Construction and Building Materials, 2009
Construction and Building Materials, 2008
Tungsten mine waste mud (TMWM) was investigated for its potential use as repair material of ordin... more Tungsten mine waste mud (TMWM) was investigated for its potential use as repair material of ordinary portland cement (OPC) concrete. Bond strength between OPC concrete substrate and three repair materials was analysed. TMWM geopolymeric binder and two commercial repair products were used as repair materials. Bond strength behaviour was assessed from slant shear tests. A total of 128 slant shear specimens were made in order to evaluate bond strength at 1, 3, 7 and 28 days curing. Four kinds of concrete substrate surface treatment were used, as cast against metallic formwork, as cast against wood formwork, saw cut and acid etching. This study indicates that TMWM geopolymeric binders possess very high bond strength even at early ages and that behaviour is not affected by low surface treatment roughness. Commercial repair products on the other hand show very low bond strength and are very dependent on surface treatment roughness. Scanning electron micrographs reveal that TMWM geopolymeric binders chemically bond to the concrete substrate, while cost comparisons show this geopolymeric repair solution is by far the most cost efficient.
Construction and Building Materials, 2008
This paper reports some results of a research project related to the development of a new binder ... more This paper reports some results of a research project related to the development of a new binder using mineral waste mud from the Portuguese mine. Some aspects related to the effect of aggregates in the microstructure and mechanical behaviour of tungsten mine waste geopolymeric binder are reported in the present study. Test results showed that the aggregate type influences strength development.
Revista Matéria, 2008
Este trabalho teve como objetivo avaliar o comportamento da resistência à compressão, ao longo do... more Este trabalho teve como objetivo avaliar o comportamento da resistência à compressão, ao longo do tempo, em amostras de argamassas à base de cinzas volantes álcali-ativadas. Como ativador alcalino foi utilizada uma solução combinada de NaOH e Ca(OH) 2 . A cura das amostras foi realizada de duas formas distintas. Na primeira, as amostras foram mantidas em estufa à 70°C/12 h e à temperatura constante de 22°C em sala climatizada até a idade de ensaio. Apesar de serem obtidas resistências da ordem de 20 MPa nas primeiras 24 h, houve decréscimo da resistência a partir da idade de 7 dias. Verificado esse comportamento, um segundo método de cura foi adotado. Para isso, o traço utilizado para o preparo de novas argamassas foi o mesmo adotado no método anterior. Porém, foram submetidas à temperatura constante de 70°C até a idade de ensaio. Nesse caso, as amostras apresentaram decréscimo mais acentuado da resistência em menor espaço de tempo, quando comparado às amostras curadas no primeiro método. Como estudos complementares foram realizadas análises microestruturais da CV antes e depois da álcali-ativação, utilizando o MEV/EDS. Nas imagens microestruturais foi possível identificar três morfologias distintas nas pastas álcali-ativadas: uma composta de regiões com aspecto denso; outra apresentando partículas de cinzas volantes parcialmente solubilizadas; e outra mostrando a formação de produtos em forma de cristais aciculares. Porém, apenas o uso do MEV/EDS não foi suficiente para que se pudesse entender o mecanismo de reação deletéria provocada entre os ativadores alcalinos e a cinza volante. Portanto, trabalhos futuros deverão contemplar o uso de ferramentas auxiliares às adotadas nesse trabalho com o objetivo de esclarecer tal mecanismo deletério.
Construction and Building Materials, 2008
Strength data show that the parameters, which lead to optimum strength for 7 days curing, remain ... more Strength data show that the parameters, which lead to optimum strength for 7 days curing, remain the same for long curing ages. However, when calcium hydroxide percentages above 10% are used, strength decrease after 14th curing day is noticed. In order to explain this behaviour several hypotheses are discussed. The use of an activator with a sodium hydroxide concentration of 24 M leads to a compressive strength of almost 70 MPa. The strength performance is typical of a very reactive binder, being suggested that it is due to the calcium hydroxide and also to the nucleation centers provided by the iron oxide of the mine waste mud. Results allow foreseeing that even higher strength performance could be achieved if lower water/sodium molar ratios were used.
Construction and Building Materials, 2008
Eco-efficient Construction and Building Materials, 2011
Eco-efficient Construction and Building Materials, 2011
Eco-efficient Construction and Building Materials, 2011
Materials and Structures, 2005
Les matériaux d'addition font actueÌlement pâÌtie des développements les plus récents dans la pro... more Les matériaux d'addition font actueÌlement pâÌtie des développements les plus récents dans la production du bétoÌr, caÌ Ì'üÍilisation des additions apporte uno amélioration des proprìáés mécâniques et de Ìa durabilité dü béton. D'autre part, leur utilisation a pour objectif de réduire la consommation de ciment. en conlribuant de maniere simple et économique à résoudre les problèmes liés à l'environnenent. Cet aÌlicle étudie les avantâges et Ìes limitations de la substin-rtion pafiielle du ciment par le nétakaolin. Les résultats obtgnus démontrent que cette substituüon apporte, pouÌ Ìe béton de même ordre dc résistancc à ìa compression, une amélioration considérable au niveau de Ìa durabilité. Ce qui penÌet de conclwe quc lc métakaolin est un substitut efficace câpable de rédui.e le contenu de ciment pour l'obtention de bétons équivalents. 1359-5997 O 2004 zuLEM. AÌl Íights rese.ved. Available online at rrvw.rilem.net Materials end Struozres 38 (April 2005) 403-410
... Tanto o tipo de ligante como os próprios agregados in-fluenciam a cor final das argamassas, p... more ... Tanto o tipo de ligante como os próprios agregados in-fluenciam a cor final das argamassas, pelo que importa saber não só quais os ligantes [cal aé- rea ou hidráulica, com ou sem ... Reabilitação ne 12,2006, pp.16 [4] COELHO, AZ;TORGAL,FP;JALALI,S. -"Acal na construção-. ...
Resumo: Embora em termos históricos tenham sido frequentes as utilizações de argamassas de cal, c... more Resumo: Embora em termos históricos tenham sido frequentes as utilizações de argamassas de cal, cuja extinção ocorreu com a adição de gordura vegetal, existe contudo um grande nível de desconhecimento sobre este material. Desconhece-se assim de que forma a adição de gordura influi nas propriedades e durabilidade das argamassas produzidas com aquela cal, quer mesmo quais os mecanismos que expliquem o comportamento das argamassas de cal com gorduras que também contenham pozolanas. O objectivo do presente artigo é por isso o de proceder a uma análise da literatura das características das argamassas à base de cal com gorduras, pondo em evidência aquilo que deverão ser aspectos a investigar num futuro próximo. Palavras-chave: Cal aérea, gorduras, propriedades, durabilidade Figura 1: Fortaleza Portuguesa "Nossa Senhora da Conceição" em Ormuz, Irão. Em cima mapa da Fortaleza do Séc. XVI. Em baixo, localização da Fortaleza no Google. Figura 2: Fortaleza "Nossa Senhora da Conceição".Em cima aspecto actual da Fortaleza.
A grande maioria das descrições sobre as argamassas históricas, refere-se à importância da adição... more A grande maioria das descrições sobre as argamassas históricas, refere-se à importância da adição de pozolanas naturais (cinzas vulcânicas) e pozolanas artificiais (telhas e tijolos de barro cozido moídos), na obtenção de argamassas com elevada resistência quer em termos mecânicos quer mesmo em relação à acção da água. Essas descrições são contudo omissas no que respeita aos mecanismos de reacção, que possam explicar essa mesma resistência, sendo também omissas relativamente à presença zeólitos na composição daquelas argamassas. O presente artigo apresenta uma revisão do estado da arte relativamente aos produtos de hidratação das argamassas históricas e nele se tecem algumas considerações sobre a influência dos mesmos na durabilidade daqueles materiais.
... do Minho Said Jalali, Eng. ... passe a ser consi-derado como um custo ambiental daquele li-ga... more ... do Minho Said Jalali, Eng. ... passe a ser consi-derado como um custo ambiental daquele li-gante, pelo que tal irá certamente reduzir de forma considerável a competitividade econó- mica do mesmo, face aos ligantes geopolimé- ricos, restando somente saber quando ocor ...
The ceramic industry is known to generate large amounts of calcined-clay wastes each year. So far... more The ceramic industry is known to generate large amounts of calcined-clay wastes each year. So far a huge part is used in landfills. Reusing these wastes in concrete could be a win-win situation. For one hand by solving the ceramic industry waste problem and at the same time leading to a more sustainable concrete industry by reducing the use of non renewable resources like cement and aggregates and avoiding environmental problems related to land filled wastes. This paper examines the feasibility of using ceramic wastes in concrete. Results show that concrete with 20% cement replacement although it has minor strength loss possess increase durability performance. Results also shows that concrete mixtures with ceramic aggregates perform better than the control concrete mixtures concerning compressive strength and chloride diffusion.
Construction and Building Materials, 2009
Construction and Building Materials, 2008
Tungsten mine waste mud (TMWM) was investigated for its potential use as repair material of ordin... more Tungsten mine waste mud (TMWM) was investigated for its potential use as repair material of ordinary portland cement (OPC) concrete. Bond strength between OPC concrete substrate and three repair materials was analysed. TMWM geopolymeric binder and two commercial repair products were used as repair materials. Bond strength behaviour was assessed from slant shear tests. A total of 128 slant shear specimens were made in order to evaluate bond strength at 1, 3, 7 and 28 days curing. Four kinds of concrete substrate surface treatment were used, as cast against metallic formwork, as cast against wood formwork, saw cut and acid etching. This study indicates that TMWM geopolymeric binders possess very high bond strength even at early ages and that behaviour is not affected by low surface treatment roughness. Commercial repair products on the other hand show very low bond strength and are very dependent on surface treatment roughness. Scanning electron micrographs reveal that TMWM geopolymeric binders chemically bond to the concrete substrate, while cost comparisons show this geopolymeric repair solution is by far the most cost efficient.
Construction and Building Materials, 2008
This paper reports some results of a research project related to the development of a new binder ... more This paper reports some results of a research project related to the development of a new binder using mineral waste mud from the Portuguese mine. Some aspects related to the effect of aggregates in the microstructure and mechanical behaviour of tungsten mine waste geopolymeric binder are reported in the present study. Test results showed that the aggregate type influences strength development.
Revista Matéria, 2008
Este trabalho teve como objetivo avaliar o comportamento da resistência à compressão, ao longo do... more Este trabalho teve como objetivo avaliar o comportamento da resistência à compressão, ao longo do tempo, em amostras de argamassas à base de cinzas volantes álcali-ativadas. Como ativador alcalino foi utilizada uma solução combinada de NaOH e Ca(OH) 2 . A cura das amostras foi realizada de duas formas distintas. Na primeira, as amostras foram mantidas em estufa à 70°C/12 h e à temperatura constante de 22°C em sala climatizada até a idade de ensaio. Apesar de serem obtidas resistências da ordem de 20 MPa nas primeiras 24 h, houve decréscimo da resistência a partir da idade de 7 dias. Verificado esse comportamento, um segundo método de cura foi adotado. Para isso, o traço utilizado para o preparo de novas argamassas foi o mesmo adotado no método anterior. Porém, foram submetidas à temperatura constante de 70°C até a idade de ensaio. Nesse caso, as amostras apresentaram decréscimo mais acentuado da resistência em menor espaço de tempo, quando comparado às amostras curadas no primeiro método. Como estudos complementares foram realizadas análises microestruturais da CV antes e depois da álcali-ativação, utilizando o MEV/EDS. Nas imagens microestruturais foi possível identificar três morfologias distintas nas pastas álcali-ativadas: uma composta de regiões com aspecto denso; outra apresentando partículas de cinzas volantes parcialmente solubilizadas; e outra mostrando a formação de produtos em forma de cristais aciculares. Porém, apenas o uso do MEV/EDS não foi suficiente para que se pudesse entender o mecanismo de reação deletéria provocada entre os ativadores alcalinos e a cinza volante. Portanto, trabalhos futuros deverão contemplar o uso de ferramentas auxiliares às adotadas nesse trabalho com o objetivo de esclarecer tal mecanismo deletério.
Construction and Building Materials, 2008
Strength data show that the parameters, which lead to optimum strength for 7 days curing, remain ... more Strength data show that the parameters, which lead to optimum strength for 7 days curing, remain the same for long curing ages. However, when calcium hydroxide percentages above 10% are used, strength decrease after 14th curing day is noticed. In order to explain this behaviour several hypotheses are discussed. The use of an activator with a sodium hydroxide concentration of 24 M leads to a compressive strength of almost 70 MPa. The strength performance is typical of a very reactive binder, being suggested that it is due to the calcium hydroxide and also to the nucleation centers provided by the iron oxide of the mine waste mud. Results allow foreseeing that even higher strength performance could be achieved if lower water/sodium molar ratios were used.
Construction and Building Materials, 2008
Eco-efficient Construction and Building Materials, 2011
Eco-efficient Construction and Building Materials, 2011
Eco-efficient Construction and Building Materials, 2011
Materials and Structures, 2005
Les matériaux d'addition font actueÌlement pâÌtie des développements les plus récents dans la pro... more Les matériaux d'addition font actueÌlement pâÌtie des développements les plus récents dans la production du bétoÌr, caÌ Ì'üÍilisation des additions apporte uno amélioration des proprìáés mécâniques et de Ìa durabilité dü béton. D'autre part, leur utilisation a pour objectif de réduire la consommation de ciment. en conlribuant de maniere simple et économique à résoudre les problèmes liés à l'environnenent. Cet aÌlicle étudie les avantâges et Ìes limitations de la substin-rtion pafiielle du ciment par le nétakaolin. Les résultats obtgnus démontrent que cette substituüon apporte, pouÌ Ìe béton de même ordre dc résistancc à ìa compression, une amélioration considérable au niveau de Ìa durabilité. Ce qui penÌet de conclwe quc lc métakaolin est un substitut efficace câpable de rédui.e le contenu de ciment pour l'obtention de bétons équivalents. 1359-5997 O 2004 zuLEM. AÌl Íights rese.ved. Available online at rrvw.rilem.net Materials end Struozres 38 (April 2005) 403-410
... Tanto o tipo de ligante como os próprios agregados in-fluenciam a cor final das argamassas, p... more ... Tanto o tipo de ligante como os próprios agregados in-fluenciam a cor final das argamassas, pelo que importa saber não só quais os ligantes [cal aé- rea ou hidráulica, com ou sem ... Reabilitação ne 12,2006, pp.16 [4] COELHO, AZ;TORGAL,FP;JALALI,S. -"Acal na construção-. ...
Resumo: Embora em termos históricos tenham sido frequentes as utilizações de argamassas de cal, c... more Resumo: Embora em termos históricos tenham sido frequentes as utilizações de argamassas de cal, cuja extinção ocorreu com a adição de gordura vegetal, existe contudo um grande nível de desconhecimento sobre este material. Desconhece-se assim de que forma a adição de gordura influi nas propriedades e durabilidade das argamassas produzidas com aquela cal, quer mesmo quais os mecanismos que expliquem o comportamento das argamassas de cal com gorduras que também contenham pozolanas. O objectivo do presente artigo é por isso o de proceder a uma análise da literatura das características das argamassas à base de cal com gorduras, pondo em evidência aquilo que deverão ser aspectos a investigar num futuro próximo. Palavras-chave: Cal aérea, gorduras, propriedades, durabilidade Figura 1: Fortaleza Portuguesa "Nossa Senhora da Conceição" em Ormuz, Irão. Em cima mapa da Fortaleza do Séc. XVI. Em baixo, localização da Fortaleza no Google. Figura 2: Fortaleza "Nossa Senhora da Conceição".Em cima aspecto actual da Fortaleza.
A grande maioria das descrições sobre as argamassas históricas, refere-se à importância da adição... more A grande maioria das descrições sobre as argamassas históricas, refere-se à importância da adição de pozolanas naturais (cinzas vulcânicas) e pozolanas artificiais (telhas e tijolos de barro cozido moídos), na obtenção de argamassas com elevada resistência quer em termos mecânicos quer mesmo em relação à acção da água. Essas descrições são contudo omissas no que respeita aos mecanismos de reacção, que possam explicar essa mesma resistência, sendo também omissas relativamente à presença zeólitos na composição daquelas argamassas. O presente artigo apresenta uma revisão do estado da arte relativamente aos produtos de hidratação das argamassas históricas e nele se tecem algumas considerações sobre a influência dos mesmos na durabilidade daqueles materiais.
... do Minho Said Jalali, Eng. ... passe a ser consi-derado como um custo ambiental daquele li-ga... more ... do Minho Said Jalali, Eng. ... passe a ser consi-derado como um custo ambiental daquele li-gante, pelo que tal irá certamente reduzir de forma considerável a competitividade econó- mica do mesmo, face aos ligantes geopolimé- ricos, restando somente saber quando ocor ...
The ceramic industry is known to generate large amounts of calcined-clay wastes each year. So far... more The ceramic industry is known to generate large amounts of calcined-clay wastes each year. So far a huge part is used in landfills. Reusing these wastes in concrete could be a win-win situation. For one hand by solving the ceramic industry waste problem and at the same time leading to a more sustainable concrete industry by reducing the use of non renewable resources like cement and aggregates and avoiding environmental problems related to land filled wastes. This paper examines the feasibility of using ceramic wastes in concrete. Results show that concrete with 20% cement replacement although it has minor strength loss possess increase durability performance. Results also shows that concrete mixtures with ceramic aggregates perform better than the control concrete mixtures concerning compressive strength and chloride diffusion.