HY-80 – (‘’High Yield 80’’) rodzaj stali zdolnej do wytrzymania naprężeń o sile 80.000 funtów na cal kwadratowy (około 60 kg/mm²)
_on_the_ways_at_Mare_Island.jpg?width=300)
| Property | Value |
|---|---|
| dbo:abstract | HY-80 is a high-tensile, high yield strength, low alloy steel. It was developed for use in naval applications, specifically the development of pressure hulls for the US nuclear submarine program and is still currently used in many naval applications. It is valued for its strength to weight ratio. The "HY" steels are designed to possess a high yield strength (strength in resisting permanent plastic deformation). HY-80 is accompanied by HY-100 and HY-130 with each of the 80, 100 and 130 referring to their yield strength in ksi (80,000 psi, 100,000 psi and 130,000 psi). HY-80 and HY-100 are both weldable grades; whereas, the HY-130 is generally considered unweldable. Modern steel manufacturing methods that can precisely control time/temperature during processing of HY steels has made the cost to manufacture more economical. HY-80 is considered to have good corrosion resistance and has good formability to supplement being weldable. Using HY-80 steel requires careful consideration of the welding processes, filler metal selection and joint design to account for microstructure changes, distortion and stress concentration. (en) Los aceros HY son una familia de aceros de baja aleación, de alta resistencia a la tracción, alto límite elástico. Fue desarrollado para su uso en aplicaciones navales, específicamente el desarrollo de cascos de presión para el programa de submarinos nucleares de Estados Unidos. El primer miembro de la familia es el HY-80, luego aparecieron el HY-100 y el HY-130. Los aceros "HY" están diseñados para poseer un alto límite elástico, es decir, capacidad para resistir la deformación plástica permanente. Los numerales 80, 100 y 130 hacen referencia a su límite elástico en psi, es decir, 80 000 psi = 5625 kg/cm², 100 000 psi = 7031 kg/cm² y 130 000 psi = 9140 kg/cm². Los HY-80 y HY-100 son ambos grados soldables; mientras que el HY-130 generalmente se considera no soldable. Los métodos modernos de fabricación de acero que pueden controlar con precisión el tiempo y temperatura durante el procesamiento de aceros HY ha hecho que el costo de fabricación sea más económico. El HY-80 se considera que tiene buena resistencia a la corrosión y tiene buena formabilidad para complementar su soldabilidad. El uso del acero HY-80 requiere una cuidadosa consideración de los procesos de soldadura, la selección del metal de relleno y el diseño de la junta para tener en cuenta los cambios en la microestructura, la distorsión y la concentración de tensiones. Y todavía se usa actualmente en muchas aplicaciones navales. Se valora por su relación . (es) HY-80 adalah baja paduan rendah, kekuatan tarik tinggi, kekuatan luluh tinggi. Paduan ini dikembangkan untuk digunakan dalam aplikasi angkatan laut, khususnya pengembangan lambung bertekanan untuk program kapal selam nuklir AS dan saat ini masih digunakan di banyak aplikasi angkatan laut. Hal ini dinilai untuk kekuatan pada rasio berat. Baja "HY" dirancang untuk memiliki kekuatan luluh tinggi (kekuatan dalam menahan deformasi plastis permanen). HY-80 disertai dengan HY-100 dan HY-130 dengan masing-masing 80, 100 dan 130 mengacu pada kekuatan luluh mereka dalam ksi (80.000 psi, 100.000 psi, dan 130.000 psi). HY-80 dan HY-100 keduanya adalah grade yang dapat dilas; sedangkan, HY-130 umumnya dianggap tidak dapat dilas. Metode manufaktur baja modern yang dapat secara tepat mengontrol waktu/suhu selama pemrosesan baja HY telah membuat biaya pembuatan menjadi lebih ekonomis. HY-80 dianggap memiliki ketahanan korosi yang baik dan memiliki kemampuan bentuk yang baik untuk melengkapi yang dapat dilas. Penggunaan baja HY-80 memerlukan pertimbangan yang cermat dari proses pengelasan, pemilihan logam pengisi, dan desain sambungan untuk memperhitungkan perubahan struktur mikro, distorsi, dan konsentrasi tegangan. (in) HY-80 – (‘’High Yield 80’’) rodzaj stali zdolnej do wytrzymania naprężeń o sile 80.000 funtów na cal kwadratowy (około 60 kg/mm²) (pl) |
| dbo:thumbnail | wiki-commons:Special:FilePath/Plunger_(SSN-595)_on_the_ways_at_Mare_Island.jpg?width=300 |
| dbo:wikiPageID | 46753209 (xsd:integer) |
| dbo:wikiPageLength | 27674 (xsd:nonNegativeInteger) |
| dbo:wikiPageRevisionID | 1121850350 (xsd:integer) |
| dbo:wikiPageWikiLink | dbr:Carbon dbr:Elastic_modulus dbr:Electric_arc_furnace dbr:Alloy dbr:Antimony dbr:Permit-class_submarine dbr:Molybdenum dbr:Carnegie_Steel dbr:Melting_point dbr:Gas_metal_arc_welding dbr:Sheffield_Forgemasters dbr:Temperature_gradient dbr:Copper dbr:Thermal_diffusivity dbr:Martensite dbr:ArcelorMittal dbr:Magnetic_particle_inspection dbr:Manganese dbr:Skate-class_submarine dbr:Skipjack-class_submarine dbr:Density dbr:Fatigue_(material) dbr:Fatigue_limit dbr:Krupp_armour dbr:Austenitic_stainless_steel dbr:Tin dbr:Titanium dbr:Distortion dbr:Heat-affected_zone dbc:Steel_alloys dbr:Eutectic dbc:Submarine_components dbr:Nickel dbr:Nuclear_submarine dbr:Charpy_impact_test dbr:Chromium dbr:Goodwin_Steel_Castings dbr:Steel dbr:Vanadium dbr:Thermal_conductivity dbr:Gigapascal dbr:Hardness dbr:Bainite dbr:Tear-yield_ratio dbr:Hydrogen_embrittlement dbr:Arsenic dbr:Acicular_ferrite dbr:Sulfur dbr:Eddy-current_testing dbr:Austenite dbr:Bulk_modulus dbr:Bureau_of_Ships dbr:Phosphorus dbr:Sonar dbr:Sonic_Layer_Depth dbr:Face-centred_cubic dbr:Ksi_(unit) dbr:Seawolf-class_submarine dbr:Shear_modulus dbr:Submarine dbr:Special_treatment_steel dbr:Silicon dbr:Submerged_arc_welding dbr:Poisson's_Ratio dbr:Specific_heat dbr:Fleet_submarine dbr:Tear_resistance dbr:Nondestructive_testing dbr:SMAW_(welding) dbr:Volumetric dbr:Autogenous_weld dbr:Rockwell_hardness dbr:Yield_strength dbr:Crush_depth dbr:Periscope_depth dbr:Coefficient_of_expansion dbr:Strength_to_weight_ratio dbr:File:Plunger_(SSN-595)_on_the_ways_at_Mare_Island.jpg |
| dbp:wikiPageUsesTemplate | dbt:' dbt:Citation_needed dbt:Convert dbt:Efn-lr dbt:Notelist-lr dbt:Reflist dbt:Sfnp dbt:Short_description dbt:USS dbt:US_submarine_classes_after_1945 |
| dct:subject | dbc:Steel_alloys dbc:Submarine_components |
| gold:hypernym | dbr:Steel |
| rdf:type | dbo:ArchitecturalStructure |
| rdfs:comment | HY-80 – (‘’High Yield 80’’) rodzaj stali zdolnej do wytrzymania naprężeń o sile 80.000 funtów na cal kwadratowy (około 60 kg/mm²) (pl) Los aceros HY son una familia de aceros de baja aleación, de alta resistencia a la tracción, alto límite elástico. Fue desarrollado para su uso en aplicaciones navales, específicamente el desarrollo de cascos de presión para el programa de submarinos nucleares de Estados Unidos. El primer miembro de la familia es el HY-80, luego aparecieron el HY-100 y el HY-130. Los aceros "HY" están diseñados para poseer un alto límite elástico, es decir, capacidad para resistir la deformación plástica permanente. Los numerales 80, 100 y 130 hacen referencia a su límite elástico en psi, es decir, 80 000 psi = 5625 kg/cm², 100 000 psi = 7031 kg/cm² y 130 000 psi = 9140 kg/cm². (es) HY-80 is a high-tensile, high yield strength, low alloy steel. It was developed for use in naval applications, specifically the development of pressure hulls for the US nuclear submarine program and is still currently used in many naval applications. It is valued for its strength to weight ratio. (en) HY-80 adalah baja paduan rendah, kekuatan tarik tinggi, kekuatan luluh tinggi. Paduan ini dikembangkan untuk digunakan dalam aplikasi angkatan laut, khususnya pengembangan lambung bertekanan untuk program kapal selam nuklir AS dan saat ini masih digunakan di banyak aplikasi angkatan laut. Hal ini dinilai untuk kekuatan pada rasio berat. (in) |
| rdfs:label | Acero HY (es) HY-80 (in) HY-80 (en) HY-80 (pl) |
| owl:sameAs | freebase:HY-80 yago-res:HY-80 wikidata:HY-80 dbpedia-es:HY-80 dbpedia-id:HY-80 dbpedia-pl:HY-80 https://global.dbpedia.org/id/551oD |
| prov:wasDerivedFrom | wikipedia-en:HY-80?oldid=1121850350&ns=0 |
| foaf:depiction | wiki-commons:Special:FilePath/Plunger_(SSN-595)_on_the_ways_at_Mare_Island.jpg |
| foaf:isPrimaryTopicOf | wikipedia-en:HY-80 |
| is dbo:wikiPageDisambiguates of | dbr:HY |
| is dbo:wikiPageRedirects of | dbr:HY-100 |
| is dbo:wikiPageWikiLink of | dbr:Permit-class_submarine dbr:USS_Topeka_(SSN-754) dbr:Collins-class_submarine dbr:Skipjack-class_submarine dbr:USS_Albacore_(AGSS-569) dbr:USS_Albany_(SSN-753) dbr:Dry_deck_shelter dbr:HY-100 dbr:HY dbr:Big_dumb_booster dbr:Autogenous_welding dbr:Seawolf-class_submarine dbr:Special_treatment_steel dbr:Submarine_depth_ratings |
| is foaf:primaryTopic of | wikipedia-en:HY-80 |