熱硬化型ダイボンドフィルムであって、有機樹脂成分に対し熱可塑性樹脂成分１５〜３０重量％及び熱硬化性樹脂成分６０〜７０重量％を主成分として含有し、熱硬化前の表面自由エネルギーが３７ｍＪ／ｍ２以上４０ｍＪ／ｍ２未満であることを特徴とする。 - 特許庁
A precursor film consisting of zinc oxide particulates is formed on a base board and irradiated with active beams having a higher energy than the band gap of the particulates and having an energy density controlled so as to be small when the film is thin and large when film is thick within the range 5-500 mJ/cm^2.例文帳に追加
基板上に、酸化亜鉛微粒子からなる前駆体膜を形成させたのち、この酸化亜鉛微粒子のバンドギャップよりも高いエネルギーを有し、かつ５〜５００ｍＪ／ｃｍ^2の範囲内で、膜厚が薄い場合は小さく、また膜厚が厚い場合には大きくなるように制御されたエネルギー密度をもつ活性線を照射して薄膜状発光素子を製造する。 - 特許庁
In the method for manufacturing the cured pattern by which a pattern obtained from a photosensitive resin composition including a resin, a photopolymerizable compound, a photopolymerization initiator and a solvent is exposed and cured with 10 to 10,000 mJ/cm^2 at 50 to 180°C, the resin includes a structural unit originating from a monomer having a 2-4C cyclic ether.例文帳に追加
樹脂、光重合性化合物、光重合開始剤及び溶剤を含む感光性樹脂組成物から得られたパターンを、５０℃〜１８０℃の条件下で、１０ｍＪ／ｃｍ^２〜１００００ｍＪ／ｃｍ^２露光する硬化されたパターンの製造方法において、樹脂が、炭素数２〜４の環状エーテルを有する単量体に由来する構造単位を含む樹脂である硬化されたパターンの製造方法。 - 特許庁
In the heat sensitive recording material comprising at least a heat sensitive recording layer and a protective layer sequentially laminated on a support, the protective layer contains at least a film forming type silicone emulsion, and a conveying torque of the material brought into contact with a thermal head when printed with an applied energy of 100 mJ/mm2 or above is 2 kg.cm or below.例文帳に追加
支持体上に、少なくとも感熱記録記録層と保護層とをこの順に積層した感熱記録材料において、前記保護層中に少なくとも被膜形成型シリコーンエマルションを含有し、１００ｍＪ／ｍｍ^2以上の印加エネルギーで印画した時の、サーマルヘッドと接触する感熱記録材料の搬送トルクが２Ｋｇ・ｃｍ以下であることを特徴とする感熱記録材料。 - 特許庁
The image forming material is imagewise exposed with light having a wavelength and intensity at which the absorbance of the layer containing the material which converts light to heat satisfies the expressing (transmission absorbance after exposure with 300 mJ/cm2)/(transmission absorbance before exposure)≤0.5.例文帳に追加
支持体上に光を熱に変換する物質を含む層および高分子重合体微粒子を含む層を有する画像形成材料の画像形成方法において、該光を熱に変換する物質を含む層の吸光度が（３００ｍｊ／ｃｍ^2の露光後透過吸光度）／（露光前透過吸光度）≦０．５となる波長及び強度の光で画像露光を行うことを特徴とする画像形成方法。 - 特許庁
There are provided: the low sensitive fracturing composition with improved deflagration transmission; the ignition mechanism for low energy ignition reacting in a low energy of several tens or hundreds millijoule (mJ) obtained by using low current of several amperes (A); and the rock fracturing apparatus for fracturing a brittle material (rock bed, concrete) by igniting the low sensitive fracturing composition by the ignition mechanism with the low sensitive fracturing composition.例文帳に追加
本発明は、殉爆度が向上された鈍感性破砕組成物、数アンペア(A)の低い電流を用いて得た数十乃至数百ミリジュール(ｍJ)の低エネルギーで反応する低エネルギー発火用発火機構及びこれらを含めて前記発火機構が前記鈍感性破砕組成物を低エネルギーで着火させ、脆性物体(岩盤、コンクリートなど)を破砕する破岩装置に関するものである。 - 特許庁
A method for temporarily fixing a member is characterized in that the member is temporarily fixed by using the composition, the processed member is immersed in water at 90°C or less to release the cured body of the composition, wherein the temporal fixing is performed by irradiation with visible or UV light having an accumulative light amount of 100 to 40,000 mJ/cm^2 at 365 nm.例文帳に追加
該組成物を用いて、部材を仮固定し、該加工された部材を９０℃以下の水に浸漬して、前記組成物の硬化体を取り外すことを特徴とする部材の仮固定方法であり、積算光量が３６５ｎｍにおいて１００〜４００００ｍＪ／ｃｍ^２である可視光線又は紫外線を照射することにより仮固定することを特徴とする該部材の仮固定方法。 - 特許庁
In the method for manufacturing the optical element including forming of the optical element of a desired shape by pressing a forming workpiece softened by heating by means of forming dies, and depositing the antireflection film on the surface of the obtained optical element, the optical element of ≥60 mJ/m^2 in surface free energy is subjected to the deposition of the antireflection film by UV ozone cleaning or plasma cleaning.例文帳に追加
加熱軟化した成形素材を成形型により加圧成形して、所望の形状の光学素子を成形し、得られた光学素子の表面に反射防止膜を成膜することを含む光学素子の製造方法であって、反射防止膜の成膜を、ＵＶオゾン洗浄又はプラズマ洗浄することにより表面自由エネルギーが60mJ/m^2以上である光学素子に対して行う。 - 特許庁
When a TFT array substrate is irradiated only once with laser light having a wavelength of 0-355 nm, a pulse width of 5-200 nsec and an energy in the range of 0.16-0.6 mJ/mm^2, only the pixel electrode 5 can be cut off selectively without having any effect on the underlying gate line 1, source line 3, TFT 6 and common capacitive line 2.例文帳に追加
また、波長が０を超え３５５ｎｍ以下、パルス幅が５〜２００ｎｓｅｃ、エネルギーが０．１６〜０．６ｍＪ／ｍｍ^2の範囲であるレーザー光を１回のみ照射するようにすると、画素電極５の下に存在するゲート配線１、ソース配線３、ＴＦＴ６および共通容量配線２に影響を与えることなく、画素電極５のみを選択的に切断しやすい。 - 特許庁
Every time the UV CCD camera 5 photographs a frame of image, the resist pattern 102 under inspection is irradiated with illuminating light having a wavelength in the UV range at an irradiating quantity of 0.5 mJ/cm2 or more, an irradiating threshold not shrinking the resist pattern 102 under inspection or an irradiating quantity below the irradiating threshold, not changing the absorption of an antireflective film.例文帳に追加
また、紫外光用ＣＣＤカメラ５が１枚の画像を撮像する毎に、検査するレジストパターンに対して、紫外域の波長を有する照明光を、０．５ｍＪ／ｃｍ^2以上の照射光量で、且つ、検査対象のレジストパターン１０２を収縮させない照射閾値、或いは、反射防止膜の吸収率を変化させない照射閾値以下の照射光量で照射する。 - 特許庁
After forming a metal thin film 110 on the rear surface 1b where the amorphous layer 12 is formed, the rear surface 1b of the n^+-type substrate 1 is irradiated with laser light under the condition that the product of photon energy and laser output is 1000-8000 eV mJ/cm^2, thereby forming a drain electrode 11 containing a silicide layer 111.例文帳に追加
そして、アモルファス層１２が形成された裏面１ｂ上に金属薄膜１１０を形成した後、ｎ^+型基板１の裏面１ｂ側に光子エネルギーとレーザ出力の積が１０００ｅＶ・ｍＪ／ｃｍ^2以上かつ８０００ｅＶ・ｍＪ／ｃｍ^2以下となるような条件でレーザ光を照射することでシリサイド層１１１を含むドレイン電極１１を形成する。 - 特許庁
The barrier laminate has an organic layer 3 and an inorganic layer 4 formed on the surface of the organic layer, and the organic layer is formed by hardening a polymerizable composition containing a polymerizable compound having a phosphoric ester group by irradiation with UV rays in an amount of UV-ray irradiation of 10-250 mj/cm^2 with a concentration of oxygen on irradiation with UV rays of ≤50 ppm.例文帳に追加
有機層３と、該有機層の表面に設けられた無機層４とを有し、有機層がリン酸エステル基を有する重合性化合物を含む重合性組成物を紫外線を照射することによって硬化させてなり、紫外線照射量が１０〜２５０ｍｊ/ｃｍ^2であり、紫外線照射時の酸素濃度が５０ｐｐｍ以下であるバリア性積層体。 - 特許庁
In the method for manufacturing the mesh member for screen printing, a plurality of holes are made in the metal foil by etching and the mesh member for screen printing is manufactured in the condition that, after applying the photoresist on the metal foil having the thickness of 5-50 μm, an energy amount when the shape of the hole on an exposure mask is exposed is 120-240 mJ/cm^2.例文帳に追加
本発明のスクリーン印刷用メッシュ部材の製造方法は、エッチングによって金属箔に多数の孔開け加工してスクリーン印刷用メッシュ部材を製造するに当り、厚さが５〜５０μｍの金属箔にフォトレジストを塗布した後に、露光用マスクに描画した孔の形状を露光するときのエネルギー量を１２０〜２４０ｍＪ／ｃｍ^2として操業する。 - 特許庁
The crosslinked polyolefin resin foam is characterized in comprising components consisting of 20-60 wt.% of polyethylene resin and 40-80 wt.% of polyolefin resin except polyethylene resin, wherein a melting energy of 140°C or higher included in the melting energy per unit weight (heat quantity value per weight obtained from a melting peak area in differential scanning calorimetry) is 28-50 mJ/mg.例文帳に追加
樹脂成分がポリエチレン系樹脂２０〜６０重量％及びポリエチレン系樹脂以外のポリオレフィン系樹脂４０〜８０重量％からなり、且つ、単位重量当たりの融解エネルギー（示差走査熱量分析の融解ピーク面積から得られる熱量値／重量）に含まれる１４０℃以上の融解エネルギーが２８〜５０ｍＪ／ｍｇであることを特徴とする架橋ポリオレフィン系樹脂発泡体。 - 特許庁
The base paper for the subsequently pasting type false adhesive paper contains 5-40 wt.% mechanical pulp, a cationic polymer having ≥0.3 meq/g cation strength, and 5-40 wt.% inorganic filler, and has 100-500 mJ internal connection strength measured based on an internal bond method regulated by Japan TAPPI 18-2.例文帳に追加
後糊方式の疑似接着紙とする疑似接着紙用原紙であって、機械パルプを５〜４０重量％含み、カチオン強度が０．３ｍｅｑ／ｇ以上のカチオン性重合体を含み、無機填料を５〜４０重量％含み、かつ、ＪＡＰＡＮ ＴＡＰＰＩ １８−２に規定されるインターナルボンド法に基づいて測定される内部結合強さが１００〜５００ｍＪであることを特徴とする疑似接着紙用原紙。 - 特許庁
A method for producing the antireflection laminate having the antifouling layer includes a process in which a curable composition containing particles coated with a protective film is applied directly or via another layer on the transparent substrate, and the paint film is heated at 60-150°C for 1-5 min and irradiated with ultraviolet rays of 100-600 mW in an accumulated quantity of light of 300-700 mJ/cm^2.例文帳に追加
透明基材上に直接またはその他の層を介して、保護膜によって被覆されている微粒子とバインダーとを含有する硬化性組成物を塗布し、該塗膜に温度６０〜１５０℃で１〜５分間加熱し、次いで紫外線を１００〜６００ｍＷで、積算光量として３００〜７００ｍＪ／ｃｍ^２照射することを含む、防汚層を有する反射防止積層体の製造方法。 - 特許庁
In this Eu doped CsBr type storage phosphor screen or panel, 10/9 of ultraviolet luminescence intensity ratio is provided after exposed by a radiation having a wavelength of a range from 150 nm to 400 nm without pretreating the storage phosphor screen or panel using a short ultraviolet ray having a wavelength of a range from 150 nm to 300 nm having 10 mj/mm^2 of energy.例文帳に追加
ＥｕドープされたＣｓＢｒ型貯蔵燐光体スクリーン又はパネルであって、１０ｍＪ／ｍｍ^２のエネルギーを有する１５０ｎｍから３００ｎｍまでの範囲の短紫外線を用いた貯蔵燐光体スクリーン又はパネルの前処理を行わずに１５０ｎｍから４００ｎｍまでの範囲の波長を有する放射線で露光された後に１０／９の紫外線ルミネセンス強度の比を与える。 - 特許庁
The precoat coating film 22 in a required area is removed from the precoated aluminum alloy plate without melting the aluminum alloy plate 21 by irradiating the required area of the precoat coating film formed surface 23 with infrared laser having 0.8-12 μm wave length at ≥10 MJ/m^2 energy density.例文帳に追加
プレコート塗膜２２は、数平均分子量が５０００〜４００００の合成樹脂からなると共に、膜厚が０．５〜２００μｍである合成樹脂塗膜を採用し、プレコート塗膜形成面２３における所望の領域に、波長が０．８〜１２μｍである赤外線レーザーを、１０ＭＪ／ｍ^2以下のエネルギー密度で照射するし、所望の領域内のプレコート塗膜２２を、アルミニウム合金板２１を溶解させることなくプレコートアルミニウム合金板２から除去する。 - 特許庁
The electrophotographic photoreceptor which has a photosensitive layer on a conductive substrate, has the extreme surface layer containing a compound polymerized with a hole transferable compound having ≥2 chain polymerizable functional groups within the same molecule on the electrophotographic photoreceptor and in which the calorific value in the differential scanning thermal analysis of the extreme surface layer is ≤60 mj/mg, the process cartridge having such electrophotographic photoreceptor and the electrophotographic device.例文帳に追加
導電性支持体上に感光層を有する電子写真感光体において、該電子写真感光体の最表面層が、同一分子内に二つ以上の連鎖重合性官能基を有する正孔輸送性化合物を重合した化合物を含有し、かつ該最表面層が示差走査熱分析での発熱量が６０ｍｊ／ｍｇ以下である電子写真感光体、その電子写真感光体を有するプロセスカートリッジ及び電子写真装置。 - 特許庁
The photosensitive resin composition contains pigments, a transparent resin, a monomer having ethylenically unsaturated double bonding, a photo-polymerization initiator and epoxy acrylate and can be cured by laser irradiation at an accumulated exposure amount of 1-150 mJ/cm^2 where the content of epoxy acrylate is 0.1-20.0 wt.% in relation to the total solid content of the photosensitive resin composition.例文帳に追加
顔料、透明樹脂、エチレン性不飽和二重結合を有するモノマー、光重合開始剤及びエポキシアクリレートを含有し、積算露光量１ｍＪ／ｃｍ^２以上、１５０ｍＪ／ｃｍ^２以下のレーザ照射により硬化可能である感光性樹脂組成物であって、前記エポキシアクリレートが前記感光性樹脂組成物の全固形分量を基準として０．１重量％以上、２０．０重量％以下であることを特徴とする。 - 特許庁
例文
In the positive electrode active material for the nonaqueous electrolyte secondary battery composed of at least lithium transition metal complex oxide of a spinel structure, a heat generation starting temperature by a differential scanning calorimetry of the lithium transition metal complex oxide is 220°C or more, a calorific value by the differential scanning calorimetry of the lithium transition metal complex oxide is 700 to 900 mJ/mg.例文帳に追加
非水電解液二次電池用正極活物質を、少なくともスピネル構造のリチウム遷移金属複合酸化物からなる非水電解液二次電池用正極活物質において、前記リチウム遷移金属複合酸化物の示差走査熱量測定による発熱開始温度は、２２０℃以上であり、前記リチウム遷移金属複合酸化物の示差走査熱量測定による発熱量は、７００〜９００ｍＪ／ｍｇである構成とする。 - 特許庁